• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.26 no.3C
• /
• pp.219-228
• /
• 2006

In this study, a series of fire tests was carried out to evaluate fire-induced damage to structural members in tunnels. From the tests, the loss amount of concrete materials under the RWS scenario was slightly bigger than under the RABT fire scenario. Especially under the RWS fire scenario where the maximum temperature is over $1,200^{\circ}C$, the loss of concrete materials was mainly induced by melting. Generally, the loss of materials in reinforced concrete was slightly smaller than that in unreinforced concrete. Depending upon an applied fire scenario, fire-induced damage to shotcrete was quite different. From the realtime investigation of a specimen surface by a digital camcorder, it was proved that the material loss under the RABT fire scenario was mainly induced by spalling. However, it was also revealed that although fire-induced damage in the initial heating stage under the RWS was so close to that under the RABT, the material loss under the RWS at the later stage after 50 minutes elapsed since fire initiation was induced not by spalling but by melting.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2009.05a
• /
• pp.195-196
• /
• 2009

This study analyzed internal temperature of tunnel structure by standard time-temperature curves. Numerical analysis applied hydro carbon, hydro carbon modified, RABT, RWS time-temperature curves.

• Journal of Korean Tunnelling and Underground Space Association
• /
• v.7 no.2
• /
• pp.165-176
• /
• 2005

A variety of research projects have been undertaken due to the recent catastrophic tunnel fires throughout the world, Among them, more emphasis was given to full scale and scale model fire experiments, and recently the area of fire resistance of tunnel structures attract more interests, On the contrary to the cases in most of the advanced countries where design standards as well as recommendations have already been announced, no local criteria for design can be found, This paper aims at deriving the fire characteristics appropriate for the assessment criteria of fire resistance of structures in local tunnels through studying the existing fire temperature curves including ISO 834 standard temperature curve, HC curve, RWS curve, ZTV curve and EBA curve.

• Journal of Korean Tunnelling and Underground Space Association
• /
• v.10 no.4
• /
• pp.329-336
• /
• 2008

Efficient traffic network is required in urban area for good living condition. However, dense traffic network creates traffic jam and gives bad influences to the ground environment. Therefore, advanced use of underground and tunnel is required. But, in the last 20 years many tunnel fire accidents have occurred all over the world. Increase of tunnels and increase of traffics result in increase of tunnel fire. Tunnel fire creates damage to people and to the tunnel structure. Also, tunnel fire creates a big economical loss. In a mountain tunnel, the stability of the tunnel will not be disturbed by fire although the tunnel lining will get a severe damage. However, in a shield tunnel or immersed tube tunnel, cut and cover tunnel, there is a high possibility that tunnel itself will collapse by fire because their tunnel concrete lining is designed as a structural member. The aim of this experimental research is to verify the fire protection performance of newly developed cementitious material compared with the broadly used existing products in Europe and Japan. For the experiments, the general NATM tunnel concrete linings with the newly developed material were tested using fire loading curve of RABT (Maximum peak temperature is $1,200^{\circ}C$) and RWS (Maximum peak temperature is $1,350^{\circ}C$). From the test results, the newly developed fire protection material applied with 30 mm thickness showed good fire-proofing performance under RABT fire loading.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.705-708
• /
• 2008

To obtain tunnel concrete safety in case of fire, this study analyzed fire proof characteristics by fire proof method change, and the results are as follows. As a fire proof characteristics by RABT temperature heating curve, plain concrete experienced severe spalling by initial extremely high temperature. In view of fire proof method, in the cases of organic fiber mixing method and board method, spalling was prevented, and in the case of spray method, severe spalling of over 100mm depth occurred along with exposure of structural concrete including spray coat by heat stress, etc while metal lath, the stiffener, falls off. As for fire proof characteristics by RWS temperature heating curve, in case of organic fiber inclusion, concrete surface experienced fusion of within 5mm, while in the case of spray method, spray coat was severely spalled to a depth of over 100mm causing structural body concrete to expose its reinforcement, and also in the case of board method, board was fused by high temperature, causing structural body concrete be directly exposed to high temperature, which triggered overall fall-off phenomenon, so in such extraordinary high temperature heating condition, establishment of special fire proof measures is needed.

• Journal of the Society of Disaster Information
• /
• v.19 no.2
• /
• pp.262-269
• /
• 2023

Purpose: In this study,fire-resistance test were executed to evaluate the effectiveness of the fireproof panel attached to the PSC slab in tunnel. Method: For the fire resistance test, the RWS curve was applied and the furnace of the KICT was used. Result: As a result of the experiment, the maximum temperature measured on the concrete surface of the PSC slab with the fireproof panel was 321.8℃, which was lower than the damage limit temperature of 380℃ for concrete. Also, at the t=25mm, the maximum temperature was 35.2℃, which was lower than the damage temperature of steel, 250℃. The use of precast fire resistance panel(t=30mm) improves fire resistance of PSC structures. Conclusion: As a result of the test, a reinforcement method for attached a fireproof panel in case of fire in a tunnel or an underground roadway is provided to protect a structure from fire. In the future, it is necessary to perform the static performance test of the slab to which the fireproof panel is attached, and to confirm the adhesion performance of the fireproof panel by performing the pull-off test and the fatigue test.

• Journal of the Korean Society for Railway
• /
• v.13 no.2
• /
• pp.194-200
• /
• 2010

Recently, a longitudinal tunnel construction has increased because of subway construction extension, geomorphological effect and the development of construction Technologies etc. When the fire occurs in a tunnel and an underground structure, the many damage of human life and the economic losses are caused. In Korea, fire resistance character study of a tunnel and an underground structure is proceeding. However, when a concrete is exposed to high temperature, study of load carrying capacity reduction and stability evaluation for spalling of a concrete is not enough. Therefore in this study, fire resistance character of a concrete evaluated according to time heating temperature curve(RABT and RWS) and a result compared on virtual fire accident in order to apply fire scenario. Also this study performed thermo-mechanical coupled analysis of a FEM-based numerical technique and estimated fire-induced damage of a tunnel and an underground structure.

• Proceedings of the Korea Institute of Fire Science and Engineering Conference
• /
• 2009.04a
• /
• pp.506-512
• /
• 2009

최근 건설 중인 금정터널(총 연장 20.3km)이나 부산-거제간 침매터널은 화재 발생시 구조체의 강도저하로 인한 붕괴 및 사회기반시설인 교통망을 장시간 끊어놓은 등 큰 피해를 야기시킬 수 있다. 이러한 초장대터널이나 침매터널은 다른 터널보다 밀폐된 공간이므로 화재 시 단시간에 급격하게 온도상승이 일어날 수 있으며 이로 인해 구조물의 주재료인 콘크리트의 폭렬이 발생하고 구조물 내부까지 고온이 전달되어 경우에 따라 구조체의 붕괴의 원인이 되기도 한다. 따라서 본 연구에서는 콘크리트 구조체의 내화성능을 확보하기 위해 유럽에서 사용되고 있는 터널내화용 보드와 모르타르를 적용한 콘크리트의 내화성능 확보방안을 위한 시험을 수행하였다. 실험에 대한 내화성능 평가는 ITA(International Tunneling Association)에서 정한 화재 손상범위를 평가기준으로 하였고 터널화재 시나리오는 네덜란드의 TNO에 의해 실행된 실험결과를 따른 RWS 화재곡선을 이용하여 수행하였다.