• Journal of Welding and Joining
• /
• 제13권4호
• /
• pp.155-162
• /
• 1995

Redistribution of residual stress and its effects during fatigue crack propagates from tensile residual stress region in weldment are investigated. Tests are performed by using welded CCT specimens of structual rolling steel (SS400) and it makes fatigue crack propagate from tensile residual stress region. For this study tension-tension loading type is selected by external loading condition and magnetizing stress indicator is used correctly to measure redistribution of residual stress according to fatigue crack growth and number of loading cycles. From this result, it is proved that redistribution of residual stress is mainly consist of residual stress released by fatigue crack growth. When fatigue crack propagates from tensile residual stress region residual stress are redistributed and it makes fatigue crack growth rate largely increase. Fatigue crack growth rate is low in case of redistributed residual stress compare with initial distributed residual stress.

• 한국레이저가공학회:학술대회논문집
• /
• 한국레이저가공학회 2006년도 춘계학술발표대회 논문집
• /
• pp.3-8
• /
• 2006

The integrity of laser welded structures is decided with fracture strength and fatigue strength. This study presents fracture behavior considering residual stress in the laser welding. Experiments are conducted and analyses are performed to explore the influence of residual stress on fracture behavior of bead-on laser welded compact specimen. Fracture experiments are performed using ASTM 1820. The performed analyses included thermo-elasto-plastic analyses for residual stress and subsequent J-integral calculation. A modified J integral is calculated in the presence of residual stresses. The J-integral is path-independent for combination of residual stress field and stress due to mechanical loading. The results indicates that the tensile residual stress near crack front bring the low fracture load while the compressive residual stress bring the high fracture load compared to no residual stress specimen. These results quantitatively understand the influence of residual stress on fracture behavior.

• 한국레이저가공학회지
• /
• 제11권2호
• /
• pp.1-7
• /
• 2008

The integrity of laser welded structures is decided in fracture strength and fatigue strength. This study made an effort to understand the fracture behavior considering residual stress. Experiments are conducted and analyses are performed to explore the influence of residual stress on fracture behavior of bead-on laser welded compact specimen. Fracture experiments are performed using ASTM 1820. The performed analyses included thermo-elasto-plastic analyses for residual stress and subsequent J-integral calculation. A modified J integral is calculated in the presence of residual stresses. The J-integral is path-independent for combination of residual stress field and stress due to mechanical loading. The results indicates that the tensile residual stress near crack front bring the low fracture load while the compressive residual stress bring the high fracture load compared to no residual stress specimen. These results quantitatively understand the influence of residual stress on fracture behavior.

• 한국압력기기공학회 논문집
• /
• 제17권2호
• /
• pp.137-144
• /
• 2021

The mode superposition time history analysis method is commonly used in a seismic analysis. The maximum response in the time history analysis can be derived by combining the responses of individual modes. The residual mode response is the response of the modes which are not considered in the time history analysis. In this paper, the residual vector method to consider the residual mode response in the time history analysis is introduced and evaluated. Seismic analyses for a sample structure model and a reactor vessel model are performed to evaluate the residual vector method. The analysis results show that residual mode response is well calculated when the residual vector method is used. It is confirmed that the residual vector method is useful and acceptable to consider the residual mode response in a seismic analysis of the nuclear power plant equipment.

• International Journal of Naval Architecture and Ocean Engineering
• /
• 제10권2호
• /
• pp.129-140
• /
• 2018

A residual stress generated in the steel structure is broadly categorized into initial residual stress during manufacturing steel material, welding residual stress caused by welding, and heat treatment residual stress by heat treatment. Initial residual stresses induced during the manufacturing process is combined with welding residual stress or heat treatment residual stress, and remained as a final residual stress. Because such final residual stress affects the safety and strength of the structure, it is of utmost importance to measure or predict the magnitude of residual stress, and to apply this point on the design of the structure. In this study, the initial residual stress of steel structures having thicknesses of 25 mm and 70 mm during manufacturing was measured in order to investigate initial residual stress (hereinafter, referred to as initial stress). In addition, thermal elastic plastic FEM analysis was performed with this initial condition, and the effect of initial stress on the welding residual stress was investigated. Further, the reliability of the FE analysis result, considering the initial stress and welding residual stress for the steel structures having two thicknesses, was validated by comparing it with the measured results. In the vicinity of the weld joint, the initial stress is released and finally controlled by the weld residual stress. On the other hand, the farther away from the weld joint, the greater the influence of the initial stress. The range in which the initial stress affects the weld residual stress was not changed by the initial stress. However, in the region where the initial stress occurs in the compressive stress, the magnitude of the weld residual compressive stress varies with the compression or tension of the initial stress. The effect of initial stress on the maximum compression residual stress was far larger when initial stress was considered in case of a thickness of 25 mm with a value of 180 MPa, while in case of thickness at 70 mm, it was 200 MPa. The increase in compressive residual stress is almost the same as the initial stress. However, if initial stress was tensile, there was no significant change in the maximum compression residual stress.

• Journal of Welding and Joining
• /
• 제5권1호
• /
• pp.42-56
• /
• 1987

Fatigue Fracture behaviors of the TIG-welded aluminum alloys, such as Al 2024-T4, A1 5050-0 and Al 7075-T7 were investigated when a crack propagated from tensile residual stress region and compressive residual stress region. The experimental values were compared with the values expected by the Forman equation. The experimental results are summarized as the following: (1) In case of fatigue crack propagation from residual stress region, the values predicted by Forman equation were Found to exactly corresponded to the experimental values. (2) When the stress intensityfactors affected by compressive residual stress, Kres, were greater than the stress intensity factors by minimum applied stresses. Kmin, the Forman equation was found to be improper to be applied directly, but the equation appeared to be proper, if the stress ratio was modified to zero. (3) The experimental results confirmed that residual stress was relaxed by repeated tensile loading and the relaxing trend was greater in case of compressive residual stress than that of tensile residual stress.

• 한국안전학회지
• /
• 제19권4호
• /
• pp.8-13
• /
• 2004

The purpose of this paper is to investigate the welding residual stress distribution according to the constraint or non-constraint welding condition with titanium commonly using power station, aircraft, and ship. The measuring method of the residual stress was applied stress release rating method with strain gages and a potable strain meter. The x direction residual stress generally showed the tensile residual stress in case of res03int welding. On the other hand, the x direction residual stress under non-restraint welding were changed tensile stress into compressive stress on 15mm away from welding bead center. Also, the y direction residual stress generally showed the tensile residual stress in case of non-restraint welding and the y direction residual stress under restraint welding were changed tensile stress into compressive stress about 60mm away from welding bead center.

• 소성∙가공
• /
• 제17권2호
• /
• pp.107-112
• /
• 2008

In order to investigate the residual stress evolution during the leveling process of hot rolled high strength coils for cold forming, the in-plane residual stress of plate sampled at SPM, rough leveler and finish leveler were measured by cutting method. Residual stress was localized near the edge of plate. As the thickness of plate was increased, the size of residual stress region was expanded. The gradient of residual stress within the plate was reduced during the leveling process. But the residual stress itself was not removed completely within the ranges of tested conditions. The exact camber of cut plate was able to be predicted by the measurement of residual stress distribution after leveling of the plate.

• Journal of Welding and Joining
• /
• 제21권7호
• /
• pp.71-77
• /
• 2003

In this study, an investigation based on the superposition principle to predict residual stress redistribution caused by crack propagation itself initially through residual tensile stress field was performed by finite element method. The tendency in residual stress redistribution caused by crack propagation recognized both from the analytical results and experimental result was the residual stress concentration consecutively occurred in the vicinity of crack tip even the situation that the crack propagated to the region initially residual compressive stress existed. The software for the analysis is ABAQUS, which is a general purpose finite element package. The analytical method that attempt to take the plastic deformation at the crack tip due to tensile residual stress into the consideration of residual stress redistribution caused by crack propagation was proposed. The plastic zone size at the tip of fatigue crack and redistributed residual stresses were calculated by finite element method on the bases of the concept of Dugdale model. Comparing these analytical results with experimental results, it is verified that the residual stress redistribution caused by crack propagation can be predicted by finite element method with the proposed analytical method.

• 품질경영학회지
• /
• 제13권2호
• /
• pp.56-60
• /
• 1985

One may be particularly interested in identifying which are the genuinely exceptional observations, in order to create a new insight into the phenomena under study. To detect outliers, many statistics have been proposed such as the maximum normed residual (MNR), a statistic equivalent to the maximum normed residual C. Daniel proposed, studentized residual, standardized residual, and so on. This paper gives a procedure for calculating critical values of the maximum modified normed residual and the distribution of the modified normed residual.