• Journal of the Korean Society for Heat Treatment
• /
• v.19 no.5
• /
• pp.257-261
• /
• 2006

Scandium(Sc) in Al-Zn-Mg-Cu based Al alloy on precipitation phenomenon was compared to a 7001(Al-7.2%Zn-3.2%Mg-1.8%Cu) Al alloy. GP zone and ${\eta}^{\prime}$ phases were the main strengthening phases at low aging temperature under $100^{\circ}C$, but ${\eta}^{\prime}$ and $Al_3Sc$ phases were the main strengthening phases at high aging temperature above $1600^{\circ}C$ in Sc added 7000(Al-7.7%Zn-2.0%Mg-1.9%Cu-0.1%Zr) Al alloy. With the addition of 0.1%Sc in 7000 Al alloy, the activation energy for the GP zone, ${\eta}^{\prime}$ and ${\eta}$ phase decreased compared to the 7001 Al alloy. This result indicates that the Sc accelerated the precipitation for the GP zone, ${\eta}^{\prime}$ and ${\eta}$ phases in 7000 Al alloy. Al-7.7%Zn-2.0%Mg-1.9%Cu-0.1%Zr-0.1 Sc alloy has higher strength than 7001 Al alloy, which has high strength.

• Journal of the Korean Society for Heat Treatment
• /
• v.35 no.3
• /
• pp.150-158
• /
• 2022

The effects of scandium addition on the Al-6Si-2Cu Alloy were investigated. The Al-6Si-2Cu-Sc alloy was prepared by gravity die casting process. In this study, scandium was added at 0.2 wt%, 0.4 wt%, 0.8 wt%, and 1.0 wt%. The microstructure of Al-6Si-2Cu-Sc alloy was investigated using Optical Microscope, Field Emission Scanning Electron Microscope, Electron Back Scatter Diffraction, and Transmission Electron microscope. The microstructure of Al-6Si-2Cu alloy with scandium added changed from dendrite structure to equiaxed crystal structure in specimens of 0.4 wt% Sc or more, and coarse needle-shape eutectic Si and β-Al₅FeSi phases were segmented and refined. The nanosized Al₃Sc intermetallic compound was observed to be uniformly distributed in the modified Al matrix.

• Journal of the Korean Society for Heat Treatment
• /
• v.17 no.1
• /
• pp.23-28
• /
• 2004

In this work, the effect of Sc and Mm(misch metal) on the high temperature behavior of Al-Mg alloys was observed. Hardness was increased due to appearance of fine $Al_3Sc$ precipitates. The elongation of Al-Mg-Sc alloy at high temperature was higher than that of Al-Mg-Sc-Mm alloy because Al-Mg-Sc alloy has finer grain sizes than Al-Mg-Sc-Mm alloy. The strain rate sensitivity factor, "m" of Al-Mg-Sc and Al-Mg-Sc-Mm at $475^{\circ}C$ and $1{\times}10^{-2}s^{-1}$ were 0.33 and 0.46, respectively. The activation energy of Al-Mg-Sc and Al-Mg-Sc-Mm alloy for superplastic deformation was 133KJ/mol and 103KJ/mol respectively. The elongation of Al-Mg-Sc alloy at high temperature was decreased by the addition of Mm, but the strength at high temperatures and low strain rate was improved.

• Journal of Korea Foundry Society
• /
• v.24 no.3
• /
• pp.145-152
• /
• 2004

The eutectic Si in Al-8.5wt.%Si alloy was changed from large flake to fine lemellar(or fibrous) shape when the Sc amount in the Al-Si alloy reaches 0.2wt.%. The optimum amount of Sc for the best modification effect was 0.8wt.% and slight decrease of modification effect occurred over this value. The study on the distribution of the modifiers(Sr, Na, and Sc) and the measurement of the surface tension of the Al-8.5wt.%Si alloy melt added with Sr, Na, and Sc modifier, respectively, reveals that Sc modifies the eutectic Si by the decrease of surface tension, while Sr and Na modify the eutectic Si mainly by impurity induced twinning mechanism.

• Journal of Korea Foundry Society
• /
• v.32 no.4
• /
• pp.181-189
• /
• 2012

The microstructures of self-designed 7000 series Aluminium alloys added with Sc are observed. Moreover, the mechanical properties of the Sc-added Aluminium alloys are evaluated as a function of tensile temperature to establish the conditions of a following extrusion process. New casting conditions in the aluminium alloys added with Sc could be established by changing the casting speed and stirring time in the existing casting conditions of Aluminium alloys. The Sc addition results in $Al_3(Sc,Zr)$ precipitates in the cast alloys, and leads to the formation of equal-axed grains and fine grains. After homogenization heat treatment at $450^{\circ}C$, the Sc-added Aluminium alloys showed the highest elongation values in the temperature ranging from $300{\sim}400^{\circ}C$.

• Korean Journal of Materials Research
• /
• v.12 no.9
• /
• pp.701-705
• /
• 2002

High temperature tensile test has been performed at $450^{\circ}C$ at different strain rate with various grain size due to different reduction rate of Al-4wt%Mg-0.4wt%Sc alloy which is known to be one of useful superplastic alloys. The grain size of Al-4wt%Mg-0.4wt%Sc alloy is $67~100\mu\textrm{m}$ which is courser than that of the alloy which is commonly used as the superplastic material. The total elongation of the Al-4wt%Mg-0.4wt%Sc alloy is strongly dependent on the average grain size, and is a linear function of the inverse average grain size for the present alloy.

• Journal of Korea Foundry Society
• /
• v.30 no.1
• /
• pp.29-33
• /
• 2010

The microstructure of Al-5%Mg based alloy mainly consists of aluminum matrix with a small amount of AlMn phase. The addition of Sc or Zn to the base alloy significantly improved the as-cast tensile strength, while the addition of Fe deteriorated both strength and ductility. Although the Al-5%Mg based alloy was not heat-treatable, aging hardening could be observed in the case that Sc or Zn was added to the base alloy. TEM analysis showed that very fine AlSc or AlMgZn precipitates were formed after T6 heat treatment, resulting in enhanced strength. The corrosion resistance measured as corrosion potential was found to decrease a little by adding Zn, whereas other alloying elements were not clearly influential.

• Korean Journal of Materials Research
• /
• v.13 no.12
• /
• pp.819-824
• /
• 2003

The Al-7.7Zn-2.0Mg-1.9Cu-0.1Zr-0.1Sc alloy exhibited excellent elongation by the new thermomechanical treatment (TMT) process; solution treatment and furnace cooling\longrightarrowhot and cold rolling and then annealing for short time. Tensile test at high temperature from 430 to $500^{\circ}C$ has been performed with various strain rates using for the Al-7.7Zn-2.0Mg-1.9Cu-0.1Zr-0.1Sc alloy obtained by the TMT process. The elongation of the Al-7.7Zn-2.0Mg-1.9Cu-0.1Zr-0.1Sc was 550% tensile tested at $470^{\circ}C$ temperature and 2.2 $\times$ $10^{-3}$ $s^{-1}$ strain rate. The m value of Al-7.7Zn-2.0Mg-1.9Cu-0.1Zr-0.1Sc alloy deformed 85% increased from 0.33 to 0.46 with increasing total elongation. This new TMT process was very simple and easy to make the sheets in the company.

• Journal of Korea Foundry Society
• /
• v.35 no.6
• /
• pp.147-154
• /
• 2015

The effects of Sc and Sr elements on the modification of the eutectic $Mg_2Si$ phase and the castability were investigated in the Al-4wt%Mg-0.9wt%Si-0.3wt%Mn-0.15wt%Fe alloy. Measurements of the cooling curve and microstructure observations were performed to analyze the additional effects of Sc and Sr minor elements during the solidification process. A prominent effect found on the modification of the eutectic $Mg_2Si$ phase with additions of the Sr and Sc elements. Here, a fine eutectic $Mg_2Si$ phase and a decrease in the growth temperature of the eutectic $Mg_2Si$ phase were evident with an addition of Sc element up to 0.2 wt%. The growth temperature of the eutectic $Mg_2Si$ phase decreased and the effect on the modification of the eutectic $Mg_2Si$ phase increased with the addition of Sr element up to 0.02 wt%. The addition of 0.02wt%Sr had the strongest effect on the modification of the eutectic $Mg_2Si$ phase, and the resulting microstructure of the eutectic $Mg_2Si$ phase was found to have a fibrous morphology with a decreased aspect ratio and an increased modification ratio. Fluidity and shrinkage tests were conducted to evaluate the castability of the alloy. The addition of 0.02wt%Sr effectively increased the fluidity of the alloy, while an addition of Sc did not show any effect compared to when nothing was added. The maximum filling length was recorded for 0.01wt%TiB-0.02wt%Sr owing to the effect of the fine ${\alpha}$-Al grains. The macro-shrinkage ratio decreased, while the micro-shrinkage ratio increased with the addition of various eutectic modifiers. The highest ratio of micro-shrinkage was recorded for the 0.02wt%Sr condition. However, the total shrinkage ratio was nearly identical regardless of the amounts added in this study.