• Korean Journal of Materials Research
• /
• v.11 no.4
• /
• pp.266-271
• /
• 2001

Effect of Cd addition on the stress corrosion cracking(SCC) resistance of Al-Cu-Mn cast alloy was investigated by C-ring test and electrical conductivity measurement. With increasing Cd contents, the electrical conductivity and the SCC resistance were increased. The PFZ and coarse precipitates along the grain boundary were observed from TEM micrographs. The fracture made of the alloys was confirmed as intergranular type and showed brittle fracture surface. As a result, it was concluded that the SCC mechanism of these alloys is the anodic dissolution model. The maximum hardness was increased from 127Hv in the Cd-free alloy to 138∼145Hv in the Cd addition alloys.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.20 no.11
• /
• pp.3433-3440
• /
• 1996

This paper was investigation of the stres corrosion cracking(SCC) mechanism and the properties of corrosion fracture surface of glass fiber reinforced plastics(GFRP) produced by hand lay up(HLU) method in synthetic sea water. Test material is GFRP, that was used vinylester type epoxy acrylate resin and an unsaturated polyester as the matrix and the chopped strand mat(CSM) type E-glss fiber as the reinforcement. The slow strain rate test(SSRT) was performed on dry, wet and saturated wet specimens in sea water. Here the pH concentration of synthetic sea water was 8.2 and the strain rate is 1 x $10^{-6}$($sec^{-1}$) and test temperature ranges varied from $-60^{\circ}C$ to $80^{\circ}C$. It could be confirmed the fact that wet specimens tested at a particular test temperature ranges were appeared the eviences of SCC such as con-planar, mirror and hackle zone. Moreover, SCC of GFRP in sea water was characterised by falt fracture surfaces with only small amounts of fiber pull-out, in partial.

• Nuclear Engineering and Technology
• /
• v.17 no.3
• /
• pp.211-215
• /
• 1985

The effects of temperature and strain rate on the I-SCC behaviors of Zircaloy-4 were investigated by constant load test at 30$0^{\circ}C$ and constant elongation rate test at 300, 350 and 40$0^{\circ}C$ in 3.34mg $I_2$/㎤. The results showed that I-SCC susceptibility increased as the strain rate decreased or the temperature increased. The empirical relation between the stress and the time to failure at 30$0^{\circ}C$ was given by 1/ $t_{f}$∝exp (0.3$\sigma$/$\sigma$$_{UTS}$-31.5) When the I-SCC susceptibility was expressed by the ratio of fracture energy in iodine atmosphere to that in the inert atmosphere, severe I-SCC susceptibility was found near 7.6$\times$10$^{-6}$ sec at 30$0^{\circ}C$ and the maximum point of I-SCC susceptibility tended to shift to the higher strain rate with increasing the temperature. The quasi-cleavage fracture was observed in I-SCC fracture surface. From these results, it was certain that the film repture step was involved as an important process in the I-SCC mechanism of Zircaloy-4.4.