• 신재생에너지
• /
• 제5권1호
• /
• pp.26-31
• /
• 2009

The surface etching characteristics of single crystalline silicon wafer were investigated using potassium hydroxide (KOH) and tetramethylammonium hydroxide (TMAH). The saw damage layer was removed after 10min by KOH 45wt% solution at $80^{\circ}C$. The wafer etched at high temperature ($90^{\circ}C$) and in low concentration (4wt%) of TMAH solution showed an increased etch rate of silicon wafer and wavy patterns on the surface. Especially, pyramidal textures were formed in 4wt% TMAH solution without alcohol additives.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2013년도 제45회 하계 정기학술대회 초록집
• /
• pp.299.2-299.2
• /
• 2013

We investigated the potassium remaining on a crystalline silicon solar cell after potassium hydroxide (KOH) etching and its effect on the lifetime of the solar cell. KOH etching is generally used to remove the saw damage caused by cutting a Si ingot; it can also be used to etch the rear side of a textured crystalline silicon solar cell before atomic layer-deposited Al2O3 growth. However, the potassium remaining after KOH etching is known to be detrimental to the efficiency of Si solar cells. In this study, we etched a crystalline silicon solar cell in three ways in order to determine the effect of the potassium remnant on the efficiency of Si solar cells. After KOH etching, KOH and tetramethylammonium hydroxide (TMAH) were used to etch the rear side of a crystalline silicon solar cell. To passivate the rear side, an Al2O3 layer was deposited by atomic layer deposition (ALD). After ALD Al2O3 growth on the KOH-etched Si surface, we measured the lifetime of the solar cell by quasi steady-state photoconductance (QSSPC, Sinton WCT-120) to analyze how effectively the Al2O3 layer passivated the interface of the Al2O3 layer and the Si surface. Secondary ion mass spectroscopy (SIMS) was also used to measure how much potassium remained on the surface of the Si wafer and at the interface of the Al2O3 layer and the Si surface after KOH etching and wet cleaning.