• Bulletin of the Korean Chemical Society
• /
• 제35권1호
• /
• pp.189-196
• /
• 2014

Water dispersible ZnS based nanocrystals: ZnS (blue), ZnS:Cu (green) and ZnS:Mn (yellow-orange) were synthesized by capping the surface of the nanocrystals with a mercaptopropionic acid (MPA) molecule. The MPA capped ZnS based nanocrystal powders were characterized by using XRD, HR-TEM, EDXS, FT-IR, and FT-Raman spectroscopy. The optical properties of the colloidal nanocrystals were also measured by UV/Vis and photoluminescence (PL) spectroscopies in aqueous solvents. The PL spectra showed broad emission peaks at 440 nm (ZnS), 510 nm (ZnS:Cu) and 600 nm (ZnS:Mn), with relative PL efficiencies in the range of 4.38% to 7.20% compared to a reference organic dye. The measured average particle sizes from the HR-TEM images were in the range of 4.5 to 5.0 nm. White light emission was obtained by mixing these three nanocrystals at a molar ratio of 20 (ZnS):1 (ZnS:Cu):2 (ZnS:Mn) in water. The measured color coordinate of the white light was (0.31, 0.34) in the CIE chromaticity diagram, and the color temperature was 5527 K.

• 대한안전경영과학회지
• /
• 제4권4호
• /
• pp.137-146
• /
• 2002

In order to investigate the effect of irradiation by $^{60}Co-\gamma$rays as well as the e thermal treatment on the dielectric deterioration in ethylene propylene rubber, insulating material for electric cables used in atomic power plants, charging discharging current, residual built- up voltage and dielectric properties are measu discussed in this study. Variance in the characteristic of relative dielectric constant as a function of tem was observed in relatively high dose of irradiation. Since glass transition tem appeared at tens of degree Celsius below zero, the characteristic is attributed orientation polarization. Dielectric loss is generally increased, with increasing d irradiation in the characteristic of dielectric loss as a function of temperature, No d loss by thermal treatment was observed. Dielectric resistance decreases with increa of irradiation in the characteristic of charging current as a function of temperature be considered that dielectric resistance seems to be recovered by thermal treatm characteristic of discharging current as a function of time in the specimen less ir become similar to that of the unirradiated, when thermal treated. A peak is shown residual built- up voltage as a function of time, and the corresponding time of the shorten as increasing dose of irradiation. It is also observed that the corresponding the peak is lengthened by thermal treatment.

• 한국세라믹학회지
• /
• 제55권6호
• /
• pp.576-580
• /
• 2018

In this study, a small amount of CoO was added to commercial Gd-doped $CeO_2$ (GDC) powder. The CoO addition greatly enhanced sinterability at low temperatures, i.e., more than 98% of relative density was achieved at $1,000^{\circ}C$. When GDC/8YSZ (8 mol% yttrium stabilized zirconia) bilayers were sintered, Co-doped GDC showed excellent adhesion to the YSZ electrolyte. Transmission electron microscope (TEM) analysis showed that there were no traces of liquid films at the grain boundaries of GDC, whereas liquid films were observed in the Co-doped GDC sample. Because liquid films facilitate particle rearrangement and migration during sintering, mechanical stresses at the interface of a bilayer, which are developed based on different densification rates between the layers, might be reduced. In spite of $Co^{2+}$ doping in GDC, the electrical conductivity was not significantly changed, relative to GDC.

• 한국분말재료학회지
• /
• 제11권6호
• /
• pp.528-534
• /
• 2004

Using the nano Fe powders having 50 nm in diameter, Fe compact bodies were fabricated by injec-tion molding process. The relationship between microstructure and material properties depending on the volume ratio of powder/binder and sintering temperature were characterized by SEM, TEM techniques. In the compact body with the volume percentage ratio of 45(Fe powder) : 55(binder), which was sintered at $700^{\circ}C,$ the relative density was about $97{\%},$ and the values of volume shrinkage and hardness were about $66.3{\%}$ and 242.0 Hv, respec-tively. Using the composition of 50(Fe powder) : 50(binder) and sintered at $700^{\circ}C,$ the values of relative density, volume shrinkage and hardness of Fe sintered bodies were $73.3{\%},\;47.6{\%}$ and 152.8 Hv, respectively. They showed brittle fracture mode due to the porous and fine microstructure.

• 한국분말재료학회지
• /
• 제11권6호
• /
• pp.472-476
• /
• 2004

The Fe-Ni compact bodies were fabricated using Fe-Ni mixed powders with 50 nm in diameter by injection molding process. The relationship between microstructure and material properties was characterized with respect to the volume ratio of powder/binder and sintering temperature with SEM and TEM. In the compact body having the volume percent ratio of 45(Fe-Ni) : 55(binder), which was sintered at $900^{\circ}C$ the values of relative density and hardness were low about 97.7% and 277.1 Hv, respectively. Using the composition of 50(Fe Ni) : 50(binder) and sintered at $900^{\circ}C$, the values of relative density and hardness were 98.5%, 294.4 Hv, respec-tively. The grain size of sintered bodies strongly depended on the sintering temperature. In both samples sintered at $600^{\circ}C$ and $900^{\circ}C$, the average grain sizes were about 150 nm and 500 nm in diameter, respectively.

• 한국분말재료학회지
• /
• 제21권2호
• /
• pp.97-101
• /
• 2014

The 304 stainless steel powders were prepared by high energy ball milling and subsequently sintered by spark plasma sintering, and the microstructural characteristics and micro-hardness were investigated. The initial size of the irregular shaped 304 stainless steel powders was approximately 42 ${\mu}m$. After high energy ball milling at 800 rpm for 5h, the powders became spherical with a size of approximately 2 ${\mu}m$, and without formation of reaction compounds. From TEM analysis, it was confirmed that the as-milled powders consisted of the aggregates of the nano-sized particles. As the sintering temperature increased from 1073K to 1573K, the relative density and micro-hardness of sintered sample increased. The sample sintered at 1573K showed the highest relative density of approximately 95% and a micro-hardness of 550 Hv.

• 대한화학회지
• /
• 제53권6호
• /
• pp.677-682
• /
• 2009

본 논문에서는 ZnS:Mn/ZnS 코어-쉘 양자점을 유기금속전구체의 열분해 방법으로 합성하였다. 쉘의 형성온도를 135$^{\circ}C$로 고정한 반면 코어 나노입자의 합성 온도 조건을 다양화 하여 각 조건하에서 형성된 양자점들의 특성을 조사하였다. 실험을 통해 얻은 양자점들은 UV-Vis, 액체 photoluminescence (PL) spectroscopy 방법으로 광 특성을 조사하였으며, 또한 XRD, HR-TEM, 및 EDXS 분석으로 입자크기와 조성 등을 측정하였다. 실험 결과 가장 좋은 광 특성을 보인 나노입자의 합성조건은 코어와 쉘 모두 135$^{\circ}C$인 것으로 밝혀 졌으며, 이 조건에서 얻은 양자점은 583 nm 의 PL 발광 피이크와 42.15%의 높은 양자효율을 나타내었다. HR-TEM 으로 측정한 ZnS:Mn/ZnS 양자점의 평균 입자크기는 지름이 약 4.0 - 5.4 nm 정도였으며, 특히 150$^{\circ}C$의 온도 조건에서는 타원형의 입자가 형성되는 것이 관찰되었다.

• 한국재료학회지
• /
• 제2권5호
• /
• pp.353-359
• /
• 1992

열산화법과 PECVD법으로 p-type (100) Si 기판위에 T$a_2O_5$ 박막을 형성시킨 후 A1/T$a_2O_5$/p-Si capacitor를 제작하였다. 제작된 시편의 제반 물성은 XRD, AES, high frequency C-V analyzer, I-V meter, TEM 등을 사용하여 분석하였다. XRD 분석을 통해 T$a_2O_5$ 박막은 비정질임이 확인되었으며 65$0^{\circ}C$ 열처리의 경우에는 hexagonal $\delta$-T$a_2O_5$ 상으로 결정화가 일어남을 확인할 수 있었다. AES spectrum의 분석을 통해 T$a_2O_5$ 박막의 조성이 2:5의 stoichiometry에 근접해 있음이 관찰되었다. 열산화법에 의해 제작된 T$a_2O_5$는 산화온도 60$0^{\circ}C$의 조건에서 누설전류 5${ imes}10^{-6}$A/c$m^2와 유전상수 31.5로 가장 좋은 성질을 나타냈으며, PECVD로 제작한 T$a_2O_5$는 RF Power가 0.47W/c$m^2일 때 2.5${ imes}10^{-5}$A c$m^2and 24.0으로 가장 좋은 특성을 나타내었다. TEM 분석을 통해 제조된 박막과 계면을 관찰하였다.

• Macromolecular Research
• /
• 제11권6호
• /
• pp.418-424
• /
• 2003

Exfoliated poly(methyl methacrylate-co-styrene) [P(MMA-co-ST)]/silicate nanocomposites were synthesized through a multistep emulsion polymerization. The methyl methacrylate monomers were polymerized first and then the styrene monomers were polymerized. The nanocomposites had core-shell structures consisting of PMMA (core) and PS (shell); these structures were confirmed by $^1$H NMR spectroscopy and TEM, respectively. P(MMA-co-ST) copolymers showed two molecular weight profiles and two glass transition temperatures (T$_{g}$) in GPC and DMA measurements. At 30 $^{\circ}C$, the nanocomposites exhibited 83 and 91 % increases in their storage moduli relative to the neat copolymer because the silicate layers were dispersed uniformly in the polymer matrix.x.

• 한국분말재료학회지
• /
• 제4권2호
• /
• pp.122-132
• /
• 1997

Nanostructured(NS) W-Cu composite powders of about 20~30 nm grain size were synthesized by mechanical alloying. The properties of NS W-Cu powder and its sintering behavior were investigated. It was shown from X-ray diffraction and TEM analysis that the supersaturated solid solution of Cu in W was not formed by the mechanical alloying of mixed elemental powders, but the mixture of W and Cu particles with nanosize grains, i.e., the nanocomposite powder was attained. Nanocomposite W-20wt%Cu and W-30wt%Cu powders milled for 100 h were sintered to the relative density more than 96% and 98%, respectively, by sintering at 110$0^{\circ}C$ for 1 h in $H_2$. Such a high sinterability was attributed to the high homogeneous mixing and ultra-fine structure of W and Cu phases as well as activated sintering effect by impurity metal introduced during milling.