• Proceedings of the KWS Conference
• /
• 2002.10a
• /
• pp.668-674
• /
• 2002

Structural integrity assessment is indispensable for preventing catastrophic failure of industrial structures/components/facilities. This diagnosis of operating components should be done periodically for safe maintenance and economical repair. However, conventional standard methods for mechanical properties have the problems of bulky specimen, destructive and complex procedure of specimen sampling. Especially, the mechanical properties at welded zone including weldment and heat affected zone could not be evaluated individually due to their size requirement problem. So, an advanced indentation technique has been developed as a potential method for non-destructive testing of in-field structures. This technique measures indentation load-depth curve during indentation and analyzes the mechanical properties related to deformation such as yield strength, tensile strength and work-hardening index. Also indentation technique can evaluate a residual stress based on the concept that indentation load-depth curves were shifted with the direction and the magnitude of residual stress applied to materials. In this study, we characterized the tensile properties and welding residual stress of various industrial facilities through the new techniques, and the results are introduced and discussed.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.32 no.10
• /
• pp.873-881
• /
• 2008

Weld overlay is one of the residual stress mitigation methods which arrest crack initiation and crack growth. Therefore weld overlay can be applied to the region where cracking is likely to be. An overlay weld used in this manner is termed a preemptive weld overlay(PWOL). In pressurized water reactor(PWR) dissimilar metal weld is susceptible region for primary water stress corrosion cracking(PWSCC). In order to examine the effect of PWOL on residual stress mitigation, PWOL was applied to a specific dissimilar metal weld of Kori nuclear power plant by finite element analysis method. As a result, strong compressive residual stress was made in PWSCC susceptible region and PWOL was proved effective preemptive repair method for weldment.

• Journal of Welding and Joining
• /
• v.15 no.1
• /
• pp.92-100
• /
• 1997

Weld repair of ASTM A-470 class 8 high pressure (HP) steam turbine rotor steel has been performed to extend the service life of older fossil units. Microhardness measurements were conducted across the weldment from unaffected base metal (BM) to weld metal (WM). The hardness of the BM was VHN 253, however it dropped up to VHN 227 at the heat affected zone (HAZ) close to unaffected BM for multipass SAW. This area of hardness drop is called "siftening zone" and has a width of 0.5-0.6mm. During creep rupture test, failure occurred around the softening zone and rupture time was 772.4hr at 19Ksi (132 Mpa) and 593.deg. C. Multipass MIG and TIG welding have been employed to reduce the softening zone width. The softening zone width for MIG was 0.3-0.4mm and for TIG was zero-0.4mm depending on heat inputs. However creep rupture time was decreased as softening zone width reduced. Creep rupture time also showed a close relationship with heat inputs in TIG process. The higher heat input, the longer rupture time. Most failure occurred at intercritical HAZ (ICHAZ), however rupture location was shifted to coarse grained HAZ (CGHAZ) as heat input decreased. The rupture surface showed tearing and dimple which indicated transgranular fracture. fracture.