• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.17 no.4
• /
• pp.156-159
• /
• 2007

The red emission properties of $Mn^{4+}$ doped $SrAl_{12}O_{19}$ prepared by the solid-state reaction was investigated, in order to verify its potential to act as the red emitting phosphor of white LEDs. The emission spectrum exhibits a narrow band between $600{\sim}700 nm $ with four sharp peaks occurring at about 643, 656, 666, 671 nm due to the $^2E\to^4A_2$ transition of $Mn^{4+}$. The excitation spectrum exhibits a broad band between $200{\sim}500 nm$ with three peaks occurring at about 338, 398 and 468 nm, respectively. Moreover, the relative emission intensity of $SrAl_{12}O_{19}:Mn^{4+}$ with or without $CaF_2$ and MgO fluxes measured at excitation source 390 nm. The relative emission intensity of $SrAl_{12}O_{19}:Mn^{4+}$ containing 0.67mol% MgO was approximately 30% higher than that of the base composition sample. Strontium hexa-aluminate measured at room temperature as a function of the substituted Mg concentration. MgO was added to replace part of the $Al_2O_3$. Also, the relative emission intensity of $SrAl_{12}O_{19}:Mn^{4+}$ containing 0.67 mol% MgO and 0.67 mol% $CaF_2$ was approximately about 48% higher than that of the base composition $SrAl_{12}O_{19}:Mn^{4+}$.