• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2002.10b
• /
• pp.379-380
• /
• 2002

Steam generators (S/G) of pressurized water reactors are large heat exchangers that use the heat from the primary reactor coolant to make steam in the secondary side for driving turbine generators. Reciprocating sliding wear experiments have been performed to examine the wear properties of Incoloy 800 and Inconel 690 steam generator tubes in high temperature water. In present study, the test rig was designed to examine the reciprocating and rolling wear properties in high temperature (room temperature - $300^{\circ}C$) water. The test was performed at constant applied load and sliding distance to investigate the effect of test temperature on wear properties of steam generator tube materials. To investigate the wear mechanism of material, the worn surfaces were observed using scanning electron microscopy. At $290^{\circ}C$, wear rate of Inconel 690 was higher than that of Incoloy 800. It was assumed to be resulted from the oxide layer property difference due to the a\loy composition difference. Between 25 and $150^{\circ}C$ the wear loss increased with increasing temperature. Beyond $150^{\circ}C$, the wear loss decreased with increasing temperature. The wear loss change with temperature were due to the formation of wear protective oxide layer. From the worn surface observation, texture patterns and wear particle layers were found. As test temperature increased, the proportion of particle layer increased.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 1999.06a
• /
• pp.203-208
• /
• 1999

Friction and wear test have been performed on nylon, polyacetal, and PTFE(polytetrafluoroethylene), in reciprocating dry sliding conditions against a steel disc. According to the results, polyacetal show lowest wear rates and PTFE was found to exhibit lowest friction coefficient. The prominent wear mechanism found were adhesion and abrasion.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 1999.11a
• /
• pp.35-41
• /
• 1999

Friction and wear test was performed for nylon, acetal resin, and PTFE(polytetrafluoroethylene) under reciprocating dry sliding conditions against a steel counterpart. Friction coefficient and specific wear rate were analysed as a function of sliding distance and applied load. The worn surfaces of plate and disc specimens were observed using SEM(Scanning Electron Microscopy). The experimental results show that acetal resin exhibited lowest wear rates whereas PTFE possessed lowest friction coefficient. The prominent wear mechanisms found were adhesion and abrasion.

• Tribology and Lubricants
• /
• v.39 no.6
• /
• pp.228-234
• /
• 2023

In this study, reciprocating wear tests are performed on AISI 52100 bearing steel to investigate its tribological behavior in a hexagonal boron nitride (h-BN) water solution. The h-BN-based aqueous lubricant is prepared using an atoxic procedure called ultrasonic sonication in pure water. Ball-on-flat reciprocating sliding experiments are conducted, where the ball is slewed on a fixed flat at 50-㎛ displacement. The lubricating behavior of h-BN is compared with that of deionized (DI) water. Results show that the friction coefficient is higher in h-BN testing than that in DI tests, but the results are equalized as the friction coefficient reaches a stable level. Scanning electron microscopic images reveal significant material loss in the center and mild abrasion on the edge of the wear scar in h-BN tests. However, these effects are minor in DI water situations. The results of energy-dispersive X-ray spectroscopy show that considerable oxidation occurs in the central zone of the wear scar in h-BN cases with strong adhesion and material removal. These findings reveal the importance of determining ideal circumstances that can tolerate material friction and wear.

• Tribology and Lubricants
• /
• v.34 no.2
• /
• pp.49-54
• /
• 2018

Hydraulic reciprocating seal has been widely used to prevent fluid leakage in hydraulic systems. Also, hydraulic reciprocating seal plays a significant role to provide lubricant film at contacting interface to minimize tribological problems due to sliding with counter material. To predict lifetime of hydraulic reciprocating seal, quantitative understanding of wear characteristics with respect to operating conditions such as normal force and sliding speed is needed. In this work, effect of sliding speed on wear of polyurethane (PU) hydraulic reciprocating seal were experimentally investigated using a pin-on-disk tribo-tester. The wear characteristics of PU specimens were quantitatively determined by comparing the confocal microscope data before and after test. It was found that the wear rate of PU specimens decreased from $4.9{\times}10^{-11}mm^3$ to $1.1{\times}10^{-11}mm^3/Nm$ as sliding speed increased from 120 mm/s to 940 mm/s. Also, it was observed that the friction decreased slightly as the sliding speed increased. Improvement of lubrication state with increasing sliding speed was likely to be responsible for this enhanced friction and wear characteristics. This result also suggests that decrease in sliding distance between PU elastomer and counter materials at lower sliding speed is preferred. Furthermore, the quantitative assessment of wear characteristics of PU specimen may be useful in prediction of lifetime of PU hydraulic reciprocating seal if the allowed degree of wear for failure of the seal is provided.

• Tribology and Lubricants
• /
• v.23 no.4
• /
• pp.170-174
• /
• 2007

Wear and scuffing tests were conducted using friction and wear measurement of piston rings and cylinder blocks in low friction diesel engine. The frictional forces, wear amounts and cycles to scuffing in boundary lubricated sliding condition were measured using the reciprocating wear tester. The cylinder blocks were used as reciprocating specimens, and the piston rings with several coatings were used as fixed pin. Several coatings were used such as DLC, TiN, Cr-ceramic and TiAlN in order to improve the tribological characteristics. From the tests wear volume of piston ring surfaces applied various coatings were compared. During the tests coefficients of friction were monitored. Test results showed that DLC coatings showed good tribological properties. TiN and Cr-ceramic coated rings showed good wear resistance properties but produced high friction.

• Journal of the Korean institute of surface engineering
• /
• v.25 no.6
• /
• pp.309-317
• /
• 1992

Evaluation of electroplated gold has been carried out to obtain the data base for electrical, mechanical and environmental properties for telecommunication component applications. Gold plating was performed to a various thickness of $0.1\mu\textrm{m}$ to 1.$25\mu\textrm{m}$ after Ni plating of $3\mu\textrm{m}$ on C52100 bronze. Electrical properties were evaluated by measuring contact resistance using 4-wire method under static contact and dynamic contact during wear. Reciprocating wear test was performed to study the wear behavior as well as failure of gold contacts. Environmental characteristics were evaluated by using salt spray testing and SO2 test. Hardness of soft gold film was measured to be 53KHN under 5g load. Friction coefficient was initially obtained to be 0.15 and 0.25 under 100g and 200g loads respectively, and then raised up to 0.8 with increasing reciprocating wear cycles. Static contact resistance was 2 to 3m$\Omega$ regardless of gold film thickness while drastic changes of contact resistance were occured upon stripping of the gold film during wear. The lifetime of contact wear showing stable contact resistance increased up to 6 times for $1\mu\textrm{m}$ thickness compared to that of$ 0.1\mu\textrm{m}$ thickness under 100g load. All gold plating appeared to be stable under salt atmosphere while only the gold plating over 1$\mu\textrm{m}$ was stable under SO2 atmosphere.

• Journal of the Korean Society for Heat Treatment
• /
• v.21 no.5
• /
• pp.259-264
• /
• 2008

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.16 no.3
• /
• pp.121-126
• /
• 2006

HVOF thermal spray coating of Co-alloy T800 is progressively replacing the classical hard coatings such as chrome plating because of the very toxic $Cr^{6+}$ ion known as carcinogen causing lung cancer. For the study of the possibility of replacing of chrome plating, the wear properties of HVOF Co-alloy T800 coatings are investigated using the reciprocating sliding tester both at room and at an elevated temperature of $1000^{\circ}F\;(538^{\circ}C)$. The possibility as durability improvement coating is studied for the application to the high speed spindles vulnerable to frictional heat and wear. Wear mechanisms at the reciprocating sliding wear test are studied for the application to the systems similar to the sliding test such as high speed spindles. Wear debris and frictional coefficients of T800 coatings both at room and at an elevated temperature of $1000^{\circ}F\;(538^{\circ}C)$ are drastically reduced compared to those of non-coated surface of parent substrate Inconel 718. This study shows that the coating is recommendable for the durability improvement coatings on the surfaces vulnerable to frictional heat. The sliding surfaces are weared by the mixed mechanisms such as oxidative wear, abrasion by the sliding ball slurry erosion by the mixture of solid particles and small drops of the melts and semi-melts of the attrited particles cavitation by the relative motions among the coating, sliding ball, the melts and semi-melts. and corrosive wear. The oxide particles and the melts and semi-melts play roles as solid and liquid lubricant reducing the wear and friction coefficient.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.16 no.6
• /
• pp.273-277
• /
• 2006

High velocity of oxy-fuel (HVOF) thermal spray coating is progressively replacing the other classical hard coatings such as chrome plating and ceramic coating by the classical methods, since the very toxic $Cr^{6+}$ ion is well known as carcinogen causing lung cancer, and the ceramic coatings are brittle. Co-alloy T800 powder is coated on the Inconel 718 substrates by the HVOF coating procesess developed by this laboratory. For the study of the possibility of replacing of chrome plating, the wear properties of HVOF Co-alloy T800 coatings are investigated using the reciprocating sliding tester with a counter sliding SUS 304 ball both at room and at an elevated temperature of $1000^{\circ}F\;(538^{\circ}C)$. The possibility as durability improvement coating is studied for the application to the high speed spindles vulnerable to frictional heat and wear. Wear mechanisms at the reciprocating sliding wear test are studied far the application to the systems similar to the sliding test such as high speed spindles. Wear debris and frictional coefficients of T800 coatings both at room and at an elevated temperature of $538^{\circ}C$ are drastically reduced compared to those of non-coated surface of Inconel 718 substrates. Wear traces and friction coefficients of both coated and non-coated surfaces are drastically reduced at a high temperature of $538^{\circ}C$ compared with those at room temperature. These show that the coating is highly recommendable far the durability Improvement coating on the surfaces vulnerable to frictional heat and wear.