• Journal of Korea Foundry Society
• /
• v.22 no.5
• /
• pp.257-264
• /
• 2002

Effects of Ca content on the refinement of primary Si of Aluminum B390 alloy have been examined. Ca was found to have an effect on the refinement of primary Si particle. Primary Si particle size has been refined as Ca content of the melts decreased and cooling rate increased. A control of Ca content by the addition of $CuCl_2$ to the melt was the most efficient in the refinement of primary Si particles. The minimum size of primary Si particles in this study was $15.0\;{\mu}m$ when a residual content of Ca element in the alloy was 5ppm, Primary Si particle size was refined as primary Si crystallization temperature increased, which was attributed to the decrease of Ca content in the melts.

• Transactions of Materials Processing
• /
• v.9 no.4
• /
• pp.389-394
• /
• 2000

The studies on gram size refinement for rheocast processing of hypereutectic Al-18%Si alloys have been investigated in the present study. To increase the efficiency of mechanical stirring, sieve type stirrer are newly designed and implemented for rheocasting of hypereutectic Al-18%Si alloy. Mechanical stirring of semi-solid slurry by using sieve type mechanical stirrer results in morphological changes of the primary Si particles, from angular rod shape to near spherical shape and uniform distribution of proeutectic Si. The remarkable spheroidization of Primary Si Particles and distributional uniformity of proeutectic Si show well the efficiency of sieve type mechanical stirring method which can accelerate the coalescence-fracture-wear of the individual particles by strong turbulent flow between lattices during rotation of sieve type stirrer.

• Journal of Korea Foundry Society
• /
• v.21 no.6
• /
• pp.328-335
• /
• 2001

The objective of this study is to investigate on manufacturing Al-scrap into hypereutectic Al-Si alloy by using electromagnetic force. The Fe element in the aluminium scrap was controlled by intermetallic compound method and using EMF(electromagnetic force). The most lumped compound was found after 10min holding at $690^{\circ}C$. A number of segregated compound was revealed when imposed to EMF at 30A. The refinement of primary Si particles was achieved by EMF stirring. Primary Si particles were refined and spheroidized most of all with the magnetic intensity of 180G for 10 min.

• Journal of the Korean Society for Heat Treatment
• /
• v.18 no.3
• /
• pp.157-163
• /
• 2005

Effects of refinement of primary Si and residual stress on the mechanical properties of Aluminum B.390 alloy have been examined. Calcium was found to have an effect on the size of primary silicon particles. Primary silicon particle was refined as Ca content decreased. Refinement of primary Si particles led to an improvement in mechanical properties of the alloy; increase of elongation was prominent, above all. By the increase of compressive residual stress in the matrix alloy, tensile strength increased but elongation decreased.

• Journal of Korea Foundry Society
• /
• v.18 no.5
• /
• pp.474-480
• /
• 1998

Microstructural characteristics of semi-solid state processed hypereutectic Al-Si alloys have been investigated. Main concern of the present study is to investigate the effects of P and Sr addition on the size and morphology change of the primary Si particles. Refinement of the primary Si particles was observed with the addition of P and Sr at the early stage of semi-solid state processing, but such a refining effects became negligible resulting in Si particles with a near-spherical morphology with continuous stirring. This implies that the microstructural transformation mechanism became more dependent to stirring effects than to the alloying effects during semi-solid state processing. Brittle fracture and agglomeration were proposed as the mechanisms for microstructural alterations during semi-solid state processing.

• Journal of Korea Foundry Society
• /
• v.36 no.2
• /
• pp.53-59
• /
• 2016

The effects of ultrasonic melt treatment on the microstructures of aluminum piston were examined at five observation parts having different cooling rates. The microstructure of aluminum piston consisted of primary Si, eutectic Si, and various types of intermetallic compounds. Regardless of cooling rate, the ultrasonic melt treatment transformed dendritic eutectic cells to equiaxed eutectic cells and it decreased the sizes of eutectic Si and intermetallic compounds that exist at eutectic cell boundaries. In the absence of ultrasonic treatment, coarse primary Si particles were severely segregated and its size was increased with decreasing the cooling rate. The ultrasonic treatment decreased the size of primary Si particles from $25.5{\sim}31.0{\mu}m$ to $17.6{\sim}23.1{\mu}m$, depending on the cooling rate. In the presence of ultrasonic treatment, relatively fine primary Si particles were homogeneously distributed throughout the piston. In addition, the ultrasonic treatment increased the population density and area fraction of fine primary Si particles.

• Korean Journal of Materials Research
• /
• v.5 no.4
• /
• pp.412-419
• /
• 1995

과공정 Al-18wt%Si합금의 초정 Si입자의 미세화에 미치는 첨가원소의 영향에 관하여 조사하였다. 초정 Si입자의 크기는 P량이 증가함에 따라 미세해졌으며 적정 P량은 40ppm이었다. 최적주입온도는 AlCuP, CuP 경우 각각 75$0^{\circ}C$, 80$0^{\circ}C$이었으며 미세화 처리 후 10분 이상 경과되어도 초정 Si입자의 크기는 변화가 없었다. 또한 WDS분석 결과 초정 Si내에 AIP가 핵생성 site로 존재함을 알 수 있었다.