• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1997년도 추계학술대회 논문집
• /
• pp.21-24
• /
• 1997

Ferroeletric LiNbO$_3$ thin films hale been prepared directly on Si(100) substrates by conventional RF magnetron spurttering system for nonvolatile memory applications. As-deposited films were performed RTA(Rapid Thermal Annealing) treatment in an oxygen atmosphere at 600 $^{\circ}C$ for 60 s. The rapid thermal annealed films were changed to poly-crystalline ferroelectric nature from amorphous of as-deposition. The resistivity of the ferroelectric LiNbO$_3$ film was increased from a typical vague of 1~2$\times$10$^{8}$ $\Omega$.cm before the annealing to about 1$\times$10$^{13}$ $\Omega$.cm at 500 kV/cm and reduce the interface state density of the LiNbO$_3$/Si(100) interface to about 1$\times$10$^{11}$ cm$^2$ . eV. Ferroelectric hysteresis measurements using a Sawyer-Tower circuit yielded remanent polarization (Pr) and coercive field (Ec) values of about 1.2 $\mu$C/cm$^2$ and 120 kV/cm, respectively.

• 전자공학회논문지A
• /
• 제32A권7호
• /
• pp.77-84
• /
• 1995

We studied the effects of the Zr/Ti ration and the bottom electrode (Pt or ITO) on the electrical properties of PZT thin films prepared by sol-gel method. Their permittivities and tagent losses with the variation of frequencies were measured by the LCR meter and their maximum polarizations, remanent polarizations, and coercive fields were obtained from the hysteresis loops measured by the Sawyer-Tower circuit. For the PZT thin film of the Zr/Ti ration of 53/47, permittivity at 10kHz, coercive field, maximum and remanent polarizations ere measured as 952, 20.7kV/cm, 10.43${\mu}C/cm^{2}$ and 4.3${\mu}C/cm^{2}$, respectively. For the film of the Zr/Ti ration of 25/75, coercive field, maximum and remanent polarizations were measured as 33.12kV/cm, 5.59${\mu}C/cm^{2}$ and 1.5${\mu}C/cm^{2}$, respectively. For the film of the Zr/Ti ratio of 75/25, they were measured as 23.8kV/cm, 7.45${\mu}C/cm^{2}$, and 3.5${\mu}C/cm^{2}$, repectively. Our investigation into the effects of the lower electrode on the electrical properties of PZT films showed the following results. The permittivities of the PZT films deposited on the ITO electrode decreased more quickly than those of the PZT films on the Pt electrode. The tangent losses of the former films increased more quickly than those of the latter. These may be due to the degradation of the quality of the interface between the electrode and the film, which results from the diffusion of Pb. It is also noticeable that permittivities and tangent losses of the PZT films deposited on the ITO electrode varied differently with the Zr/Ti ratio. This may indicate that the quality of the interface between the electrode and the film changes with the Zr/Ti ration of the PZT film.

• E2M - 전기 전자와 첨단 소재
• /
• 제10권2호
• /
• pp.134-140
• /
• 1997

PbTiO$_{3}$-PbZrO$_{3}$-Pb(Ni$_{1}$3/Nb $_{2}$3/O$_{3}$)(PZT-PNN) thin films were prepared from corresponding metal organics partially stabilized with diethanolamine by the sol-gel spin coating method. Each mol rates of PT:PZ:PNN solutions were #1(50:40:10), #2(50:30:20), #3(45:35:20) and #4(40:40:20), respectively. The spin-coated PZT-PNN films were sintered at the temperature from 500.deg. C to 600.deg. C for crystallization. The P-E hysteresis curve was drawn by Sawyer-Tower circuit with PZT-PNN film. The coercive field and the remanent polarization of #4(40:40:20 mol%) PZT-PNN film were 28.8 kV/cm and 18.3 .mu.C/cm$^{2}$, respectively. Their dielectric constants were shown between 128 and 1120, and became maximum value in MPB(40:40:20 mol%). The leakage currents of PZT-PNN films were about 9.4x 10$^{-8}$ A/cm$^{2}$, and the breakdown voltages were about 0.14 and 1.1 MV/cm. The Curie point of #3(45:35:20 mol%, sintered at 600.deg. C) film was 330.deg. C.