• 대한치과교정학회지
• /
• 제20권1호
• /
• pp.103-110
• /
• 1990

Metal brackets were recycled by variable methods for economic reason. Such recycling methods had a great effect on bracket slot width and bonding strength. Therefore, the recycling methods that don't change the properties of original bracket were suggested. In this study, debonded brackets were recycled with 30 kinds of solvents and bracket surfaces were examined by S.E.M. (Super IIIA, ISI International Scientific Instruments, Japan) and Stero Microscope (Sz-Tr, Olympus Tokyo, Japan) methods. The following results were obtained. 1. Thermosetting resin adhesives (eq. $Monolok^{(R)}$, $Concise^{(R)}$) were swelled most in sulfuric acid (assays 95%) and slightly in alcohol groups. 2. The solvent was exchanged every 24 hours during the brackets were recycled with sulfuric acid (assays 95%). As the passage of time, the adhesives were removed more clearly, and after 72 hours adhesives were nearly detached from bracket base. 3. Chemical recycled metal bracket surface showed no irregular structure by S.E.M. method.

• 구강회복응용과학지
• /
• 제22권2호
• /
• pp.193-202
• /
• 2006

Objective To evaluate the influence of water storage on the mechanical properties of dental adhesives over 1 and 3 months. Materials and Methods Adhesive resin sheets were prepared by pouring either All-bond 2(AB), Clearfil SE Bond(SE) into a mold measuring $15{\times}15{\times}0.9mm$. After solvent in primer evaporation, the adhesives were light-cured and removed from the mold and divided in two pieces, trimmed to hourglass shape that were used to determine the micro-tensile strength(MTS). Another hourglass shaped metal mold measuring $2.0{\times}1.5mm$ in cross-section area was made to determine the Young's modulus(E). Adhesive specimens for Young's modulus(E) were prepared in the same method. Specimens were stored at $37^{\circ}C$ in distilled water and tested after 1 and 3 months. The data were analyzed by one-way ANOVA and Tukey's test. Results Water storage significantly decreased the micro-tensile strength(MTS) of AB and SE specimens after 1 and 3 months(P<0.05). The Young's modulus(E) were also decreased after water storage for 1 and 3 months, but statistically not significant in each group of AB and SE group respectively. Conclusions Long-term exposure of adhesive resin to water can cause reduction of mechanical properties. It may compromise resin/dentin bonds and affect longevity of restorations.

• 한국인쇄학회지
• /
• 제18권1호
• /
• pp.13-24
• /
• 2000

UV-curable resin has the properties of quick-drying, high productivity at low temperature, energy, space saving, solventless, non-polluting and low-stinking, and thus, UV-curing system has been widely used in the fields of printing inks, adhesives, paints and coating agents. This study has been executed to develop a new functionnal material by the polymerization induced phase separation. The results obtained were as follows. As for the curing properties of the monomer/prepolymer/alkyd resin blends, it was found out that there was a peak by the polymerization induced phase separation when measuring the changes of viscosity and elasticity. It was also found out that such polymerization phase separation occurred in case that the alkyd resin contents were 20wt% and 30wt% and not found at the contents of 40wt%. Therefore, it would be desirable to maintain the contents of alkyd resin at less than 30wt% in order to use the polymerization induced phase separation.

• 한국섬유공학회:학술대회논문집
• /
• 한국섬유공학회 1998년도 가을 학술발표회논문집
• /
• pp.61-65
• /
• 1998

Epoxy resins are currently one of the most widely used thermoset polymers. Applications on epoxy-based materials range from common to structural adhesives as well as to matrix materials for high performance composites. The outstanding versatility of this resin can be related to the reactivity of the epoxy group, which can be opened by a large number of different chemical compounds, such a aliphatic and aromatic amines, anhydrides and poly-amides. (omitted)

• Journal of the Korean Wood Science and Technology
• /
• 제27권2호
• /
• pp.23-30
• /
• 1999

한지제지 공정 중에서 발생하는 백색슬러지와 흑색슬러지를 각각 일정비율(10:90, 20:80, 30:70, 40:60)로 목재 섬유와 혼합하고 PMDI, 요소 및 폐지수지를 이용하여 목표비중 0.60, 0.75, 0.90 별로 복합보드를 제조한 결과 전반적으로 볼 때 백색슬러지를 20% 정도까지 혼합하고 PMDI 수지를 적용하면 통상적인 보드와 유사하거나 오히려 더 좋은 치수안정성을 가지는 것으로 판단된다. 또한 흑색슬러지의 경우는 요소수지를 사용하거나 PMDI 수지의 첨가량을 증가시켜 조절한다면 20%의 슬러지 첨가량까지는 치수안정성 면에서 통상적인 보드와 큰 차이가 없는 보드를 제조할 수 있다고 믿어진다.

• Restorative Dentistry and Endodontics
• /
• 제43권2호
• /
• pp.20.1-20.9
• /
• 2018

Objectives: The aim of this in vitro study was to evaluate the bond strength of 2 universal adhesives used in different application modes to bleached enamel. Materials and Methods: Extracted 160 sound human incisors were used for the study. Teeth were divided into 4 treatment groups: No treatment, 35% hydrogen peroxide, 16% carbamid peroxide, 7.5% carbamid peroxide. After bleaching treatments, groups were divided into subgroups according to the adhesive systems used and application modes (n = 10): 1) Single Bond Universal, etch and rinse mode; 2) Single Bond Universal, self-etch mode; 3) Gluma Universal, etch and rinse mode; 4) Gluma Universal, self-etch mode. After adhesive procedures nanohybrid composite resin cylinders were bonded to the enamel surfaces. All specimens were subjected to shear bond strength (SBS) test after thermocycling. Data were analyzed using a 3-way analysis of variance (ANOVA) and Tukey post hoc test. Results: No significant difference were found among bleaching groups (35% hydrogen peroxide, 16% carbamid peroxide, 7.5% carbamid peroxide, and no treatment groups) in the mean SBS values. There was also no difference in SBS values between Single Bond Universal and Gluma Universal at same application modes, whereas self-etch mode showed significantly lower SBS values than etch and rinse mode (p < 0.05). Conclusions: The bonding performance of the universal adhesives was enhanced with the etch and rinse mode application to bleached enamel and non-bleached enamel.

• 대한치과의료관리학회지
• /
• 제9권1호
• /
• pp.7-13
• /
• 2021

The present randomized controlled trial aimed to evaluate changes in occlusion of indirect restorations before and after attachment using resin cement according to universal adhesives. This study included patients who underwent indirect restoration treatment at the Yonsei University Dental Hospital between April and October 2016. Universal adhesives requiring light curing and those not requiring light curing were used in this study. Changes in occlusion before and after adhesion of the indirect restoration were evaluated using articulating paper and shimstock as well as through the discomfort felt by the patients. To analyze the differences between the universal adhesive, Fisher's exact tests were performed using SPSS ver. 22.0 software. Of the 39 cases of indirect restoration, 29 were included in the study. A change in occlusion after adhesion of the indirect restoration was observed in only one case of universal adhesive that required light curing. The patient felt that the occlusion increased after the attachment of the restoration, and it was observed that the occlusion point was different from that before attachment. However, the results of the analysis were not statistically significant. Based on the findings, the universal adhesives did not affect the occlusion before and after indirect adhesion restoration using RelyX Ultimate.

• Journal of the Korean Wood Science and Technology
• /
• 제36권3호
• /
• pp.30-38
• /
• 2008

현재 국내에서 목질계 판상재를 생산하기 위해 사용되고 있는 석유화학계 접착제의 제조비용 상승과 포름알데히드 방산 문제로 대체 접착제의 개발이 필요한 상황이다. 따라서 본 연구에서는 대체 접착제 개발 방안의 하나인 bio-based 접착제 개발을 위하여 유기폐기물인 두부비지의 원료화 가능성을 확인하였다. 먼저 두부비지의 이화학적 성질을 조사하였고, 두부비지를 황산 또는/그리고 가성소다로 화학적으로 개량한 후 phenol formaldehyde (PF) prepolymer와 혼합하여 접착제를 조제하였으며, 그 접착제를 합판 제조에 사용하였다. 또한 제조된 합판의 접착강도 및 포름알데히드 방산량을 측정하여 합판용 접착제로서 사용가능성을 확인하였다. 본 연구에서 원료로 사용된 두부비지의 고형분 함량 및 pH는 각각 20% 내외, 약산성이었으며, 화학적 조성은 탄수화물의 함량이 가장 높았으며 다음으로 단백질을 많이 함유하고 있었다. 두부비지를 이용하여 조제된 접착제를 이용하여 제조된 합판의 인장전단강도는 KS 규격의 보통합판 품질기준을 상회하였으나, 목파율은 기준에 비해 낮은 것으로 조사되었다. 또한 포름알데히드 방산량도 KS 규격의 E1 기준보다 높은 것으로 나타났다. 따라서 두부비지가 환경친화적인 목질계 판상재료용 접착제의 원료로서 사용될 수 있다는 가능성을 보여 주었으나 접착강도의 향상과 포름알데히드 방산량 저감을 위해 두부비지의 생물학적 개량방안과 가교제로 사용된 PF prepolymer에 대한 좀 더 많은 연구가 필요하다.

• Journal of the Korean Wood Science and Technology
• /
• 제45권2호
• /
• pp.223-231
• /
• 2017

This work was conducted to investigate on the effect of urea-formaldehyde (UF) resin viscosity on plywood adhesion. The viscosity of UF resin was controlled either by adjusting the condensation reaction during its synthesis to obtain different target viscosities (100, 200 and 300 mPa.s) at two levels of formaldehyde/urea (F/U) mole ratios (1.0 and 1.2) or by adding different amounts (10, 20 and 30%) of wheat flour into the resins for the manufacture of plywood. When the viscosity of UF resin increased by the condensation reaction, the adhesion strength of plywood bonded with UF resin of 1.2 F/U mole ratio consistently increased, while those bonded with the 1.0 F/U mole ratio resin slightly decreased, suggesting a difference in the adhesion in plywood. However, the adhesion strength of plywood decreased as the viscosity increased by adding wheat flour, regardless of F/U mole ratio. The manipulation of UF resin viscosity by adjusting the condensation reaction was much more efficient than by adding wheat flour in improving the adhesion performance of plywood. These results indicated that a way of controlling the viscosity of UF resin adhesives has a great influence to their adhesion in plywood.

• 치위생과학회지
• /
• 제18권4호
• /
• pp.218-226
• /
• 2018

불소 적용 후 교정용 브라켓 접착제 종류에 따른 불소의 재흡수성과 표면의 변화를 비교 평가하고자 하였다. 불소가 방출되지 않은 복합레진 Transbond $XT^{(R)}$, 불소 방출성 복합레진 $Blugloo^{(R)}$와 $LightBond^{(R)}$, 레진강화형 글라스 아이오노머 Rely $X^{TM}$ Luting $2^{(R)}$, 재래형 글라스 아이오노머 Fuji $I^{(R)}$를 사용하였다. 시편에서 방출되는 불소 방출량을 측정하였고, 불소 재흡수 능력을 비교하기 위해서 시편에 3가지의 불소 제품(APF gel, Tooth Mousse $Plus^{(R)}$, Fluor Protector)을 도포하였으며, 불소함유 치약으로 잇솔질을 하여 불소방출량 변화를 측정하였고, 표면조도 측정기와 FE-SEM을 이용하여 시편의 표면 조도 및 변화를 비교 평가하였다. Rely $X^{TM}$ Luting $2^{(R)}$와 Fuji $I^{(R)}$에서는 다른 불소 제품인 Tooth Mousse $Plus^{(R)}$, Fluor Protector뿐만 아니라 불소함유 치약으로 잇솔질한 후에도 불소의 재흡수량을 관찰할 수 있었다. Tooth Mousse $Plus^{(R)}$를 도포한 후에는 Transbond $XT^{(R)}$를 제외하고 표면 조도 값이 유의하게 증가하였으며, 모든 교정용 접착제에서 부분적인 미세 필러 입자의 탈락을 보였다. Fluor Protector를 도포한 후에는 Transbond $XT^{(R)}$, Rely $X^{TM}$ Luting $2^{(R)}$를 제외하고 표면 조도 값이 유의하게 증가하였으며, 모든 교정용 접착제의 표면에 막을 형성하여 기포가 생긴 부분을 제외하고 매끄러운 양상을 나타내었다. 모든 교정용 접착제에 APF gel을 도포했을 때는 표면 조도 값이 유의하게 크게 증가하였다. 이상의 결과를 종합해 볼 때, 교정용 브라켓을 접착할 때 치아우식 예방 효과를 도모하기 위한 불소 방출량을 고려한다면 Rely $X^{TM}$ Luting $2^{(R)}$와 Fuji $I^{(R)}$가적극 추천되며, 불소 제품으로는 Tooth Mousse $Plus^{(R)}$, Fluor Protector가 APF gel보다 우수한 것으로 나타났고, 불소가 함유된 치약으로 잇솔질을 하였을 때도 치아우식을 예방할 수 있을 것으로 생각된다.