• Proceedings of the Korean Radioactive Waste Society Conference
• /
• 2005.11a
• /
• pp.79-86
• /
• 2005

In PSR on the Kori 3&4 NPP, The low level radioactive waste resin from SGBD demineralizer is more than $65\%$ of total waste resin in NPP So, it needs to be improved. The secondary cooling water pH control methods are used ammonia-AVT from the first. According to changing ETA which is better than ammonia, SGBD cation load is increased about 2-3 times. Waste resin product is also increased in proportion to the SGBD cation load. To reduce the waste volume, new cation resin exchange criteria is confirmed that demineralizer is almost saturated.

• Magazine of the Korea Concrete Institute
• /
• v.2 no.1
• /
• pp.109-119
• /
• 1990

This study was accomplished to investigate the characteristics of hardening shrinkage and initial creep of epoxy resin concrete depending on the presence of filler. According to the test results, the hardening shrinkage was increased with increment of sLOrage temperature, and the ef¬feel of tempemture on the hardening shrinkage of epoxy resin concrete with 6% filler was more Significant than that of epoxy resin concrete without filler. Also, the initial creep strain was increased with loading times, stress--strength ratio and elastic strain, and the values for opoxy resin concrete with 6 % filler are higher than that for eposy resin concrete without filler.

• Journal of the Korean Wood Science and Technology
• /
• v.12 no.1
• /
• pp.38-43
• /
• 1984

Water soluble urea-melamine-phenol copolymer adhesive manufactured with 80 percent of urea resin contents was manufactured by different molar ratio for a high temperature curing type, and their properties and strengthes were examined through manufactures of plywood with Kapur (Dryobalanops spp.) veneers. The results are summarized as follows: 1. Specific gravities of air dried plywood manufactured from each adhesive ranged from 0.78 to 0.84 and their moisture contents met the KS requirement. 2. In dry and wet shear strength, $U_{80}M_{10}P_{10}$ copolymer resin showed the highest value and urea resin was the lowest, indicating that melamine and phenol were effective for increasing glue shear strength of urea resin. 3. In case of glue shear strength after boiling test, phenolic resin was the nest and melamine was not so effective as phenol on reinforcement of boiling water resistance of urea resin.

• Journal of the Korean Applied Science and Technology
• /
• v.28 no.2
• /
• pp.203-212
• /
• 2011

In this study we experimented that how chain extension influences to waterborne urethane-acrylic hybrid resin for leather garment coatings. We knew that polyurethane-acrylic hybrid resins had 5 grades of solvent resistance. Tensile strength measured in the polyurethane-acrylic resin(EDA 5.37 g, 1.928 kgf/$mm^2$) had the most strong strength. Also polyurethane-acylic hybrid resin(EDA 5.37 g. 30.2 mg. loss) had better result than other hybrid resins. EDA contents higher, we obtained low elongation and low flexibility. In this result, chain extension of waterborne polyurethane-acrylic hybrid resin showed the effect in leather coating with ratio of EDA.

• Journal of the Korean Applied Science and Technology
• /
• v.28 no.1
• /
• pp.109-117
• /
• 2011

In this study, we experimented that how influence chain extension to waterborne urethane-epoxy hybrid resin for leather garment coatings. First of all, We had analyzed datas by FT-IR, SEM and machanical properties. By instruments analysis measurement we confirmed that synthesis of epoxy and hybrid resin. In this experiment we knew that polyurethane-epoxy hybrid resin have 5 grades of solvent resistance. Tensile strength measured in the polyurethane-epoxy resin(EDA 5.37g, 2.386 $kg_f/mm^2$) had the most strong strength.. Also polyurethane-epoxy hybrid resin had better result(EDA 5.37g. 37.4 mg. loss) than other hybrid resins. As hight proportion of EDA in hybid resin, we obtained low elongation and low flexibility. In this result, chain extension of waterborne polyurethane-epoxy hybrid resin showed that how effect in leather coating by ratio of EDA.

• Magazine of the Korean Society of Agricultural Engineers
• /
• v.24 no.3
• /
• pp.92-99
• /
• 1982

The objective of this study was to investigate the compressive and bending strength characteristics of epoxy resin mortar, which is still in an early stage of its use and study in Korea. The results obtained are summarized as follows; 1. The compressive strengths of epoxy resin mortar after 1 day, 2 days and 3 days were gained 87%, 91% and 95%, respectively, in view of that of mortar at the age of 7 days. This result showed that the initial compressive strength within 1 day was very high. 2. The highest compressive strength of epoxy resin mortar was 914 kg/cm2 at the point of having the mixing ratio of one to two. It reached up to 3.7 times that of the normal portland cement mortar at the age of 28 days. 3. The bending strengths of epoxy resin mortar after 1 day, 2 days and 3 days came up to 88%, 93% and 97%, respectively, in comparing that of mortar at the age of 7 days. It was expressed to be simielar to the tendency of compressive strength. 4. The highest bending strength of epoxy resin mortar was 384 kg/cm2 at mixing ratio of one to two. It came up to as much as 6.5 times in comparing with that of the normal portland cement mortar at the age of 28 days. Therefore, the epoxy resin mortar would be effective for promoting the bending strength of structural members. 5. The regression equation between compressive and bending strength was obtained as follows; oo~=0.391 oc+27.54 (r=0.99) And the estimated value of bending strength was corresponded to about 44 per cent in comparing with that of the compressive strength.

• Polymer(Korea)
• /
• v.30 no.4
• /
• pp.350-356
• /
• 2006

In order to investigate the effect of the composition of weather-resistant coatings on physical properties, three different weather-resistant coatings were prepared by varying the ratio of a mill-base silicone/acrylic resin and let-down silicone/acrylic resin in weight ratios of 2 : 8, 3 : 7, and 4 : 6. The physical properties and weather-resistance of the prepared coatings were tested. It was found that the thermal stability, salt spray exposure, and weather-resistance were improved with increasing the amount of silicone. The optimum mixing ratio of mill-base silicone/acrylic resin to the let-down silicone/acrylic resin was 2 : 8. The coating containing silicone component of 30 wt% was found to be suitable as high weather-resistant coatings.

• Resources Recycling
• /
• v.24 no.3
• /
• pp.51-58
• /
• 2015

In order to recover tin from the waste tin plating solution, we used the ion exchange method using three types of ion exchange resins. The ion exchange resin with tertiary functional group(Lewatit TP 272) has not adsorption ratio of tin. The ion exchange resin with iminodiacetic functional group(Lewatit TP 207) has high adsorption ratio of tin, but impurity content in the recovered tin solution was relatively high. Whereas, in case of the ion exchange resin with functional group of ethylhexyl-phosphate(Lewatit VP OC 1026), adsorption ratio of tin was less than that of Lewatit TP 207. However, it was possible to remove impurities in the recovered tin solution by controlling the pH of the solution. High purity tin solution can be recovered by removing the organic materials with water washing process.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2002.10a
• /
• pp.185-188
• /
• 2002

An abrasive vitreous bonded solid mass having a vitrified abrasive structure comprising diamond grains which are held by an in inorganic bonding agent, the vitrified diamond wheel is impregnated with a composition which comprises a thermosetting synthetic resin and a surfactant. The vitrified diamond wheel is manufactured by preparing the composition including the resin and the surfactant, impregnating the abrasive structure with the composition, and curing the composition. The diamond wheel newly developed showed excellent performance in grinding carbide.

• Journal of the Korean Applied Science and Technology
• /
• v.37 no.5
• /
• pp.1248-1256
• /
• 2020

In this study, the polyurethane resin was synthesized by applying PTMG and DMBA of different composition ratios for the synthesis of water-dispersible polyurethane used in wound coating resin. The varying properties of the synthesized water-dispersible polyurethane were measured through tensile strength, elongation, and abrasion resistance analysis. As for the tensile strength measurement result according to the PTMG content, the sample with the highest reaction molar ratio was measured as 1.08 kgf/mm2 and the elongation was measured as 520%. As for the tensile strength result according to the DMBA content, the sample with the highest reaction molar ratio was measured as 0.51 kgf/mm2, and the elongation was measured as 435%. The degree of surface destruction by the abrasion resistance measurement was visually confirmed through SEM.