• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.23 no.6 s.165
• /
• pp.943-951
• /
• 1999

The welded structure unnecessarily remains residual stress due to the very high heating of local region and lastly cooling. The residual stress sometimes causes fracture initiation of welded structures. In this paper, distribution and magnitude of tensile and compressive residual stresses in the TIG(Tungsten Inert Gas) welded aluminum alloy such as Al5083-H112 are measured by using the hole-drilling method. Furthermore, the effects of residual stresses in the TIG welded aluminum CCT(Center Crack Tension) and SEN(Single Edge Notched) Specimens on the fatigue crack propagation behavior are analyzed. The fatigue cracks initiated at residual stresses region are influnced by tensile and compressive residual stresses. However, the effects are found to be released fast for both cases according to the cyclic loads and extension of crack length.

• Tribology and Lubricants
• /
• v.15 no.1
• /
• pp.39-45
• /
• 1999

The wear behavior of $Al_2$O$_3$-40%TiO$_2$deposited on casted aluminum alloy (ASTM A356) by APS (Air Plasma Spray) against SiC ball has been investigated in this work. Wear tests were carried out at room temperature. The friction coefficient of $Al_2$O$_3$-40%TiO$_2$coating is lower than that of pure $Al_2$O$_3$coating(APS). $Al_2$O$_3$-40%TiO$_2$coating indicated the existence of the optimal coating thickness. It is found that voids and pores of coating surface resulted in the generation of cracks, and the cohesive of splats and the porosity of surface play a role in wear characteristics. It is suggested that the mismatch of thermal expansion of substrate and coating play an important role in wear performance. Tension and compression under thermo-mechanical stress may be occurred by the mismatch between thermal expansion of substrate and coating. The crack propagation above interface is observed in SEM.