• Journal of the Korean Ceramic Society
• /
• v.53 no.5
• /
• pp.541-547
• /
• 2016

In developing high temperature molds with advantages of the sand and precision (investment) castings, mechanical properties of the mold were improved through homogeneous coating of starting powders with an inorganic binder and improvement of fabrication process. Beads with mullite composition were employed for properties of the mold under high temperature, which was compared with artificial sands. Precursors of silica and sodium oxide were used as starting materials for an inorganic binder to achieve homogeneous coating on the starting powders. Strength was enhanced by the glass phase converted from the inorganic binder through heat treatment process. Also, two kinds of process, wet and dry processes, were incorporated to prepare mold specimens. Consequently, fabrication process of the mold with superior strength and high temperature applicability, compared with the previous molds for sand casting, could be suggested through control of the starting material and enhancement of the vitrification efficiency.

• Journal of the Korean Institute of Landscape Architecture
• /
• v.32 no.6 s.107
• /
• pp.109-116
• /
• 2005

This study was conducted to examine the growth and physiological characteristics of Asplenium scolopendrium native fern as affected by irrigation times and soil media as an environment modeled on habitate where was sunken-condition. 1. Light intensity was lower in sunken than in non-sunken, but air humidity was higher in sunken about $2040\%$. Soil moisture content was higher with the leaf mold in sunken irrigating 2 times/week. The results of chemical analysis of medium showed that EC, pH, organic matter content, total nitrogen, CEC, Exch-Ca, Exch-Mg and Exch-K were higher with leaf mold than sud: leafmold and field soil: sud: leaf mold. 2. In the case of irrigation 2 times/week Asplenium scolopendrium grew well sunken more than non-sunken. As non-sunken condition similar with, 7 times/week irrigation, plant height, frond width, frond length and stipe length increased. In case of soil media, growth of Asplenium scolopendrium was better with leaf mold than that of sand: leafmold or field soil: sand: leaf mold. 3. In the case of irrigation 2 times/week photosynthetic rate, $CO_2$ absorption rate and water efficiency were higher with non-sunken than that of sunken, expect of stomatal conduction, $CO_2$ use efficiency. The physiological characteristics of Asplenium scolopendrium were highest in non-sunken irrigating 7 times/week In case of soil media, physiological activity was higher with leaf mold than sand: leafmold or field soil: sand: leaf mold.

• Journal of Korea Foundry Society
• /
• v.4 no.2
• /
• pp.102-107
• /
• 1984

The variations of the mold compression strength were studied by varing the contents of the silicon powder and water glass, silion purities, and molecule rates of the water glass, when domestic JA EUN DO sand is mixed with water glass (sodium silicate) and metallic silicon or ferro - silicon powder by the self - hardening N - PROCESS method. The results obtained from this experiment are as follows; 1) The compression strength of the mold used with metalic powder was higher and more stable than to be used ferro - silicon powder. 2) 6% water glass of 2.8 molecule rate and 1.5% of ferro - silicon of 75% purity for the N - PROCESS used with JA EUN DO sand was suitable mixing rate. 3) The compression strength increased with self - hardening time, and the PH values of the mixture of silicon powder and water glass did not change after 2 hours, but the compression strength increased steadily due to the reaction of remained silicon. 4) It is recommended to take 24 hours for self - hardening time at least.

• Design & Manufacturing
• /
• v.14 no.4
• /
• pp.52-57
• /
• 2020

In this study attempted to prevent defects due to blow holes among defects of sand casting products. It was intended to reduce the defect rate by reducing the blow hole of the inner surface. Currently, expectations and requirements for the quality level of non-ferrous aluminum casting in the casting industry are increasing. In addition, the shape is complex and the shrinkage precision is required. Among them, the test prototype is expensive to manufacture the mold, and the production time is also long, and the product is manufactured by sand casting. At this time, the highest defect rates are defects caused by shrinkage defects, surface defects, and blow holes.. At this study, the manufacturing time was shortened by using the shape of the fluid movement path in advance. Also, it is possible to reduce defects due to blow holes.

• Journal of the Korean Society of Environmental Restoration Technology
• /
• v.8 no.6
• /
• pp.13-20
• /
• 2005

This study was conducted to examine the growth and physiological characteristics of Polystichum lepidocaulon native fern as affected by soil mixture as an environment modeled on habitate where was sunken-condition. 1. Polystichum lepidocaulon grew well sunken more than non-sunken condition. Under soil mixture of field soil : sand : leaf mold, Plant height, frond width, frond length, stipe length and ornamental value were increased compared with the other soil mixture. 2. Fresh and dry weight of fronds were higher with non-sunken than sunken condition. In sunken condition, fresh and dry weight were better with field soil : sand : leaf mold than the other soil mixture. 3. Number of spore fronds were increased with sunken condition. As sunken condition, sand : leaf mold was better than field soil : sand : leaf mold or leaf mold. 4. Photosynthetic rate, $CO_2$ absorption rate and water efficiency were higher with field soil : sand : leaf mold than that of sand : leaf mold or leaf mold. expect of stomatal conduction and $CO_2$ use efficiency.

• Journal of Korea Foundry Society
• /
• v.43 no.3
• /
• pp.107-136
• /
• 2023

Natural silica sand was commonly used for sand casting of cast steel products, and chromites sand was used to suppress seizure defects due to the lack of thermal properties of silica sand. However there are disadvantages such as deterioration by repeated use, system sand mixing problem, difficulty separating and removing, increased during mold according to high density and to being waste containing chrome. Recently, industrial waste reduction and atmospheric environment improvement have been highlighted as important tasks in the casting industry. In order to solve the problems that occur when using foundry Sand and to improve the environment of casting factories, various artificial sands that can be applied instead of natural silica sand have been developed and introduced. Artificial sands can be classified into artificial sand manufactured by the electric arc atomization or gas flame atomization, artificial sand manufactured by the spray drying & sintering process, artificial sand manufactured by the sintering & crushing process and exhibit different physical properties depending on the type of raw-minerals and manufacturing method. In this study, comparative evaluation tests were conducted on the physical properties of various foundry sands, mold strength, physical durability, thermal durability, and casting test pieces. When comprehensively considering the actual amount of molding sand used according to density, the mold strength according to the shape of sand, the physical and thermal durability of foundry sand, and the heat resistance characteristics of foundry sand, 'Molten artificial sand A1' or 'Molten artificial sand B' is judged to be the most suitable spherical artificial sand for casting of heavy steel castings.

• Journal of Korea Foundry Society
• /
• v.14 no.1
• /
• pp.45-51
• /
• 1994

The possibility of using bulk talc as molding material was reviewed and tested with the measurement of thermal properties and computer simulations. The measured thermal conductivity and heat diffusivity($k{\rho}c$) of talc were $2.4W/m^{\circ}C$ and $6.6{\times}10^6J^2/m^4^{\circ}C^2s$, respectively. Thermal properties of talc could be ranked between those of sand mold and iron mold. Talc transforms into cristobalite and enstatite at $910^{\circ}C$, During the transformation volume and structure change, cracks appear on the surface and distortion occurs. Therefore talc can be used for molding material below $910^{\circ}C$ if carefully treated. Computer simulation was carried out to test whether talc insert could promote directional solidification in sand mold and iron mold. In sand mold, it was possible to achieve directional solidification of thin plate casting with the length to thickness ratio of 15, if both iron insert and talc insert were used. In iron mold, it was possible to achieve directional solidification only with talc insert.

• Journal of the Korean Society of Industry Convergence
• /
• v.25 no.5
• /
• pp.889-898
• /
• 2022

In this study, sand casting process was applied to manufacture a large aluminum turbo-type fan used for tank powerpack. To apply the sand casting method, the turbo fan was reverse engineered, and after designing three gating systems, the optimal gating system design was selected by performing casting simulation. In the case of the bottom up-gating system, there is a significant temperature loss of the molten alloy during blade filling. When the molten alloy is completely filled into the sand mold, the blade upper tip and front shroud are below the liquidus temperature. In the case of the top down-gating system, molten alloy scattering occurs, but the temperature loss while the blade is filled is smaller than that of the bottom up type. And after the inflow of molten alloy into the mold is completed, the blade upper tip and front shroud are higher than the liquidus temperature. A sand mold was manufactured with the top down-gating system and the casting process was performed. The fan was made perfectly in appearance without any unfilled parts.

• Journal of the Korean Society for Heat Treatment
• /
• v.10 no.3
• /
• pp.159-164
• /
• 1997

Non-alloyed and 1.0%Ni alloyed ductile cast iron were cast into the sand mold and metal mold, and finer graphite size was obtained in case of metal mold casting. Direct tempering after casting showed the slight increase of absorbed energy, which is largely due to the relieving of residual stress that is developed during casting. After austempering heat treatment, higher impact energy was obtained in case of metal mold casting than sand mold casting, which is due to the finer graphite size.

• Korean Chemical Engineering Research
• /
• v.44 no.2
• /
• pp.136-148
• /
• 2006

A foundry makes various machinery parts made by iron. For manufacturing machinery parts, they usually uses wooden mold with molding sand and pour the molten iron into wooden mold through inlet. A foundry have many processes including Furan process, In Furan process workers prepares a wooden mold in the molding sand. So they fixes wooden mold in sand housing and then they fill the molding sand in the sand housing. Molding sand should be sticky enough to sustain the shape of wooden mold, so several materials are needed to prepare the suitable molding sand. The first step of Furan process is making the molding sand with molding sand and Voltaic Organic Compounds (VOC) and the second step of Furan process is pour the molding sand into the wooden molding housing. This two step of process generated noxious VOC and various size of dust. So the process is very dirty and dangerous one. Because of these, Workers frequently shrink out of the plant. The company related with foundry usually faced on the difficult situation for engagement and always have shortage of hiring problem. Through this study, we developed a system which removes toxic VOC and dust simultaneously. We design and construct real system and install it at real plant. Before setting up this system, the working surroundings VOC (for formaldehyde) 15 ppm and Dust(for $PM_{10}$) $8,000{\mu}g/m^3$. After setting up this system, working surroundings is improved by VOC (for formaldehyde) 0 ppm, Dust(for $PM_{10}$) $4{\mu}g/m^3$, and the work evasion factor is removed. So we contribute to solve hiring problem of this company and increasing the productivity also.