• Journal of Industrial Technology
• /
• v.22 no.A
• /
• pp.161-168
• /
• 2002

Latex modified concrete is governed by both cement hydration and polymer film formation processes in its binder phase. Such the reactions are expected to improve the polymer-cement co-matrixes themselves and the bond between the cement hydrates and aggregates, and to improve the properties of hardened latex-modified concrete. The purpose of this study was to study the strength and chemical resistance of Rapid-setting latex modified concrete(RSLMC) with the main experimental variables such as latex content(0, 5, 10, 15, 20%) and water-cement ratio(36, 38, 40%) at latex content 15%. Water absorption test was earned out to estimate water permeability resistance. Chemical resistance test was carried out to measure the weight change and to observe the appearance of RSLMC immersion in hydrochloric acid, sulfuric acid, and calcium choloride.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2002.05a
• /
• pp.355-360
• /
• 2002

The purpose of this study was to remove the excessive air foaming which was produced in mixing the RSLMC(latex-modified concrete with rapid- setting cement) by choosing the best antifoam agent type and the optimized quantity for performance improved RSLMC. A series of RSLMM(latex-modified mortar with rapid-setting cement) experiments were carried out as the basic for RSLMC with the main experimental variables such as antifiamer types(A, B, C, D), antifoamer contents(0, 1, 2, 3%). Air content test and compressive, flexural tests were carried out to measure the improved properties of RSLMM and RSLMC. Chloride ion permeability test was carried out to estimate water permeability resistance. The results of RSLMM showed that the decrease of 50% air content was obtained by admixturing a antifoam agent by 1%. The compressive strength and flexural strength at 3 hours after RSLMC placement were 235kgf/cm$^2$ and 49kgf/cm$^2$, respectively, which exceeded the flexural strength criterion of 45kgf/cm$^2$ in order to open the RSLMC placed to traffic. The chloride permeability using A and C antifoamer at 28 days were below 100 coulombs, which was the permeability rating of negligible according to ASTM.

• Journal of the Korea Concrete Institute
• /
• v.15 no.1
• /
• pp.95-101
• /
• 2003

Drying shrinkage cracking which may be caused by the relatively large specific surface is a matter of grave concern for latex modified concrete(LMC) overlay and rapid-setting cement latex modified concrete(RSLMC) overlay. LMC and RSLMC were studied for field applications very actively in terms of strength and durability in Korea. However, there were no considerations in drying shrinkage. Therefore, the purpose of this dissertation was to study the drying shrinkage properties of LMC and RSLMC with the main experimental variables such as cement types(ordinary portland cement, rapid setting cement), latex contents(0, 5, 10, 15, 20%) and curing days at a same controlled environment of 60% of relative humidity and $20^{\circ}C$ of temperature. The drying shrinkage for specimens was measured with a digital dial gauge of Demec. The test results showed that the drying shrinkage of LMC and RSLMC were considerably lower than that of OPC and RSC, respectively. This might be attributed to the interlocking of hydrated cement and aggregates by a film of latex particles, water retention due to hydrophobic, and colloidal properties of the latexes resulting in reduced water evaporation.

• Journal of the Korea Concrete Institute
• /
• v.14 no.3
• /
• pp.299-306
• /
• 2002

The purpose of this research was to develop a rapid setting cement latex modified concrete (RSLMC) for bridge deck repairing and overlaying. The main experimental variables were latex contents, antifoamer contents and water-cement ratioes. The workability, strength development and permeability were measured as responses. The results showed that latex content increased the slump and reduced the unit water required for same workability. The air contents were measured as 8.0∼9.0％ and 2.0∼3.0％ without antifoamer and with 1.6∼3.2％ of antifoamer, respectively. This resulted in the increment of compressive strength development by 10∼20 ％. The flexural strength of RSLMC increased greatly as the latex content increased, but not in compressive strength. The compressive strength and flexural strength developed enough for opening the overlayed RSLMC to the traffic after 3 hours of RSLMC placement. The permeability of RSLMC was evaluated as negligible due to its very low charge passed. Thus, RSLMC could be used at repairing or overlaying the concrete bridge deck at fast-track job sites.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2002.05a
• /
• pp.151-156
• /
• 2002

Drying shrinkage cracking which may be caused by the relatively large specific surface is a matter of grave concern for latex modified concrete(LMC) overlay and rapid-setting cement latex modified concrete(RSLMC) overlay. LMC and RSLMC were studied for field applications very actively in terms of strength and durability in Korea. However, there were no considerations in drying shrinkage. Therefore, the purpose of this study was to investigate the drying shrinkage properties of LMC and RSLMC with the main experimental variables such as cement types(ordinary portland cement, rapid setting cement), latex contents(0, 5, 10, 15, 20%), W-C ratios, and curing days at a controlled environment of 60% of relative humidity and 2$0^{\circ}C$ of temperature. The drying shrinkage for specimens was measured with a digital dial gauge of Demec. The test results showed that the drying shrinkage of LMC and RSLMC were considerably lower than that of OPC and RSC, respectively. This might be attributed to the interlocking of hydrated cement and aggregates by a film of latex particles, water retention due to hydrophobic, and colloidal properties of the latexes resulting in reduced water evaporation.

• International Journal of Highway Engineering
• /
• v.4 no.2 s.12
• /
• pp.1-8
• /
• 2002

Latex modified concrete(LMC) became to be applied as a new material for newly constructed bridge deck overlays in Korea due to its excellent bond strength, flexural strength and impermeability against water and chloride. However, it could not be adopted at repair job site because of its long curing time required. Thus, a research on latex modified concrete with rapid-setting cement(RSLMC) is necessary if it could develope the sufficient strength for early opening to traffic. This study focused on the durability of latex modified concrete with rapid-setting cement mainly on water permeable resistance and freeze-thaw resistance. The main experimental variables were latex contents(0, 5, 10, 15 and 20%) and antifoamer contents (0, 1.6, 3.2, 4.8 and 6.4%). Test results show that the permeability of RSLMC is very low indicating below 100 coulombs at 15% of latex contents at all antifoamer contents. The freeze-thaw resistance of RSLMC maintains above 90% of relative dynamic modulus at 3.2% of antifoamer content until 300 freezing-thawing cycles.

• Journal of Industrial Technology
• /
• v.22 no.A
• /
• pp.193-200
• /
• 2002

Drying shrinkage cracking which may be caused by the relatively large specific surface IS a matter of grave concern for latex modified concrete(LMC) overlay and rapid-setting cement latex modified concrete(RSLMC) overlay. LMC and RSLMC were studied for field applications very actively in terms of strength and durability in Korea. However, there were no considerations in drying shrinkage. Therefore, the purpose of this dissertation was to study the drying shrinkage properties of LMC and RSLMC with the main experimental variables such as cement types(ordinary portland cement, rapid setting cement), water-cement ratios and curing days at a same controlled environment of 60% of relative humidity and $20^{\circ}C$ of temperature The drying shrinkage for specimens was measured with a digital dial gauge of Demec. The test results showed that the drying shrinkage of LMC and RSLMC were considerably lower with low water-cement ratio, respectively This might be attributed to the interlocking of hydrated cement and aggregates by a film of latex particles, water retention due to hydrophobic, and colloidal properties of the latexes resulting in reduced water evaporation.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.11a
• /
• pp.1029-1034
• /
• 2001

The purpose of this research is to develop rapid setting cement latex modified concrete (RSLMC) which will be used to overlay bridge deck for maintaining and repairing. The main experimental variables were the types of rapid setting cement and variation of latex and antifoam agent contents were selected as admixture factor, then the properties of workability and strength development and durability properties were investigated. The results of this study show that latex content give increment of a slump due to surface tension in polymer particles and reduce unit weight of water for preservation of workability. In addition, When no and 1.6~3.2% antifoam agent were mixed, 8%, 2.0~3.8% were respectively obtained. An increasing the amount of latex produced concrete with increased flexural strength, but with slightly lower compressive strength. Rapid chloride permeability and freezing-thawing test carried out. As a results, according to increment of containing ratio antifoamer, strength of RSLMC increase, permeability showed lower value than ignorable 100 coulombs. Also, in the case of more than antifoamer 1.6%, the relativity dynamic modulus is mantained more than 90%, but in case of 0, 5%, it decrease. In consequence, with the view of strength and workability of RSLMC, it is considered that appropriate content ratio of antifoam agent and latex solid are respectively 1.6% by latex weight, 15% by cement weight.

• Journal of Industrial Technology
• /
• v.24 no.A
• /
• pp.165-171
• /
• 2004

Latex modification of concrete provides the material with higher flexural strength, as well as high bond strength and reduced water permeability. However, If the thermal expansion properties of overlay concrete (latex-modified concretes) are big different from that of substrate (ordinary portland cement concrete), these would cause a big interfacial stresses and result in premature failure. Therefore, the purposes of this study were to investigate thermal expansion characteristics of latex-modified concrete with cement types. The result of thermal expansion showed the coefficient of thermal expansion of concretes increased with latex inclusion. The coefficient of thermal expansion of RSLMC was a little smaller than that of LMC, which might be due to the finer cement grain, compacter internal, and stiffer properties of concrete. However, the coefficients of LMC and RSLMC were quite similar to that of ordinary cement concrete. Thus, this would not cause an interfacial stresses and will enable to ensure long-term performance of concrete bridge deck overlays.

• Journal of Industrial Technology
• /
• v.21 no.B
• /
• pp.301-306
• /
• 2001

Drying shrinkage cracking which may be caused by the relatively large specific surface is a matter of grave concern for latex modified concrete(LMC) overlay and rapid-setting cement latex modified concrete(RSLMC) overlay. Therefore, the purpose of this dissertation was to study the drying shrinkage properties of LMC and RSLMC with the main experimental variables such as cement types(ordinary portland cement, rapid setting cement), latex contents(0, 5, 10, 15, 20%), W-C ratios, and curing days at a same controlled environment of 60% of relative humidity and $20^{\circ}C$ of temperature. Test results revealed that the drying shrinkage of latex modified concrete(LMC), rapid-setting cement latex modified concrete(RSLMC) was considerably lower than that of ordinary portland cement concrete(OPC), rapid-setting cement concrete(RSC), respectively. This may be attributed to the interlocking of hydrated cement and aggregates by a film of latex particles, water retention due to hydrophobic and colloidal properties of the latexes, resulting in reduced water evaporation.