• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 1999년도 추계학술발표대회 논문집
• /
• pp.36-39
• /
• 1999

Steel tire cords were coated via RF Plasma Polymerization of acetylene in order to enhance adhesion to rubber compounds. Adhesion of tire cords was measured by TACT as a function of plasma polymerization and argon etching conditions such as power, treatment time and chamber pressure. Tested tire cords were analysed by SEM to elucidate the adhesion mechanism. The highest adhesion values were obtained with argon etching condition at 90W, 10min, 30mtorr followed by acetylene plasma polymerization condition at 10W, 30sec., 30mtorr. In SEM analysis, the plasma polymerized tire cord at the optimized condition showed 100% rubber coverage as observed from brass-plated steel tire cords.

• 접착 및 계면
• /
• 제4권1호
• /
• pp.28-34
• /
• 2003

강철 타이어 코드의 접착력 향상을 위하여 아세틸렌 플라즈마 중합 코팅, 아르곤 에칭+아세틸렌 플라즈마 중합 코팅, 그리고 아르곤 에칭+담채를 이용한 아세틸렌 플라즈마 중합 코팅을 실시하였으며, 접착력은 TCAT시편으로 측정하였다. 플라즈마 중합 코팅된 타이어 코드의 내구성을 고찰하기 위하여 제 1 단계로 아세틸렌 플라즈마 중합 코팅된 타이어코드를 상온에서 1, 3, 5, 10, 15일 동안 방치한 후 TCAT 시편을 제조하여 접착력변화를 측정하였으며, 제 2 단계로는 플라즈마 중합 코팅된 코드로 TCAT 시편을 제조한 후 증류수, 10% NaCl 수용액에서 또는 $100^{\circ}C$ 오븐에서 1, 2, 3, 4주간 노화시키면서 접착력 변화를 측정하였다. SEM/EDX을 이용하여 코드의 파괴표면을 분석하였으며, 황동코팅과 비교 분석하였다. 아르곤 에칭+담채를 이용한 아세틸렌 플라즈마 중합으로 코팅된 강철 타이어 코드의 접착력은 황동코팅된 시편의 접착력과 거의 같은 수준이었다. 타이어 코드의 상온 노화시험에서 황동코팅된 시편이 아세틸렌 플라즈마 중합 코팅된 시편에 비하여 우수 내구성을 보여주었으나, TCAT 시편의 노화에서는 아세틸렌 플라즈마 중합 코팅이 황동코팅에 비하여 우수하거나 비슷한 결과를 보였다.

• Elastomers and Composites
• /
• 제35권1호
• /
• pp.63-70
• /
• 2000

아연 도금된 강철 타이어 코드의 접착성 향상을 위하여 아르곤 플라즈마로 에칭후 아세틸렌 또는 부타디엔 플라즈마 고분자 중합으로 코팅하였다. 플라즈마 고분자 중합은 10W, 30분, 30mTorr에서 실시하였으며, 아르곤 에칭은 90W, 30초, 30mTorr에서 실시하였다. 타이어 코드의 접착력은 TACT으로 측정하였으며, 파괴 표면을 주사전자현미경으로 분석하였다. 또한 플라즈마고분자로 코팅된 타이어 코드의 표면을 FT-IR, Alpha-step 및 접촉각 측정기로 분석하여 접착 메카니즘을 규명하고자 하였다.

• Elastomers and Composites
• /
• 제35권1호
• /
• pp.53-62
• /
• 2000

아연 도금된 강철 타이어 코드를 아세틸렌 또는 부타디엔 가스를 이용한 플라즈마 고분자 중합으로 고무와의 접착성 향상을 위하여 코팅하였다. 플라즈마의 세기, 중합 시간 및 가스의 압력을 변화시키면서 플라즈마 고분자 중합을 실시하였으며, 아르곤 가스를 이용한 에칭도 실시하였다. 또한 플라즈마 중합시에 아르곤, 질소 또는 산소를 담체 가스로 사용하여 접착성 향상으로 도모하였으며, 접착성은 TACT 방법으로 측정하였다. 아르곤 에칭 (90W, 10min, 30mTorr) 후에 아르곤 가스를 (25/5 : 아세틸렌/아르곤) 담체로 사용하여 아세틸렌 플라즈마 중합 (10W, 30sec, 30mTorr)으로 코팅된 타이어 코드가 285N의 접착력으로 가장 좋은 결과를 보였으며, 이는 황동으로 코팅된 타이어 코드의 290N과 같은 수준의 접착력이다.

• Elastomers and Composites
• /
• 제34권2호
• /
• pp.128-134
• /
• 1999

타이어 코드용 강철선을 RF 플라즈마를 이용한 acetylene 및 butadiene 가스의 플라즈마 중합으로 코팅하였으며, 타이어용 고무와의 접착력을 TCAT 또는 T-test로 측정하였다. 강철선의 접착력은 사용된 gas, plasma power, 코팅시간 및 가스 압력에 따라 측정하였으며, 플라즈마 중합에 앞서 Ar 플라즈마 에칭으로 타이어 코드를 세척하였다. 또한 $80^{\circ}C$의 증류수에서 7일간 노화시켜 접착력 저하를 고찰하였으며, 접착력 시험 후 타이어 코드 표면을 SEM으로 분석하여 파괴거동을 규명하고자 하였다. 가장 우수한 접착력은 acetylene의 경우 20W, 2분, 25mtorr에서, 그리고 butadiene의 경우는 l0W, 4분, 25mtorr에서 얻을 수 있었으며, Ar 에칭에 의한 접착력 변화는 없었다. 노화에 의한 접착력 저하는 없었으며, 도리어 증가하는 현상을 보였다. SEM 분석에서 강철선의 높은 거칠기와 플라즈마 코팅의 얇은 두께로 인하여 파괴거동 규명에는 한계가 있었다.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2008년도 춘계학술대회 논문집
• /
• pp.201-204
• /
• 2008

In this paper, several process parameter studies of the manufacturing process of the steel cords are carried out to verify the relation between the process parameters and the residual stresses on the steel cords. At first, the finite element analysis of the drawing process is performed and the residual stress distributions with respect to the wire material and the area reduction ratio are obtained. The residual stress of the drawn wire is imported the finite element analysis of the twisting process as an initial stress. After that a parameter study of the twisting process is carried out. The process parameters are the applied tension, the over-twisting angle and the tensile strength of the drawn wire. Based on these studies, the optimum values of the process parameters which can remove or reduce the undesired residual stresses are determined. The optimum value of the process parameters are confirmed by the finite element analysis of the elastic recovery process of the steel cords. Finally, the finite element analysis of the roller straightening process is done to study the variation of the distribution of the residual stress before and after the process.

• Bulletin of the Korean Chemical Society
• /
• 제15권2호
• /
• pp.122-126
• /
• 1994

Corrosion of brass coated steel cords in the acetonitrile solution of sulfenamide derivatives, N-Cyclohexylbenzothiazole-2-sulfenamide (CBTS), N,N'-Dicyclohexylbenzothiazole-2-sulfenamide (DCBS), N-tert-Butylbenzothiazole-2-sulfenamide (TBBS), N-tert-Amylbenzothiazole-2-sulfenamide (TABS), and N-Oxydiethylbenzothiazole-2-sulfenamide (OBTS) was investigated by potentiostatic anodic and cathodic polarization (Tafel plot), DC polarization resistance, and AC impedance measurements. The corrosion current densities and rates are 1.236 ${\mu}A /cm^2$ and 0.655 MPY for CBTS; 1.881 ${\mu}A/cm^2$ and 0.988 MPY for DCBS; 2.367 ${\mu}A/cm^2$ and 1.257 MPY for TBBS; 3.398 ${\mu}A /cm^2$ and 1.809 MPY for TABS, respectively. OBTS among derivatives under study shows the lowest corrosion density (0.546 ${\mu}A /cm^2$) and the slowest corrosion rate (0.288 MPY). Also, the charge transfer resistances and the double layer capacitances are 275.21 $k{\Omega}{\cdot}cm^2$ and 7.0 ${\mu}F{cdot}cm^{-2}$ for CBTS; 14.24 ${\mu}F{\cdot}cm^2$ and 26 ${\mu}F{\cdot}cm^{-2}$ for DCBS; 54.15 $k{\Omega}{\cdot}cm^2$ and 26 ${\mu}F{\cdot}cm^{-2}$ for TBBS; 0.96$k{\Omega}{\cdot}cm^2$ and 83 ${\mu}F{\cdot}cm^{-2}$ for TABS, respectively. The weaker the electron donating inductive effect of derivatives is and the smaller the effect of steric hindrance is, the more the corrosion of brass coated steel cords in the acetonitrile solution of sulfenamide derivatives is prevented. The above results agree with that observed in the field of tire industry.

• Composites Research
• /
• 제16권3호
• /
• pp.9-17
• /
• 2003

타이어 벨트층내의 코드간 균열연결 및 층간균열진전을 모사하기 위해 자유단을 갖는 2층 고무/코드 적층시험편에 대한 4~11mm 변위제어 실험을 수행하였다. 자유단의 코드간 균열연결시의 폭방향 균열진전량은 45$^{\circ}$ 경사진 코드들간 길이의 절반에 도달할 때의 측정값으로 하였으며, 이는 탐침법에 의해 측정되었다 또한, 자유단에서 코드들간 균열연결을 모사하기위해 2차원의 이상화된 모델링 기법을 고안하였다. 이론수명은 테어링에너지(균열파단면의 단위면적당 방출에너지)를 이용하여 코드간 균열연결수명(임계값)과 이후 최종파손까지의 수명으로 구분하였으며, 이들을 각기 실험값과 비교하였다. 임계값까지의 수명예측은 실험과 비교하여 약 20%, 최종파손까지 약 65%의 오차가 발생하였다. 따라서, 전체 이론수명은 실험과 비교하여 약 45%의 오차를 발생하였다.

• 대한기계학회논문집
• /
• 제13권5호
• /
• pp.820-830
• /
• 1989

본 논문에서는 타이어의 각 부분의 물성치 계산을 위한 식을 유한요소법에 적용할 수 있도록 제안하였다. 이 식은 강철 코드의 굽힙효과를 고려 하였으며, 특히 각 요소에서 전단변형이 일어나는 동안의 굽힘효과를 고려하였다. 유한요소 공식화는 가상일의 원리에 의하여 평형 방정식으로부터 유도하였고, Updated refer- ence coordinate에 대해 증분해석을 적용하여 Updated Lagrangian공식화를 하였다. 그리고 차량하중에 의하여 타이어가 노면에 접지될때의 응력상태를 게산할 수 있도록 접촉문제 공식화를 유한요소 공식화에 첨가 하였다.