• Textile Coloration and Finishing
• /
• v.9 no.2
• /
• pp.41-49
• /
• 1997

To control free formaldehyde release from fabric finished with N-methylol compounds, resin finished cotton fabric was treated with resorcinol solution, dried and cured. Factors affecting to control formaldehyde release have been investigated. It was shown that the aftertreatment with resorcinol greatly suppressed the free formaldehyde release. Up to concentration of about 5% of resorcinol, the concentration of resorcinol effected on the control of free and evolved formaldehyde. And at high concentration of resorcinol, however, the concentration became rather insensitive to contol formaldehyde release. Addition of some salt catalysts such as ammonium chloride, zinc nitrate, sodium acetate and ammonium acetate, was effective in decreasing formaldehyde release. Considering the effect on the control of formaldehyde and crease recovery, ammonium acetate was concidered to be the best catalyst. It was observed that the optimum curing temperature for the resorcinol treatment was about 15$0^{\circ}C$, and that the curing time did not affected formaldehyde release over three minutes. Although the treatment of resorcinol had a little adverse effect on crease recovery of resin finished fabric, this effect could be negligible.

• Journal of the Korean Wood Science and Technology
• /
• v.21 no.1
• /
• pp.51-58
• /
• 1993

The phenol resorcinol formaldehyde resin (PRF) adhesives which are curing at ambient temperature for structural purposes were synthesized. A PRF resin is produced according to the two-stage reaction system. In first stage, a low-condensed resol or methylolated phenol were prepared from phenol by reaction with a formaldehyde in alkaline condition. The molar ratio of phenol to formaldehyde was 1.0~1.4. And in second-stage, resorcinol was added to combine with the methylol group of a low-condensed resol(R/P molar ratio 0.3). The glue-joint strength, pot-life and workability of this synthetic PRF resin were superior to conventional ambient temperature setting adhesives such as oilic urethane or water based polymer-isocyanate resin for wood adhesives.

• Analytical Science and Technology
• /
• v.11 no.3
• /
• pp.174-178
• /
• 1998

A chelating resin was prepared by the reaction of formaldehyde and resorcinol. It possesses high adsorption selectivity for transition metal ions such as Pb(II) and Ni(II). The adsorption and desorption yields of Pb(II), Ni(II), Co(II), Fe(II) and Zn(II) were determined using batch method. The significant characteristics of the chelating resin is the exchange processes between its hydrogen and metal ions. The mechanism of metal adsorption and desorption seems to be the competing protonation and complexation reaction of the functional group of the resin. This resin was applied to the rapid concentration of trace amounts of these metal ions and to the separation of Pb(II) from other metal ions in bulk solution.

• Journal of the Korean Wood Science and Technology
• /
• v.8 no.2
• /
• pp.1-5
• /
• 1980

This study is carried out to determine the scavenging effect of resorcinol added into the urea formaldehyde resin on the formaldehyde release of plywood, as the preliminary study of using the phenolic substances. The method for formaldehyde determination used in this report is the improved chromotropic acid determination. The results are summarized as follows: 1. Resorcinol added into the urea formaldehyde adhesive acts as a good scavenger. 4 percent of resorcinol reduced the formaldehyde release to less than half content. 2. Adding resorcinol gave better glue shear strength than that of control, showing the peak of the shear strength, at 2 percent and decreased to the same strength as control along its content of 4 percent. 3. Moisture content of air dried plywood met the standard very well.

• Macromolecular Research
• /
• v.8 no.3
• /
• pp.125-130
• /
• 2000

Resorcinol formaldehyde resins are synthesized by polycondensation of resorcinol with formal-dehyde and have various structures by the condensation type. The influence of polycondensation type on the stability and structure of the resorcinol formaldehyde resin was studied by molecular mechanics and molecular dynamics. The resins formed by 2,6-polycondensation and 4,6-polycondensationwith head-to-tail orientations have structures of intramolecular hydrogen bonds between 1-hydroxyl groups and between outer hydroxyl groups of the adjacent resorcinols, respectively. The resin formed by 2,6-polycon-densation with head-to-head orientation has a structure that inner hydroxyl groups cluster in the center of the molecule. Energetical stability of the resin is affected by both the intramolecular hydrogen bonds and the steric' hindrance by phenyl group.

• Carbon letters
• /
• v.5 no.4
• /
• pp.159-163
• /
• 2004

The polymer-ceramic hybrid, known as 'ceramer', was synthesized by a sol-gel process by incorporating different amount of alkoxide as source of silicon in resorcinol-formaldehyde in presence of basic catalyst to get different percentage of silicon in ultimate carbonized composites. FTIR of the ceramer confirms that it is a network of Si-O-Si, Si-O-$CH_2$ and Si-OH type groups linked with benzene ring. Different amount of silicon in the ceramer exhibits varying temperature of thermal stability and lower coefficient of thermal expansion as compared to pure resorcinol-formaldehyde resin. The lower value of CTE in ceramer is due to existence of silica and resorcinol -formaldehyde in co-continuous phase. Unidirectional composites prepared with ceramer matrix and high-strength carbon fibers show lower value of flexural strength at polymer stage as compared to those prepared with resorcinol-formaldehyde resin. However, after heat treatment to $1450^{\circ}C$, the ceramer matrix composites show large improvement in the mechanical properties, i.e. with 7% silicon in the ceramer, the flexural strength is enhanced by 100% and flexural modulus value by 40% as compared to that of pure resorcinol-formaldehyde resin matrix composites.

• Journal of the Korean Applied Science and Technology
• /
• v.24 no.1
• /
• pp.23-30
• /
• 2007

Kevlar was chemically surface modified with resorcinol-formaldehyde(RF) prepolymer and VP rubber latex for application to high strength tirecords. RF prepolymer was easily obtained by polymerization at room temperature in the presence of a base catalyst. The mechanical and thermal properties of Kevlar were not significantly changed during surface treated under various conditions. The change of adhesion with rubber were investigated through H-test method. Maximum increase of adhesion force between rubber and Kevlar was obtained up to 40% than that of untreated one when the fiber was soaked in RFL dipping solution and thermally treated at $170^{\circ}C$ for 3 - 5min.

• Journal of the Korean Wood Science and Technology
• /
• v.42 no.1
• /
• pp.34-40
• /
• 2014

The effect of neonicochid type wood preservatives on adhesive properties of resorcinol-formaldehyde resin for laminated wood manufacture was examined. By the previous studies, it was verified that the neonicochid type preservative has a high termite-proofing and anti-mold effectiveness. Commercial ACQ (ammoniacal copper quaternary compounds) and CUAZ (copper azol compounds) were used as comparison preservatives of effects on adhesive properties. The wood specimens used japanese red pine (Pinus densifrora) after application with preservatives and then bonded with resorcinol-formaldehyde resin. Adhesive properties were evaluated by shearing strength of adhesive bond and wood failure to dry condition or after accelerated aging test. Of all laminated woods, the wood specimens spread with ACQ or CUAZ showed the lowest shearing strength of adhesive bond. We estimated that the decrease of shearing strength was caused by copper in the ACQ or CUAZ preservatives. On the application of the neonicochid type preservatives, the wood specimens showed the highest shearing strength even after accelerated aging test. From these results, it is concluded that the copper-free neonicochid type preservative not affected the curing of resorcinol-formaldehyde resin.

• Macromolecular Research
• /
• v.8 no.2
• /
• pp.53-58
• /
• 2000

Stabilities and structures of resorcinol formaldehyde resins (RF resins) and their dependence on solvent were studied by molecular mechanics and molecular dynamics. Dimers to decamers of the RF resins in the conditions of dielectric constant = 1.00, 21.01, 36.64, and 80.10 were calculated. The average distance between oxygen atoms in 1-hydroxyl groups of adjacent resorcinols of the resins became longer with increased dielectric constant of the environment. The number of intramolecular hydrogen bonds of the resins decreased by increasing the dielectric constant of the environment. The RF resin structure on the surface of fabric or steel cord was explained based on the present calculation.

• Textile Coloration and Finishing
• /
• v.4 no.3
• /
• pp.116-121
• /
• 1992

This paper is on for a material to replace the petroleum-based resins used as adhesives for the fiber in rubber composite materials. The study limited to the reaction properties of tannin with formaldehyde. Tannin-formaldehyde(TF) reactions were carried out in aqueous media. Rates of reaction were strongly dependent on concentration, temperature, pH, and the mole ratio of tannin to formaldehyde. Viscosities of reaction mixtures were followed up to gelation. The reactivity of tannin-formaldehyde resins was greater than that of resorcinol-formaldehyde resins. To formulate an adhesive, a styrene-butadiene-vinyl pyridine terpolymer latex(L) was added to the TF. This preliminary results suggest that the condensed tannins have considerable promise as substitutes for resorcinol used in resin formulation for bonding of fiber to rubber.