Fretting fatigue behavior of SCM420 steel commonly used in the automotive industry for structural applications was investigated in this study. In addition, the effect of bridge pad on the fretting fatigue test was evaluated from different pad materials and following conclusions were drawn. Simple fatigue limit of SCM 420 steel was determined to be 350 MPa while this value was 225 MPa and 285.5 MPa with SCM420H and with SM45C pad, respectively. Reduction in fatigue limit was, thus found to be 35.7% and 17.9% with SCM 420H pad and SM45C pad, respectively. Results of fracture surface observation revealed that typical striation pattern of fatigue failure existed as well as dimpled and cleavage frature appearance was found in final fractured region. From the EDS compositional analysis, test sample and pad part all had high signals for oxygen and iron, suggesting that worn particles might be iron oxide, although exact chemical composition has to be confirmed. Considerable reduction in fatigue life was apparent in SCM 420 steel under fretting fatigue against simple fatigue. Such reduced fatigue life by fretting damage should be considered as an important factor not only in the viewpoint of repairing but also inevitably in the design stage of structural components.