• International Journal of Highway Engineering
• /
• v.3 no.4 s.10
• /
• pp.117-126
• /
• 2001

In this research, evaluation of adhesion in tension property of SBR-modified concrete to ordinary portland cement concrete was conducted with uniaxial direct tensile bond test which was proposed by Kuhlmann. A test set-up was fabricated in order to minimize the eccentric force by introducing a joint which might fully rotate. The main experimental variables were cement-latex ratios, surface preparations and moisture levels. The results obtained were as follows: The LMC specimen at 15% latex-cement ratio increased the adhesion in tension by range of 37% compared to that of conventional cement concrete. This might be due to latex film formed between cement paste and aggregate. The effects of surface preparation on bond of latex modified concrete to conventional concrete were significant at the conditions by sand paper and wire brush. A better bond could be achieved by rough surface rather than smooth. The saturated and surface dry (SSD) condition were considered to be the most appropriate moisture level followed by wet, finally by dry. Thus, a proper surface preparation and moisture level are quite necessity in order to obtain better bonding at LMC overlay.

• International Journal of Highway Engineering
• /
• v.17 no.2
• /
• pp.39-46
• /
• 2015

PURPOSES: The objectives of this study were to develop a new polymer-modified emulsion for application to tack coats and to evaluate its properties by comparing it with other types of asphalt emulsions, with the goal of providing an enhanced tack coat material for use in construction. METHODS: Modified asphalt binders were developed from using SBS and SBR latex in the laboratory, and their fundamental properties, such as their penetration index and PG grade, were evaluated. Based on the properties, a new tack coat material was developed. To evaluate the newly developed asphalt emulsion, the bonding strength between the two layers of HMA was measured by applying a uniaxial tensile test and shear test. For the tests, a total of four different conditions were applied to the specimens, including the developed asphalt emulsion, latex modified asphalt emulsion, conventional asphalt emulsion, and non-tack coating. RESULTS AND CONCLUSIONS: Overall, the developed asphalt emulsion exhibits the best bonding strength behavior among all of the three types. Also, the two types of polymer-modified emulsions were found to be better for application for use as a tack coat than a conventional emulsion. Especially, at a high temperature ($50^{\circ}C$), the conventional asphalt emulsion no longer acts as a tack coating material. Therefore, the polymer-modified emulsion should be considered for application to tack coat construction during the summer.

• Elastomers and Composites
• /
• v.44 no.1
• /
• pp.22-33
• /
• 2009

Recently, elastomer-nanocomposites reinforced with low volume fraction of nanofillers have attracted great interest due to their fascinating properties. The incorporation of nanofillers, such as, layered silicate clays, carbon nanotubes, nanofibers, calcium carbonate, metal oxides or silica nanoparticles into elastomers improves significantly their mechanical, thermal, dynamic mechanical, barrier properties, flame retardancy, etc. The properties of nanocomposites depend greatly on the chemistry of polymer matrices, nature of nanofillers, and the method in which they are prepared. The uniform dispersion of nanofillers in elastomer matrices is a general prerequisite for achieving desired mechanical and physical characteristics. In this paper, current developments in the field of elastomer nanocomposites reinforced with layered silicates, silica, carbon nanotubes, nanofibers and various other nanoparticles have been addressed.

• Macromolecular Research
• /
• v.8 no.6
• /
• pp.285-291
• /
• 2000

Influence of silane coupling agent, bis-(3-(triethoxisilyl)-propyl)-tetrassulfide, on cure characteristics and bound rubber content of filled styrene-butadiene rubber (SBR) compounds and on physical properties of the vulcanizates was studied. Carbon black-filled and silica-filled compounds were compared. Content of the bound rubber increased with increased content of the silane coupling agent and this trend was shown more clearly in the silica-filled compounds. Optimum cure time of the carbon black-filled compound increased with increase of the silane content, while that of the silica-filled one decreased. Cure rate of the carbon black-filled compound became slower as the silane content increased while that of the silica-filled one became faster. By increasing the silane content, the minimum torque decreased and the delta torque increased. Physical properties of the silica-filled vulcanizate were found to be improved by adding the silane coupling agent. However, for the carbon black-filled vulcanizates, the tensile strength and tear resistance decreased with increase of the silane content. The differences between the carbon black-filled and silica-filled compounds were explained by difference in the reactivities of the fillers with the silane.

• 한국방재학회:학술대회논문집
• /
• 2010.02a
• /
• pp.46.2-46.2
• /
• 2010

아스팔트 포장의 공용성능 행장을 위해 널리 사용되고 있는 폴리머 개질 아스팔트(PMA)는 높은 생산온도와 다짐온도로 인해 생산 시 연료 소비가 많고 시공관리가 어려운 단점을 가지고 있다. 이에 중온형 아스팔트 기술을 접목하여 고온에서의 아스팔트 점도를 낮춤으로써 이와 같은 문제점을 해결하고자 하였다. 바인더의 전반적 공용성능 향상을 위해서 폴리머 (SBR)와 작업성 개선을 위해 Wax 및 기타 첨가제를 혼합하여 아스팔트 바인더를 제조하였으며, 실험결과 PG 82-22의 높은 공용등급의 바인더를 얻었으며, 생산 및 시공온도는 기존의 PMA 아스팔트와 달리 일반 스트레이트아스팔트와 비슷한 수준을 확보하였다. 이를 이용한 아스팔트 혼합물의 공용 성능 면에서도 PMA개질 아스팔트와 비슷한 수준을 나타내었다.

• Magazine of the Korea Concrete Institute
• /
• v.5 no.4
• /
• pp.145-155
• /
• 1993

The results of an experimental study on the manufacture and the mechanical properties of fiber reinforced fly ash$\cdot$lime$\cdot$gypsum composites are presented in this paper. 'The composites using fly ash, lime, and gypsum were prepared with various fibers (PAN-derived and Pitch-derived carbon fiber, alkali-resistance glass fiber) and a small amount of polymer emulsion-styrene butadiene rubber latex (SBR). As the test results show, the manufacturing process technology of fly ash$\cdot$lime$\cdot$gypsum composites was developed and its optimum mix proportions were successfully proposed. And the flexural strength and toughness of fiber reinforced fly ash$\cdot$lime $\cdot$gypsum composites were increased remarkably by fiber contents, but the compressive strength of the composites were influenced by the kinds fiber more than by the fiber contents. Also, the addition of a polymer emulsion to the composites decreased the bulk specific gravity, but the compressive and flexural strength, and the toughness of the composites were not influenced by it, but were considerably improved by increasing fiber contents.

• Journal of the Korean Wood Science and Technology
• /
• v.48 no.5
• /
• pp.755-764
• /
• 2020

Due to pronounced mechanical performance and being environmental friendly, aqueous polymer isocyanate adhesive (API) has been widely applied in the production of formaldehyde-free wood products. In this study, flame retardant formaldehyde-free plywood was prepared by incorporation of flame retardants into the API adhesive. Partially phosphorylated poly (vinyl alcohol) (PPVA) which was prepared by reacting poly (vinyl alcohol) with phosphoric acid was used to replace PVA in API formula. In addition, Mg-Al layered double hydroxides (LDH) was chosen as additive flame retardant, replacing traditional filler CaCO₃ in API adhesive formula. And then, the flame retardant API adhesive with main agent (PPVA replacing PVA70wt.%, SBR emulsion 30wt.%), curing agent 10wt.% (accounts for of the main agent), and 20wt.% LDHs (accounts of the main agent) was used to prepare flame retardant plywood. The effect of application of PPVA and Mg-Al LDH on bonding strength of plywood was investigated. The flammability characteristics of the plywood were determined by cone calorimeter test (CCT). The results revealed that compared with the plywood prepared with API adhesive, the use of PPVA and LDH enhanced the flame retardancy of plywood without negatively affecting bonding strength. The CCT tests indicated that the heat release and smoke production flame retardant API plywood were lower than those of the ordinary API glued plywood. Promising developments for flame retardant API adhesive were expected in future applications of flame retardant formaldehyde-free plywood.

• Journal of the Korea Institute of Building Construction
• /
• v.16 no.2
• /
• pp.97-105
• /
• 2016

Recently, application case of the ultra rapid hardening concrete-polymer composite(URHCPC) are increasing to repair for the deterioration of pavement. But it is a major disadvantage that the main material is expensive and has environmental load. For these reasons, the development of the economic, eco-friendly materials is needed. Calcium Aluminate Composite (CAC), produced by rapid cooling of atomizing method with molten ladle furnace slag, is a material capable of improving the economic feasibility and reducing the environmental load of URHCPC. In this paper, the properties of CAC and gypsum mixed CAC (GC) as alternative materials of RSC according to the types of polymer dispersion were studied. The results were as follows; compressive strength, tensile strength, flexural strength, bonding strength and modulus of elasticity of the composites using CAC or GC showed higher values than those of plain proportion in 3 hour. In later age, they were at the same level as the general proportions. URHCPC using BPD as polymer dispersion had superior strength properties generally. But modulus of elasticity was the same level as the case of using a SBR latex. According to these results, CAC or GC can partially substituted for RSC to product the URHCPC. When URHCPC uses the BPD as the polymer dispersion, it can be improved performance.