• Journal of Welding and Joining
• /
• v.20 no.3
• /
• pp.84-90
• /
• 2002

The strength and the life of welded components are affected extensively by the residual stresses distributed around their weldments not only under static loads, but also fatigue loads. The residual stress can be superimposed with externally applied loads, so that unexpected deformations and failures of members will be occurred. These residual stresses are not kept constant, but relaxed or redistributed during in service. Under static loads the relaxation takes place when the external stress superimposed with the residual stress exceeds locally the yield stress of material used. It is shown that under fatigue loads the residual stress is considerably relieved by the first or flew cycle loading, and then gradually relaxed with increasing loading cycles. In this study the phenomenon and mechanism of the stress relaxation by mechanical means were investigated and a model to predict quantitatively the residual stress relaxation for the case of static and fatigue loading condition was proposed.

• Proceedings of the KSME Conference
• /
• 2001.06a
• /
• pp.424-429
• /
• 2001

Residual stresses can be produced during manufacturing processes, eg. welding, machining and plastic working, and also in service. It can be superimposed with externally applied loads, so that unexpected deformations and failures of members will be occurred. Especially, the strength and the life of welded components are affected extensively by the residual stresses distributed around their weldments not only under static loads, but also fatigue loads. These residual stresses are not kept constant, but relaxed or redistributed during service. Under static loads the relaxation takes place when the residual stress superimposed with external stress exceeds locally the yield stress of material used. It is shown that under fatigue loads the residual stress is considerably relieved by the first or few cycle loading, and then gradually relaxed with increasing loading cycles. Although many investigations in this field have been carried out, the phenomenon and mechanism of the stress relaxation by mechanical means are still not clear, and there are few comprehensive models for predicting specific effects on the stress relaxation. In this study, the effects of applied static and fatigue loads on the residual stress relaxation were Investigated, and a model to predict quantitatively the residual stress relaxation was proposed.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.26 no.10
• /
• pp.2018-2025
• /
• 2002

It is well known that the strength and the fatigue life of welded steel components are affected extensively by welding residual stresses distributed around their weldments under not only monotonic but also cyclic loads. The externally applied loads are to be superimposed with the welding residual stresses, so that unexpected deformations and failures of the components might occur. These residual stresses are not kept constant, but relaxed or redistributed during in service. Under monotonic loads the relaxation takes place when the sum of external and welding residual stress exceeds locally the yield stress of material used. By the way, it is shown that under cyclic loads the welding residual stress is considerably relieved by the first or the early cycles of loads, and then gradually relaxed with increasing loading cycles. Although many investigations in this field have been carried out, the phenomenon and mechanism of the stress relaxation are still not clear, and there are few comprehensive models to predict amount of relaxed welding residual stress. In this study, the characteristics of the welding residual stress relaxation under monotonic and cyclic loads were investigated, and a model to predict quantitatively amount of welding residual stress relaxation was proposed.

• Proceedings of the KWS Conference
• /
• 2003.11a
• /
• pp.216-218
• /
• 2003

Most of ferrous b.c.c weld materials may experience martensitic transformation during rapid cooling after welding. And it is well known that volume expansion due to phase transformation could influence in the case of welding of high tensile strength steels on the relaxation of welding residual stress. To apply this effect practically, it is a prerequisite to establish a numerical model which is able to estimate the effect of phase transformation on residual stress relaxation quantitatively. In this study, we investigated the effect of phase transformation on the relaxation of welding residual stress through experiment. And three-dimensional thermal elastic-plastic FEM analysis is conducted to compare the effect of phase transformation on the relaxation of welding residual stress in high strength steels(POSTEN60, POSTEN80) with analytical results which is not considering the effect of phase transformation on residual stress relaxation. According to the results, the extents of welding residual stress relaxation due to phase transformation in the case of welding of POSTEN60, POSTEN80 are 0.85 $\sigma$/$\sigma$$\sub$Y0/, 0.75$\sigma$/$\sigma$$\sub$Y0/, respectively.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2006.05a
• /
• pp.191-194
• /
• 2006

Recently the quality improvement of the steel cord product is demanded by the tire market. After wire drawing process, produced residual stresses have a harmful effect on the durability of the wire and become the cause which decreases the quality of the product. Therefore, to improve the quality of the steel cord product, the research regarding the method of residual stress relaxation is necessary. To evaluate the quality of the drawn wire, it is important to measure the residual stress, because the residual stress decides a variety of the quality level which is demanded in the drawn wire. This study proposed a residual stress relaxation method in the drawn wire using FE analysis. The validity of the analysis results was verified by nanoindentation test.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.28 no.9
• /
• pp.1328-1336
• /
• 2004

According to our fatigue tests carried out at 20 Hz, R=0.1 on transversely butt-welded joints, fatigue strengths of as-welded specimens, that is, specimens having residual stress are higher than those of annealed specimens in short life range, but vice verse in long life range. This behavior seems to be concerned mainly with residual stress relaxation by applied loading. After analyzing the welding process, we conducted finite element analysis to quantify the degree of residual stress relaxation. By taking into account residual stress relaxation, modified Goodman diagram, and nominal stress, we evaluated the fatigue life of the welded joint from the S-N curve for the parent material. The estimated results are in a good agreement with the experimental results.

• Proceedings of the KSME Conference
• /
• 2004.04a
• /
• pp.108-113
• /
• 2004

According to our fatigue tests carried out at 20 Hz, R=0.1 on transversely butt~welded joints, fatigue strengths of as-welded specimens, that is, specimens having residual stress are higher than those of annealed specimens in short life range, but vice verse in long life range. This behavior seems to be concerned mainly with residual stress relaxation by applied loading. After analyzing the welding process, we conducted finite element analysis to quantify the degree of residual stress relaxation. By taking into account residual stress relaxation, modified Goodman diagram, and nominal stress, we evaluated the fatigue life of the welded joint from the S-N curve for the parent material. The estimated results are in a good agreement with the experimental results.

• Journal of Welding and Joining
• /
• v.17 no.6
• /
• pp.84-89
• /
• 1999

Most of ferrous b.c.c weld materials may experience martensitic transformation during rapid cooling after welding. It is well known that volume expansion due to the phase transformation could influence on the relaxation of welding residual stress. To apply this effect practically, it is a prerequisite to establish a numerical model which is able to estimate the effect of phase transformation on residual stress relaxation quantitatively. For this purpose, the analysis is carried out in two regions. i.e., heating and cooling, because the variation of material properties following a phase transformation in cooling is different in comparison with the case in heating, even at the same temperature. The variation of material properties following phase transformation is considered by the adjustment of specific heat and thermal expansion coefficient, and the distribution of residual stress in analysis is compared with that of experiment by previous study. consequently, in this study, simplified numerical procedures considering phase transformation, which based on a commercial finite element package was established through comparing with the experimental data of residual stress distribution by other researcher. To consider the phase transformation effect on residual stress relaxation, the transition of mechanical and thermal property such as thermal expansion coefficient and specific heat capacity was found by try and error method in this analysis.

• Proceedings of the KSME Conference
• /
• 2003.04a
• /
• pp.43-48
• /
• 2003

The problem of welding stresses and fatigue behavior is the main concerns of welding research fields. The residual stresses and distortion of structures by welding is exert negative effect on the safety of mechanical structures. That is, expansion of material by high temperature and distortion by cooling during welding process is caused of tensile and compressive residual stresses on welding material, and this residual stresses reduce fracture and fatigue strength of welding structures. The accurate prediction of residual stress and relaxation due to loading and post weld heat treatment of weld zone is very important to improve the quality of weldment. In this study, a finite element modeling technique is developed to simulate the relaxation of residual stresses due to loading and post weld heat treatment of weld zone. The accuracy of finite element models is evaluated based on experimental results and the results of the analytical solution.

• Proceedings of the KSME Conference
• /
• 2001.06a
• /
• pp.237-242
• /
• 2001

Residual stress is a dominant obstacle to efficient production and safe usage of products by reducing the mechanical strength and failure properties. Especially, it causes interfacial failure and substrate deflection in the case of thin film. So, the exact evaluation and optimum control of thin film residual stress is indispensable. However, hole drilling or X-ray diffraction techniques have some limits in application to thin film. And, curvature technique for thin film materials cannot give the information about local stress variation. Therefore, we applied the nanoindentation technique in evaluating the thin film residual stress. In this study, we modeled the change of indentation loading curve for residually stressed and stress-free thin films during stress relaxation. The value of residual stress was directly related to the indentation depth change by relaxation. The residual stress from nanoindentation analysis was consistent with the result from curvature technique.