• Journal of Ocean Engineering and Technology
• /
• v.32 no.6
• /
• pp.492-501
• /
• 2018

The following results were obtained from a series of studies to accumulate data to reduce the coefficient of friction for press dies by performing tribological tests before and after the UNSM treatment of SM45C. The UNSM-treated material had a nano-size surface texture, high surface hardness, and large and deep compressive residual stress formation. Even when the load was doubled, the small amount of abrasion, small weight of the abrasion, and width and depth of the abrasion did not increase as much as those for untreated materials. When loads of 5 N, 7.5 N, and 10 N were applied to the untreated material of SM45C, the coefficient of friction was approximately 0.76-0.78. With the large specimen, a value of 0.72-0.78 was maintained at a load of 50 N despite the differences in the size of the wear specimen and working load. Tribological tests of large specimens of SM45C treated with UNSM under tribological conditions of 100 N and 50 N showed that the frictional coefficient and time constant stably converged between 0.7 and 0.8. The friction coefficients of the small specimens treated with UNSM showed values between 0.78 and 0.75 under 5 N, 7.5 N, and 10 N. The friction coefficients of the SM45C treated with UNSM were comparable to each other.

• Journal of Welding and Joining
• /
• v.26 no.3
• /
• pp.45-50
• /
• 2008

SM45C steel rods being used generally for power transmission shafts and machine components was selected and welded by Butt-GMAW(Gas Metal Arc Welding) method. An estimation of fatigue life was studied by constructing S-N curve. Fatigue strength of base metal zone showed higher values than one of weld zone in low cycles between $10^4$ and $10^6$cycles. However, significant decrease in fatigue strength of base metal was found around $10^6$cycles, which were almost same as one of heat affected zone. This decrease was attributed that initial residual stress of the steel rods distributed by drawing process was diminished by continually applied load, and resulted in softening of base metal. The fatigue limit of the weld zone was highest in the boundary between deposited metal zone and heat affected zone, and followed by in the order of deposited metal zone, base metal zone, and heat affected zone. Based on these results, it is revealed that the stress for safety design of machine components using SM45C butt-welded steel rods must be selected within the region of the lowest fatigue limit of heat affected zone.

• Transactions of the Korean Society of Machine Tool Engineers
• /
• v.12 no.3
• /
• pp.58-67
• /
• 2003

Welding characteristics of austienite 304 stainless and SM45C using a continuous wave Nd:YAG laser n experimentally investigated Laser beam welding is increasingly being used in welding of structural steels. The laser welding process is one of the most advanced manufacturing technologies owing to its high speed and deep penetration. The thermal cycles associated with laser welding are generally much Inter than those involved in conventional welding processes, leading to a rather small weld zone. Experiments are performed for 304 stainless steel plates changing several process parameter such as laser power, welding speed, shielding gas flow rate, presence of surface pollution, with fixed or variable gap and misalignment between the similar and dissimilar and plates, etc. The Nd:YAG laser welding process is one of the most advanced manufacturing technologies owing to its high speed and penetration. This paper describes the weld ability of SM45C carbon steel for machine structural use by Nd:YAG laser. The follow conclusions can be drawn that laser power and welding speed have a pronounced effect on size and shape of the fusion zone. Increase in welding speed resulted in an increase in weld depth/aspect ratio and hence a decrease in the fusion zone size. The penetration depth increased with the increase in laser power.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.20 no.4
• /
• pp.401-406
• /
• 2011

This study presents the stress safety analysis of a cylinder, which is manufactured by a tempered ASTM D2, tempered SM45C and normalized SM45C materials, respectively. The inner diameter of three cylinder models are 85mm, 95mm, and 11 Omm and the total length of a cylinder is 2,365mm for a high pressure injection molding machine. The FEM computed results show that the inner diameter of 85mm with a thick thickness of 62.5mm may produce the injection pressure of 325MPa and the inner diameter of 110mm with 50mm thickness reduces up to the injection pressure of 220MPa because of a reduced thickness of a cylinder. These injection pressures are enough for a high pressure injection molding machine assembled by ASTM D2 cylinder. And also, an injection cylinder manufactured by a tempered SM45C material in which is low priee may produce 225MPa injection molding pressure and this may sufficiently endure stress safety compared to that of ASTM D2 cylinder material. Thus, this study recommends that tempered SM45C cylinder is appropriated for a mild injection molding machine as an alternative cylinder material when the safety strength and low prices are considered. But the normalized SM45C cylinder material does not meet a stress safety of yield strength in general.

• Journal of the Korean Society for Precision Engineering
• /
• v.20 no.7
• /
• pp.44-55
• /
• 2003

The Nd:YAG laser process is known to have high speed and deep penetration capability to become one of the most advanced welding technologies. This paper describes the machining characteristics of SM45C carbon steel welding by use of an Nd:YAG laser. In spite of its good mechanical characteristics, SM45C carbon steel has a high carbon contents and suffers a limitation in the industrial application due to the poor welding properties. The major process parameters studied in the present laser welding experiment were position of focus, travel speed and laser power. Optical microscope and SEM were used to investigate the microstructures of the welded zone. The experimental results showed that penetration depth of the welding process increases with laser power. Both the microstructural investigation and the theoretical calculations indicated that materials undergoes a very high heating and cooling cycle during welding process. It was also found that the austenite nucleation takes place at the initial stage and the completion temperature of austenite transformation is much higher than in the case of the arc welding.

• Transactions of the Korean Society of Machine Tool Engineers
• /
• v.16 no.6
• /
• pp.29-36
• /
• 2007

The present study examined the mechanical properties of the friction welding of Ni-Cr-Mo to SM45C. Friction welding was conducted at welding conditions of 2,000 rpm, friction pressure of 100MPa, friction time of 0.8, 1.0, 1.2, 1.4, 1.6, 1.8, 2.0 seconds, upset pressure of 150MPa, and upset time of 3.0 seconds. When the friction time was 1.6 seconds, the maximum tensile strength of the friction weld happened to be 1,020MPa, which is 120% of the base material's tensile strength(850MPa). At the same condition, the maximum shear strength was 438MPa, which is equivalent to 103% of the base material's shear strength(425MPa). At the same condition, the maximum vickers hardness was Hv490 at Ni-Cr-Mo nearby weld interface, which is higher Hv40 than condition of the friction time 0.8 seconds, and the maximum vickers hardness was Hv305 from weld interface of SM45C, which is higher Hv12 than condition of the friction time 0.8 seconds. The results of microstructure analysis show that the structures of two base materials have fined and rearranged along a column due to heating and axial force during friction, which has affected in raising hardness and tensile strength.

• Journal of the Korean Society for Heat Treatment
• /
• v.8 no.1
• /
• pp.44-52
• /
• 1995

The specimen for laser hardening have been carried out using SM45C which is coated with black paint or graphite for better absorption. Segmented mirror was used in order to produce a square beam ($10{\times}10mm$) at the surface with a homegeneous intensity distribution across the beam. $CO_2$-Laser power was changed from 2kW to 4kW and transfer velocity was varied from 0.1m/min to 2.0m/min. The maximum hardness and case depth of SM45C steel are 790Hv and 1.5mm by laser hardening. When the surface of specimens was melted during laser hardening. the surface hardness of SM45C steel was decreased. The surface hardness of 2 layer coated specimen(black paint: $15.4{\mu}m$, graphite coating: $9.5{\mu}m$) was increased than that of 1 layer coated specimen. It is desirable to prepare 2 or more coating layer on the steel surface in order to sufficient case depth and hardness in laser hardening. The graphite coating on the specimen surface was obtained more uniform temperature distribution than black paint coating in laser hardening process.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2001.04a
• /
• pp.1012-1015
• /
• 2001

The purpose of this paper is to evaluate the specific cutting energy characteristics during turning SM45C steel. Using the orthogonal array method the specific cutting energy has been predicted. And the significance of the equation is checked by ANOVA test. Predicted values of specific cutting energy are well concide with the measured ones. When the feed rate becaomes larger than 0.5mm/rev, predicted specific cutting energy increases.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2004.10a
• /
• pp.1369-1375
• /
• 2004

For many years and primarily for economical reasons, Dissimilar Metal Welds have been used as transition joints in a variety of equipment and applications. But Dissimilar Metal Welds have several fabrication and metallurgical drawbacks that can often lead to in-service failures. For example, the most pronounced fabrication faults are hot cracks. Laser welding techniques have been characterised for various materials. In this paper, the laser weldability of STS304 stainless steel and SM45C at dissimilar metal welds using a continuous wave Nd：YAG laser are experimentally investigated. An experimental study was conducted to determine effects of welding parameters, on eliminating or reducing the extent welding zone formation at dissimilar metal welds and to optimize those parameters that have the most influence parameters such as focus length, power, beam speed, shielding gas, and wave length of laser were tested

• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 1998.10a
• /
• pp.248-253
• /
• 1998

Recently, the uses of Ceramic/metal bonded joints, resin/metal joints, adhesive joints, composite materials which are composed of dissimiliar materials have increased in various industry fields. Since the ceramic/metal bonded joints material is made at a high temperature, residual stress distributions due to differences in material properties were investigated by varying material parameters. The two dimensional finite element analysis was performed to study residual stress distribution in Si3N4/SM45C bonded joint with a copper interlayer between the silicon nitride(Si3N4) and the structural carbon steel(SM45C) and 4-point bending tests were carried out under room temperature. Fracture surface and crack propagation path were observed using scanning electron microscope and characteristics of its fracture was discussed.