• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.05b
• /
• pp.341-344
• /
• 2005

Recently, the application of Rapid Setting Cement has been gradually increased as an important construction. However, Rapid Setting Cement shows brittle failure. Therefore, in this study, tests are carried out using Rapid Setting Cement containing fiber in order to improve such a poor property. silica-cement ratio are varied. According to experimental results, Fiber reinforced Rapid -Setting Cement showed the high ductility and strain capacity regardless of silica-cement ratio. With 0.5 silica-cement ratio, a bending strength is the highest.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2006.05b
• /
• pp.589-592
• /
• 2006

The growth in concrete structure repair has prompted major efforts to develop high early strength concrete. So, we were examined fundamental properties of cement mortar using the ordinary portland cement with rapid-setting cement. The experiments were carried out to investigate the characteristics of rapid-setting cement according to the blended ratio. The containing ratio of rapid-setting cement were changed five steps (20, 30, 50, 70, 100%) and then the flow value, setting time, compressive and bond strength test of cement mortar with RSC were investigated in this study.

• Journal of Industrial Technology
• /
• v.21 no.B
• /
• pp.301-306
• /
• 2001

Drying shrinkage cracking which may be caused by the relatively large specific surface is a matter of grave concern for latex modified concrete(LMC) overlay and rapid-setting cement latex modified concrete(RSLMC) overlay. Therefore, the purpose of this dissertation was to study the drying shrinkage properties of LMC and RSLMC with the main experimental variables such as cement types(ordinary portland cement, rapid setting cement), latex contents(0, 5, 10, 15, 20%), W-C ratios, and curing days at a same controlled environment of 60% of relative humidity and $20^{\circ}C$ of temperature. Test results revealed that the drying shrinkage of latex modified concrete(LMC), rapid-setting cement latex modified concrete(RSLMC) was considerably lower than that of ordinary portland cement concrete(OPC), rapid-setting cement concrete(RSC), respectively. This may be attributed to the interlocking of hydrated cement and aggregates by a film of latex particles, water retention due to hydrophobic and colloidal properties of the latexes, resulting in reduced water evaporation.

• Journal of the Korean Ceramic Society
• /
• v.44 no.9
• /
• pp.496-501
• /
• 2007

The properties of the polymer-modified mortars are influenced by the polymer film, cement hydrates and the combined structure between the organic and inorganic phases. Also, this quality of polymer modified cement strongly depend on weather condition. To overcome this problem, polymer-modified cement based on rapid setting cement mortars were prepared by varying polymer/cement mass ratio (P/C) with a constant water/cement mass ratio of 0.5. The effect of polymer on the hydration of this polymer cement is studied on different curing temperature. The results showed that the polymer mortar which is modified with rapid setting cement have superior physical strength properties on independent curing temperature. In addition the PIC ratio, the compressive strength, flexural strength, tensile strength and adhesion strength of mortar is enhances and polymer-modified cement based on rapid setting cement is more beneficial to the improvement of the mortar properties in jobsite.

• International Journal of Highway Engineering
• /
• v.17 no.2
• /
• pp.21-30
• /
• 2015

PURPOSES : The purpose of this study was to evaluate the performance of rapid-setting polymer-modified asphalt mixtures with a high reclaimed asphalt pavement (RAP) content. METHODS: A literature review revealed that emulsified asphalt is actively used for cold-recycled pavement. First, two types of rapid-setting polymer-modified asphalt emulsion were prepared for application to high-RAP material with no virgin material content. The quick-setting polymer-modified asphalt mixtures using two types of rapid-setting polymer-modified asphalt emulsion were subjected to the following tests: 1) Marshall stability test, 2) water immersion stability test and 3) indirect tensile strength ratio test. RESULTS AND CONCLUSIONS : Additional re-calibration of the RAP was needed for laboratory verification because the results of analyzing RAP aggregates, which were collected from different job sites, did not deviate from the normal range. The Marshall stability of each type of binder under dry conditions was good. However, the Type B mixtures with bio-additives performed better in the water immersion stability test. Moreover, the overall results of the indirect tensile strength test of RAP mixtures with Type B emulsions exceeded 0.7. Further research, consisting of lab testing and on-site application, will be performed to verify the possibility of using RAP for minimizing the closing of roadways.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.11a
• /
• pp.1029-1034
• /
• 2001

The purpose of this research is to develop rapid setting cement latex modified concrete (RSLMC) which will be used to overlay bridge deck for maintaining and repairing. The main experimental variables were the types of rapid setting cement and variation of latex and antifoam agent contents were selected as admixture factor, then the properties of workability and strength development and durability properties were investigated. The results of this study show that latex content give increment of a slump due to surface tension in polymer particles and reduce unit weight of water for preservation of workability. In addition, When no and 1.6~3.2% antifoam agent were mixed, 8%, 2.0~3.8% were respectively obtained. An increasing the amount of latex produced concrete with increased flexural strength, but with slightly lower compressive strength. Rapid chloride permeability and freezing-thawing test carried out. As a results, according to increment of containing ratio antifoamer, strength of RSLMC increase, permeability showed lower value than ignorable 100 coulombs. Also, in the case of more than antifoamer 1.6%, the relativity dynamic modulus is mantained more than 90%, but in case of 0, 5%, it decrease. In consequence, with the view of strength and workability of RSLMC, it is considered that appropriate content ratio of antifoam agent and latex solid are respectively 1.6% by latex weight, 15% by cement weight.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2002.05a
• /
• pp.323-328
• /
• 2002

Rapid set accelerators are widely used in tunnel construction, however quality criteria of and dosage are not well established. The density and solid content of admixtures, setting time and compressive strength of paste and mortar with admixtures were investigated to establish the quality criteria. While the early strength of mortar with sodium-silicate, sodium-aluminate and calcium aluminate type admixtures that have high alkali content are very high, but long-term strength are low. Aggregates of shotcrete has to be carefully selected. Sodium-silicate type admixture need longer setting time than the others.

• International Journal of Highway Engineering
• /
• v.10 no.4
• /
• pp.189-198
• /
• 2008

Generally, UFF A(Ultra Fine Fly Ash) has merit that advances a greater concrete workability and activates a greater pozzolanic reaction than common fly ash due to its ultra fine particle size. These properties enhance concrete durability by reducing permeability and increasing resistance of alkali silica reaction(ASR) and sulfate attack, etc. Due to these reasons, UFFA can be used in a rapid setting concrete. The purpose of this study is to develop and evaluate the rapid setting concrete with UFF A as a repair material for early-opening-to-traffic. In previous studies, if only UFFA is added to the rapid setting concrete mixture, pozzolanic reaction doesn't happen actively. Therefore, in this study, the chemical and physical tests were performed for rapid setting concrete with UFFA including calcium hydroxide and the activity of pozzolanic reaction was evaluated. Finally, the effectiveness of this mixture on enhancing concrete durability was investigated. As results, adding UFF A decreased the water/cement ratio of concrete, and compensated the reduced portion of the early strength of concrete. Also, rapid setting concrete with UFFA including calcium hydroxide activated a greater pozzolanic reaction than normal-UFF A concrete. As calcium hydroxide increases, electrical indication of concrete's ability to resist chloride ion penetration is promoted significantly.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2003.05a
• /
• pp.799-804
• /
• 2003

The purpose of this study was to investigate the effects of re-vibration and curing temperature onto the physical properties of latex-modified concrete with ordinary cement and rapid-setting cement, and thus to provide a guide line of re-vibration and curing conditions for good quality controls. The main experimental variables included two cement types(ordinary portland cement, rapid-setting cement), curing Temperature($10^{\circ}C$, $20^{\circ}C$, $30^{\circ}C$), re-vibration methods(continued, intermittent), and re-vibration times(initial setting, one day after mixing). The experimental results showed that the re-vibration affected little to the mechanical properties of LMC and RSLMC, while, the curing temperature a quite some. The early strength development was the highest at $20^{\circ}C$ curing temperature, and decreased at higher temperature. The permeability of concrete generally decreased with curing time. The rapid chloride permeability was a function of time and temperature. The chloride permeability of RSLMC was so small and negligible.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.17 no.2
• /
• pp.135-141
• /
• 2013

In this study, to improve the early-age compressive strength of mortar, the compressive strength tests of mortar mixed smart BFS powder added powder of rapid setting additives milled by processing, using functional grinding aid, the power-typed rapid setting cement clinker developed by sintering industrial waste and by-products with much CaO-$SiO_2-Al_2O_3$ to cement were performed. From the tests, the followings are found that (1) for BFS early-age strength improvement test (Series I): early-age strength improvement of BFS mixed rapid setting additive milled after adding functional grinding aid, when the clinker is milled, is superior and (2) for OPC early-age strength improvement test (Series II): case of additive mixed rapid setting powder typed activator milled after adding functional grinding aid to Clinker-C showed the higher compressive strength.