• Journal of the Korean Ceramic Society
• /
• v.33 no.9
• /
• pp.995-1002
• /
• 1996

The TiC-(Ni/Ti) composites were prepared by reaction bonding between TiC preforms and the melted mixture of Ni/Ti metal the atomic ratio of which were the ranges of 0.3 to 3. And their microstructures phase composi-tions and mechanical properties were investigated. During reaction bonding Ni/Ti metal mixture had a good wettability an permeability with TiC preforms and pore-free and fully dense sintered bodies were fabricated. TiC particle shape changed from spherical to angular platelet-like and grain size was grown with Ni/Ti atomic ratio increasing from 0.3 to 1. whereas grain growth of TiC particle was restrained and its shape changed gain from angular platelet-like to spherical when Ni/Ti atomic ratio was more than 2. Maximum bending strength and fracture toughness were obtained at the Ni/Ti atomic ratio being 1 their values were 582 MPa and 11.1 MPa.m1/2 respectively.

• Journal of the Korean Ceramic Society
• /
• v.35 no.10
• /
• pp.1020-1029
• /
• 1998

The reaction-bonded TiC-Ni/Si/Co composites were prepared by the melt infiltration of Co, Si, and Ni me-tal into the TiC preforms. The miocrostructure reaction composition and mechanical properties were in-vestigated. In the case of the melt infiltrated with Co and Ni TiC grain shape was changed from angular to spherical shape with the average grain size of ∼5$\mu\textrm{m}$. In the case of the melt infiltrated with Co/Si or Ni/Si, Si was reacted with TiC particles and formed SiC particles. The bending strength of both specimens which have atomic ratio of 3 were 710 MPa and 515 MPa respectively. In the case of the melt infiltrated with Ni/Si/Co,. nonstoichiometric TiC was formed and its bending strength decreased to 420 MPa.