• Korean Journal of Materials Research
• /
• v.16 no.8
• /
• pp.497-502
• /
• 2006

Recently, many attention have been focused on illite as a material for the well-being industry. Illite contains various kinds of iron bearing materials and they restrict their usage. In this study, Fe impurities in the illite produced in Yeongdong-gun, Chungcheongbuk-do were characterized and their removal experiments were performed. According to the characterization of illite raw ore, it contained 1.54 wt.%$Fe_2O_3$ due to the existence of iron oxide($Fe_2O_3$) and pyrite($FeS_2$). The raw ore was crushed into 3 mm or less using cone crusher and then ground by rod mill for the liberation of impurity mineral. For the removal of iron bearing minerals, an acid treatment, a flotation, a magnetic separation, and a flotation combined with magnetic separator were performed respectively. When the illite raw ore was treated with magnetic separation and various kinds of acid, 1.54wt.%. $Fe_2O_3$ content was reduced to 0.78 and 1.0 wt.%, respectively. On the other hand $Fe_2O_3$ content was reduced to be 0.52 wt.% after flotation. These results indicate that iron bearing minerals cannot be reduced below 0.3wt.%$Fe_2O_3$. However, combination of magnetic separation and flotation enable us to get 0.24wt.% of illite concentrate. It is concluded that, for the refinement of illite from Yeongdong-gun, the flotation combined with magnetic separation is good for high purity illite.

• KOREAN JOURNAL OF PACKAGING SCIENCE & TECHNOLOGY
• /
• v.16 no.1
• /
• pp.19-25
• /
• 2010

It is becoming increasingly important to utilize alternative raw materials for plastic industries other than petrochemical-based plastics. Cellulose derivatives were the bases of the original synthetic plastics. Cellulose and its derivatives, especially the widely used cellulose acetate (CA), constitute one of the main classes of raw materials for production on artificial fibers, films, plastics etc. CA is one of the well known polymers produced from naturally available plant substance. Many researches have focused on the isolation of cellulose from the plant cells to use them as cellulose derivatives and composite materials. Chemical and mechanical treatments provide changes on the molecular structures influencing the fundamental properties of these naturally abundant polymer. The aim of this review article is to review biodegradation, synthesis, formation, and utilization of cellulose esters, especially di-acetate, used in packaging related researches.

• Proceedings of the Korean Professional Engineer Association Conference
• /
• 1984.12a
• /
• pp.84-91
• /
• 1984

Heavy Residual Fuel oils is a mixture of reduced crude from crude unit, bottom products from vacuum and/or catalytic cracking unit with distillate to meet the specification and generally used as Heavy Fuel Oil for large combustion engines, boilers, etc…. But this study was made to investigate Heavy Residual Fuel oils for using as industrial raw material and resulted the following possibilties as valuable raw material as well as Heavy Fuel Oil. 1) Production of straight asphalt through vacuum distillation unit. 2) Using straight asphalt from vacuum distillation unit for manufacturing of Blown Asphalts, Cut Back Asphalts, Emulsified Asphalts and Asphalt Compound, etc…. 3) Using waxy oil side streams for manufacturing of raw oil to be Lube Oil base stocks through solvent dewaxing. 4) Production of lube base oils from dewaxed raw oil through chemical treatments. 5) Manufacturing of paraffine wax from slack wax to be produced as by product of dewaxing process.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.25 no.8
• /
• pp.664-669
• /
• 2012

Nano-structured one-dimensional $Na_2Ti_6O_{13}$ particles were synthesized by a molten salt process. Effects of processing parameters on the microstructure and band gap energy of the $Na_2Ti_6O_{13}$ powder were studied in this paper. For the synthesis of the $Na_2Ti_6O_{13}$ particles, two different raw materials of tubular shaped Na-titanate (Na-TiNT) and spherical shaped $TiO_2$ were utilized. Synthesizing with the raw material of Na-TiNT, around 70nm thick 1D-$Na_2Ti_6O_{13}$ with the bandgap energy of 3.5 eV was obtained at $810^{\circ}C$. Below $810^{\circ}C$ or without the presence of NaCl, 1D-$Na_2Ti_6O_{13}$ was in a relatively short in length and agglomerated state. With the processing temperature increased, the thickness of the 1D-$Na_2Ti_6O_{13}$ was also observed to be increased. On the other hand, when $TiO_2$ was employed as a raw material, the mixed amount of $Na_2CO_3$ played an important role in transforming the morphology and phase of the raw material, affecting the bandgap energy of the synthesized product. Specific surface area of the synthesized 1D-$Na_2Ti_6O_{13}$ was significantly affected by the raw and mixed materials as well as processing temperature. When Na-TiNT was processed at $810^{\circ}C$ with NaCl, the specific surface area of the 1D-$Na_2Ti_6O_{13}$ showed the best value of 30.63 $m^2/g$.

• Journal of the Korean Society of Tobacco Science
• /
• v.8 no.1
• /
• pp.13-21
• /
• 1986

The fragility, which express the fineness index, increased linearly with the moisture content for various tobacco shreds and showed a high correlation to the moisture content. Then, fineness index (FIs) at reference moisture content(l2.5%) was obtained by following equation. FIs=FIm+A(12.5-Mm) A" denote the gradient of simple linear regression equation between the fineness index and moisture content. FIm; the fineness index measured at the standard moisture content(12.5%). The characteristics of fragility concerning with some kinds of tobacco raw materials, stalk position, moisture content and storaged time were investigated. The following results were obtained. 1. The moisture content range of less fragile of tobacco raw material was from 16% to 20%. whereas the rolled process sheet tobacco was from 12% to 16%. 2. The Bright yellow and the paper process sheet tobacco were less fragile than that of the other tobacco raw materials. 3. The leaves were more distant from middle stalk position, and its become more fragile. 4. Physical properties of the storaged tobacco leaves were determined as a function of each storageunction of each storage time. The long-term storaged leaves(more than 3 years) were slightly lighter weight, more fragility and lower equilbrium moisture content than thos of the mid-term storaged leaves.(less than 3 years). 5. Contents of chemical component of the storaged leaves were determined every storage time. The long-term storaged leaves were slightly lower content of nicotine and chlorine than those of mid-term storaged leaves, but contents of crude fiber, total ash and calcium were increased significantly.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.36 no.4 s.107
• /
• pp.1-8
• /
• 2004

Linerboards and corrugating mediums are being produced using recycled old corrugated containers (OCC) as major raw materials. The utilization rate of recycled fibers is ex­pected to increase further in the future to reduce raw material cost. Use of recycled fibers as raw materials for linerboard, however, causes many problems for papermakers. As the utilization rate of recycled fiber and number of recycling of fibers increases, quality and process problems including strength reduction and deterioration of machine runn­ability will increase. To overcome the problem of strength reduction associated with the use of recycled fibrous materials for producing quality linerboards, diverse extensive research efforts and new technological approaches have been taken. In this study, disintegration characteristics of aee was evaluated by determining the unslushed contents. The amount of unslushed content of KOCC was lower than AOCC. But contaminants content of KOCC was higher than AOCC. As the consistency in disintegration increased, the amount of unslushed fiber content decreased.

• Asian-Australasian Journal of Animal Sciences
• /
• v.12 no.3
• /
• pp.460-466
• /
• 1999

The huge amount of demand for feedgrains from this region could not possibly be met by producing countries from the other regions. In order to fulfill this increasing demand for conventional raw materials, an alternative for the conventional raw materials produced in the Asia and Pacific region is becoming increasingly more important. A potential alternative is concentrates or non-conventional concentrates produced locally in relative abundance in this region. These feedstuffs include feed grains, by-products from the milling, sugar industries, brewing and distilling industries. Vegetable, citrus, and animal by-products from abattoir, feather meal and blood meal are also possibilities. In addition to more widespread use of unconventional feed sources, the following approach is recommended to improve utilization and performance. These include establishing the nutritive value of non-conventional feeds, quality control to minimize variability, proper storage and processing to assure the nutritive value and prevent mycotoxin contamination, properly balance amino acids with protein sources, supplementation with synthetic amino acids and the use of enzymes to increase digestibility. Currently, practical applications for these resources in feed formulation are negligible despite the potential. The socio-economic aspects will dominate the use of these non-conventional concentrates. In the future, the feed industry will resolve the problems in using locally available raw feed materials.

• 보존과학연구
• /
• s.21
• /
• pp.57-75
• /
• 2000

We performed the scientific analysis through composition analysis, micro-structure investigation, melting point and hardness test to the glass beads excavated at Naesanri in Gosung. Through this investigation, we could examine closely the characterization of raw materials and manufacture technique As a result of micro-structure investigation of glass beads, it appeared that the bubbles in glass beads have remained. Coloring agents of yellow glass bead was remained to the shape of inclusion. And on observing the transparent solid particle, we can know that these do not melt the raw materials because of low melting temperature of a crucible. The result of composition analysis of all glass beads using ICP, these were classified as $Na_2O_2$-$SiO_2$ type of glass. Also, these added to $AI_2O_3$ to improve the durability. The value of Vickers hardness of glass beads appeared the HV 490-530. The HV 1,440 of the transparent solid particle was much more than that of inner glass bead. This means that raw materials do not melt because of a low melting temperature of a crucible. The result of melting temperature analysis of glass beads using DSC/TGA, it was measured about $1,250^{\circ}C$.

• Korean Journal of Microbiology
• /
• v.9 no.2
• /
• pp.47-54
• /
• 1971

This study is concerned to the microbial population and its effects in the fish paste products. Experimental results were summarized as following orders ; 1) The number of bacteria in accordance with raw materials and coocking site waas known to as ; Wheat flor - $7.0{\times}10^8$/gram , Brayed fish meat - $2.0{\times}10^7$/gram, Cooking table - $6.1{\times}10^6$/$1.54cm^2$Chopped fish meat -$4.1{\times}10^6$/gram, Wooden plate - $5.5{\times}10^5$/218.32cm, Sodium chloride - $8.8{\times}10^4$/gram, Wheat starch - $4.5{\times}10^4$/gram, Fish meat - $2.3{\times}10^4$/gram. However, there were a few bacterial numbers less than 300 per gram of raw materials, such as monosodium glutamate, tap water, sugar, saccharine and eggs. 2) Bacterial population in the raw materials might be changed according to the conditions of preservation. 3) When the heat tratment is used for the preservation, the thermal effects were rarely found at the interior part of fish paste products. Conduction of heat into the interior part dose not rise about $84^{\circ}C$ and the survival of bacteria could be possible under the condition. Therefore, cooking being used requires further studies. 4) Number of bacteria in the fish paste products sold in the market was higher on April and May than those on June. Especially on June, the number of bacteriz in the interior part were found higher than those in the exterior part of the products.

• Journal of the Korean Ceramic Society
• /
• v.52 no.2
• /
• pp.154-158
• /
• 2015

This paper investigates the reaction rates of $CO_2$ that stores carbonation through comparing the carbonation behavior between $Ca(OH)_2$ and fly ash with circulating fluidized bed combustion (CFBC) containing a large amount of free CaO. Because fly ash with CFBC contains abundant free CaO, it cannot be used as a raw material for concrete admixtures; hence, its usage is limited. Thus, it has been buried until now. In order to consider its reuse, we conduct carbonation reactions and investigate its rates. X-ray diffraction (XRD), thermogravimetric/differential thermal analysis (TG/DTA), and X-ray fluorescence (XRF) are conducted for the physical and chemical analyses of the raw materials. Furthermore, we use a PH meter and thermometer to verify the carbonization rates. We set the content of the fly ash of CFBC, $Ca(OH)_2$, $CO_2$ flow rate, and water to 100 ~ 400 g, 30 ~ 120 g, 700 cc/min, and 300 ~ 1200 g, respectively, based on the content of the free CaO determined through the TG/DTA analyses. As a result, the carbonization rate of the fly ash with CFBC is the same as that of $Ca(OH)_2$, and it tends to increase linearly. Based on these results, we investigate the carbonization behavior as a function of the free CaO content contained in the raw material.