• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2014.11a
• /
• pp.171-171
• /
• 2014

열교환기용 304L SUS 강관의 열에 기인한 열처리 영향이 강관의 조직과 기계적 성질에 미치는 영향을 평가하고자하였다. 이를 위하여 인위적으로 열처리시킨 304L SUS 강관의 표면과 표면하 마이크로 비커스 경도시험과 와전류 비파괴검사시험을 하였다. 또한 열처리영향에 따른 강관내 조직변화를 금속현미경으로 관찰하여, 열교환기용 304L SUS 강관의 열영향 평가를 비파괴적 기법으로 조사하고자 하였다.

• Journal of the Korean Society of Marine Environment & Safety
• /
• v.23 no.4
• /
• pp.407-414
• /
• 2017

In this study, a performance evaluation was conducted using a SUS 304 plate applied to low-temperature co-fired coating as a replacement for titanium plates. As a result of computational fluid dynamic analysis, the SUS 304 plate, applied to low-temperature co-fired coating, showed better heat transfer performance than a titanium plate, for 100 micron thickness coating. The result of the experiments using an actual heat exchanger revealed that a coated SUS 304 plate showed better heat transfer performance than a titanium plate. Furthermore, as the degree of corrosion and scale formation of the plate was confirmed through an overhaul inspection, the corrosion resistance of a coated SUS 304 plate was found to be almost the same as that of a titanium plate, and the inhibition effect of scale formation by sea water was better with a coated SUS 304 plate.

• Proceedings of the KWS Conference
• /
• 2000.10a
• /
• pp.94-97
• /
• 2000

• Proceedings of the KWS Conference
• /
• 1995.04a
• /
• pp.110-113
• /
• 1995

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2009.10a
• /
• pp.203-203
• /
• 2009

• Korean Journal of Materials Research
• /
• v.10 no.12
• /
• pp.838-844
• /
• 2000

For the fabrication of titanium diboride($TiB_2$)- based cermet as applications of cutting tools and wear resistant materials, a binder metal with good mechanical properties and sinterability is essential. In this study, SUS316L was chosen for the binder metal to obtain a new $TiB_2$ cermet with superior hardness and toughness.$TiB_2$-SUS316L cermets were densified to relative density of more than 99% by pressureless sintering at temperature above $1650^{\circ}C$ The flexural strength was up to 1290MPa at 10vo1%SUS316L cermet in spite of the formation of $Fe_2$B phase during the sintering. The fracture toughness was obtained up to $6MPam^{1/2}$ with Victors hardness over 18Gpa. These hardness and fracture toughness combinations are better than those of conventional cermet. The high temperature strength remarkably decreased by the plastic deformations of SUS316L binder phase at nearby $800^{\circ}C$ .

• Journal of Energy Engineering
• /
• v.10 no.2
• /
• pp.132-139
• /
• 2001

석탄가스화 복합발전의 집진 공정에 사용하기 위한 금속제 safety filter의 재질 선정을 위하여 황화수소 가스 분위기에서 합금강의 부식 특성을 규명하였다. 사용 합금강은 SUS 310, SUS 316, Inconel 600과 Hastelloy X이다. 전기로 내에 설치된 지름 50mm의 qualtz 튜브 반응기에서 부식실험이 행하여졌다. 40$0^{\circ}C$부터 $700^{\circ}C$까지의 등은 조건에서 실험이 행하여졌고, 분위기 가스의 영향을 보기 위하여 H$_2$S 가스를 함유한 $N_2$(dry), $N_2$(saturation), $CO_2$(dry), 그리고 석탄가스 분위기에서 실험하였다. 부식 생성물을 파악하기 위하여 X-ray 회절기와 주사전자현미경 분석이 함께 이루어졌다. 1.7% H$_2$S, $600^{\circ}C$ 이하 온도 조건에서는 니켈계 내식강 중 Hastelloy X와 철계 내식강 중 SUS 310 등 고크롬 합금강이 IGCC 용 필터 소재 금속으로서 높은 내부식성을 나타내었다. 0.3%~4.99% 황화수소 농도 범위에서 황화수소 농도 변화에 따라서 SUS 310의 경우 3~237mg/d$m^2$.day, Inconel 600의 경우 4~660mg/d$m^2$.day로 부식속도는 크게 증가되었다. 50$0^{\circ}C$, 석탄가스 분위기에서 부식속도는 SUS 310은 45mg/d$m^2$.day, SUS 316은 110mg/d$m^2$.day, Inconel 600은 576mg/d$m^2$.day, 그리고 Hastelloy X 는 140mg/d$m^2$.day로서 합금강 시편 중 SUS 310 합금강이 가장 우수한 내식성을 나타내었다. 부식 표면에는 황화니켈, 황화철 피막이 형성되었다.

• Tribology and Lubricants
• /
• v.38 no.5
• /
• pp.222-226
• /
• 2022

Between diaphragms made of stainless steel (SUS), which is the main component of a hydrogen gas compressor, micro-slip occurs owing to repeated bending, resulting in scratches on the surface. The surface scratch of the compressor part is a problem with airtightness, which reduces the efficiency of the compressor; in severe cases, damage is a possibility. In this study, the changes in friction and wear characteristics due to the surface polishing of SUS and carbon-based solid lubricant films (graphene and CNT) were analyzed. Bare SUS, polished SUS, graphene film, and CNT film specimens were prepared. The surface roughness of the SUS was significantly reduced by surface polishing but increased by carbon-based solid lubricating films. In contrast, the friction coefficient maintained a similar value after surface polishing but was significantly reduced by the carbon-based solid lubricant films. In particular, the graphene film exhibited the lowest initial friction coefficient, while the CNT film exhibited the lowest overall average friction coefficient. Regarding the wear rate, polished SUS exhibited the lowest value, but the surface condition of the wear track showed that the carbon-based solid lubricating films were relatively less damaged. Although the wear rate measured was largely attributed to the solid lubricating film peeling off, the SUS surface under the film was considered protected.

• Journal of Korean Society of Environmental Engineers
• /
• v.39 no.2
• /
• pp.82-88
• /
• 2017

MET (Microbial Electrochemical Technology), such as MFC (Microbial Fuel Cell) and MEC (Microbial Electrolysis Cell), is a promising technology for producing sustainable biogas from an anaerobic digester (AD). At current stage, however, the most likely limiting factors, large internal resistances, should be overcome for successful scale up of this technology. Various researchers reported that application of electrode materials containing high current density, increase of ion strength and conductivity, configuration of electrode are good methods for minimizing internal resistances. Recently, stainless steel is receiving great attention because of not only high performance and durability but also low cost. Therefore, in this study, we evaluate electrochemical characteristics and biogas production rate using various electrode materials and configuration (graphite carbon coated with catalysts ($GC-C_M$) or not (GC), stainless steel mesh (SUS-M) and plate (SUS-P)). As the results, current densities of $GC-C_M$, GC, SUS-P, SUS-M were 2.03, 1.36, 1.04, $1.13A/m^2$, respectively. Methane yields of $GC-C_M$, GC, SUS-P, SUS-M were 0.27, 0.14, 0.19, 0.21 $L-CH_4/g-COD_{rem}$., respectively. Stainless steel shows high current density and methane yield, which are similar as graphite carbon coated with catalysts.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2013.05a
• /
• pp.1029-1030
• /
• 2013