• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1996.05a
• /
• pp.193-197
• /
• 1996

BaTiO$_3$films in pure Ar atmosphere were prepared by RF sputtering method at low substrate temperature(100$^{\circ}C$). The structural and crystallographic properties were studied with deposition conditions and annealing methodes. Deposition rates and structural properties of BaTiO$_3$ thin filles were investigated by the SEM and X-ray diffraction. The chemical composition of BaTiO$_3$ thin films grown on Si(100) wafer was studied by tole EDS and EPHA. The optimised Ar pressure and RF power were 8[mtorr] and 180[W], respectively. The thickness of BaTiO$_3$ thin films deposited at optimised conditions was ∼3400[${\AA}$], and the dielectric constant of the thin films heat-treated at 750[$^{\circ}C$] for 1[hr] was 259.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.14 no.3
• /
• pp.234-240
• /
• 2001

Using RF magnetron sputtering, amorphous carbon(a-C) thin films as electron filed emitter were fabricated. these a-C thin films were deposited on Si(001) substrate at several temperatures. The field electron emission property of these a-C thin films was estimated by a diode technique. As the result, we observed that the field emission properties of the films were changed singnificantly with the substrate temperature and structural features of a-C film. The field emission properties were promoted by higher substrate temperatures. Furthermore N-doped a-C film exhibits more field emission property than that of undoped a-C film. These results are explained as change of surface morphology and structural properties of a-C film.

• Korean Journal of Materials Research
• /
• v.12 no.1
• /
• pp.82-88
• /
• 2002

Chromium carbide films were deposited on high speed steels using a Cr_3C_2$ target by magnetron sputtering. Effects of the deposition parameters (power, Ar pressure and substrate temperature) on deposition rates and surface roughnesses of the films were investigated. The morphologies of those films were characterized by scanning electron microscopy and atomic force microscopy. The grain size of the samples deposited using dc-power is larger than that using equivalent rf-power. The hardness of the sample increases with increasing rf-power, whereas the elastic modulus nearly does not change with rf-power. The optimum sputter deposition conditions for chromium carbide on high speed steels in the corrosion resistance aspect were found to be the rf-power with small roughness.

• Proceedings of the KIEE Conference
• /
• 2004.07c
• /
• pp.1621-1623
• /
• 2004

The $Pb(Zr_{0.52}Ti_{0.48})O_3/(Ba_{0.6}Sr_{0.4})TiO_3$ [PZT(52/48)/BST(60/40)] heterolayered thin films were deposited on Pt/Ti/$SiO_2$/Si substrates by using the RF sputtering method with RF powers of 60,70,80,90[W]. All thin films showed the peaks of the tetragonal phase. Increasing the RF power, dielectric constant and loss of the PZT(52/48)/BST(60/40)] heterolayered thin films were decreased. The thickness ratio of PZT and BST thin films was 1/1. The relative dielectric constant and the dielectric loss of the PZT(52/48)/ BST(60/40) heterolayered thin films were 562 and 13%, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.1001-1004
• /
• 2001

The (Sr$_{l-x}$Ca$_{x}$)TiO$_3$(SCT) thin films are deposited on Pt-coated electrode(Pt/TiN/SiO$_2$/Si) using RF sputtering method with substitutional contents of Ca. The maximum grain of thin films is obtained by substitution of Ca at 15[mol%]. The dielectric constant was increased -with increasing the substitutional contents of Ca, while it was decreased if the substitutional contents of Ca exceeded over 15[mol%]. The dielectric constant changes almost linearly in temperature ranges of -80~+90[$^{\circ}C$]. The temperature properties of the dielectric loss have a stable value within 0.02 independent of the substitutional contents of Ca. The current-voltage characteristics of SCT15 thin films showed the increasing leakage current as the measuring temperature increases.ses.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.18 no.11
• /
• pp.977-982
• /
• 2005

Al/AlN/n-type 6H-SiC (0001) MIS structures were prepared by AlN layers on vicinal 6H-SiC(0001) substrates with reactive RF magnetron sputtering method. The AlN films were annealed at $900^{\circ}C$, $N_2$ atmosphere lot 1 minutes showed the best result. With XRD analysis, AlN(0002) peak was clearly found. The typical dielectric constant value of the AlN film in the MIS capacitors was obtained as 8.4 from photo C-V. Also, the gate leakage current density of the MlS capacitor was $10^{-10}\;A/cm^2$ order within the electric field of 1.8 MV/cm. Finally, the amount of interface trap densities, $D_{it}$, was evaluated as $5.3\times10^{10}\;eV^{-1}cm^{-2}$ at (Ec-0.85) eV.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07b
• /
• pp.624-627
• /
• 2003

The BLT thin-films were one of the promising ferroelectric materials with a good leakage current and degradation behavior on Pt electrode. The BLT target was sintered at $1100^{\circ}C$ for 4 hours at the air ambient. $Bi_{3.25}La_{0.75}Ti_3O_{12}$ (BLT) thin-film deposited on $Pt/Ti/SIO_2/Si$ wafer by rf magnetron sputtering method. At annealed $700^{\circ}C$, (117) and (006) peaks appeared the high intensity. The hysteresis loop of the BLT thin films showed that the remanent polarization ($2Pr=Pr^+-Pr^-$) was $16uC/cm^2$ and leakage current density was $1.8{\times}10^{-9}A/cm^2$ at 50 kV/cm with coersive electric field when BLT thin-films were annealed at $700^{\circ}C$. Also, the thin film showed fatigue property at least up to $10^{10}$ switching bipolar pulse cycles under 7 V. Therefore, we induce access to optimum fabrication condition of memory device application by rf-magnetron sputtering method in this report.

• Journal of the Korean Vacuum Society
• /
• v.5 no.2
• /
• pp.139-146
• /
• 1996

Transparent and conducting Sb-doped $SnO_2$ thin films were prepared by rf magnetron sputtering technology. But it showed a serious damage phenomenon on the surface of as-deposited films. In order to avoid a damage caused in the substrate center and location facing to target erosion, a ring plate of masking glass was installed at 1.5 cm above target surface. The uniformity and electrical characteristic of $SnO_2$ thin films were evaluated by the control of optimal conditions in the magnetron sputtering operation such as rf power, sputtering gas pressure, and substrate temperature. In the experimental results using the operating conditions, the optimum temperature, which produced uniform and damageless films, shifted with the change of gas pressure. The rate was about $100^{\circ}C$/5 mTorr at rf power of 50 W Similarly, the optimum temperature in compensation for an increase of rf power shifted down to a proper rate.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.51-54
• /
• 2000

In this paper, $Ba_{0.5}$Sr$_{0.5}$TiO$_3$ thin films were prepared on Pt/Ti/SiO$_2$/Si substrate by RF magnetron sputtering method. We investigated effect of deposition conditions (especially RF input power) on structural properties of BST thin films. Deposit conditions of BST films were set working gas ratio, Ar:O$_2$= 70 : 30, working pressure 10mTorr, and RF input power 25W, 50W, 75W and 100W. Post-annealing using rapid thermal annealing(RTA) performed at 45$0^{\circ}C$, 55$0^{\circ}C$, $650^{\circ}C$, and 75$0^{\circ}C$ in oxigen ambient for 60 sec, respectively. The structural properties of BST films on Pt/Ti/SiO$_2$/Si substrate analysed by X-ray diffraction(XRD).).).

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07b
• /
• pp.939-942
• /
• 2004

Al doped Zinc Oxide(ZnO:Al) films, which is widely used as a transparent conductor in optoelectronic devices such as solar cell, liquid crystal display, plasma display panel, thermal heater, and other sensors were Prepared by using the capacitively coupled RF magnetron sputtering method. In this paper the effect of RF discharge power on the electrical, optical and structural properties were investigated experimentally. The results show that the structural and electrical properties of the film are highly affected by the variation of RF discharge power. The optimum growth conditions were obtained for films doped with 2 wt% of $Al_2O_3$ and 200 W in RF discharge power, which exhibit a resistivity of $10.4{\times}10^{-4}{\Omega}-cm$ associated with a transmittance of 89.66 % for 1000nm in films thickness in the wavelength range of the visible spectrum.