• Proceedings of the KIEE Conference
• /
• 1987.11a
• /
• pp.210-212
• /
• 1987

• Journal of information and communication convergence engineering
• /
• v.4 no.4
• /
• pp.147-150
• /
• 2006

The thin film of PbTiO3 is fabricated at substrate temperature of 100-150$^{\circ}C$. The infrared spectrum of the ferroelectric thin film is measured as temperature of thermal treatment, 400 - 550$^{\circ}C$. According to infrared spectrum analysis, there are absorption bands at a nearby wave number of 1000 $\sim$ 400 cm-l and the thin film treated by temperature of 550$^{\circ}C$ has absorption bands of wave number 500 cm-l similar to infrared response property of PbTiO3 powder. The pyroelectric infrared detector is fabricated after deposition of Pt and PbTiO3 thin film on Si wafer by sputtering machine. The measured remnant polarization are 11.5-12.5$\muC/cm2$, breakdown electric field Ec is 100-120KV/cm, and voltage responsivity and detectivity is -280V/W, -108cm Hz/W.

• Applied Science and Convergence Technology
• /
• v.24 no.6
• /
• pp.215-218
• /
• 2015

A pyroelctric properties of Ni(x)-doped PMNT systems were analyzed. Modified PMNT samples were prepared using the columbite structure method. Pyroelectric current, polarization, dielectric constant and dissipation factor of Ni-doped PMNT samples were measured as a function of temperature. By adding a small amount of NiO, pyroelectricity of PMNT is increased. Unlike the normal $ABO_3$ ferroelectric, Ni-doped PMNT showed properties for relaxor ferroelectric of causing the successive phase transition over a wide temperature. The optimum conditions for obtaining compositions with improvement ferroelectric properties are a nominal addition of 0.02 mole% Ni. Also, Ni-doped PMNT ferroelectric showed excellent pyroelectric figures of merit in the vicinity of room temperature. The pyroelectric coefficient ($0.00524C/m^2K$ at $25^{\circ}C$) and figures of merit ($F_v{\sim}0.039m^2/C$ and $F_d{\sim}0.664{\times}10^{-4}Pa^{-1/2}$) of composition PMNT with 0.02 mole% Ni are comparable to the earlier reports on lead-type pyroelectrics.

• Proceedings of the KIEE Conference
• /
• 1994.07b
• /
• pp.1496-1498
• /
• 1994

In this study, x PSN - y PT - z PZ ceramics doped with w $MnO_2$ were fabricated by the mixed oxide method at 1250 [$^{\circ}C$] for 2[hr] and then the dielectric and pyroelectric properties were investigated. In the 0.05 PSN - 0.4 PT - 0.55 PZ specimen with 0.5[wt%] $MnO_2$ the Pyroelectrics coefficient was $6.6{\times}10^{-8}[C/cm^2.^{\circ}C]$, respectibly.

• Journal of the Korean Ceramic Society
• /
• v.32 no.6
• /
• pp.748-760
• /
• 1995

Pyroelectric properties, figure of merits, and the other properties of the Pb(Zn1/3Nb2/3)O3-Pb(Fe1/2Nb1/2)O3 system, as expected to have excellent pyroelectric properties in the operating temperature range of pyroelectric type infrared sensor, were investigated. In the Pb(Zn1/3Nb2/3)O3-Pb(Fe1/2Nb1/2)O3 system, suppression of the pyrochlore phase depended on sintering condition, as like sintering temperature, holding time, sintering atmosphere. The specimen, sintered by the same composition atmosphere powder at 105$0^{\circ}C$ for 1.5h, possessed the best physical property. It was found that the piezoelectric parameters were mainly depended on the amount of spontaneous polarization and then the 0.2PZN-0.8PFN showed the best pyro- and piezoelectric properties. In terms of the experimental method, two pyroelectric-testing methods, i.e. static and dynamic methods, had a same tendency. Also the result of pyroelectric testing by the static method indicated that the diffuse phase transitiion resulted in the temperature difference of phase transition between dielectric constant and pyroelectric coefficient.

• Applied Science and Convergence Technology
• /
• v.26 no.4
• /
• pp.70-73
• /
• 2017

The dielectric constant and loss of poling/non-poling was measured in the $Pb_{1-3x/2}La_x[(Mg_{1/3}Ta_{2/3})_{0.66}Zr_{0.34}]O_3$ samples. The addition of $La^{3+}$ to the $Pb_{1-3x/2}La_x[(Mg_{1/3}Ta_{2/3})_{0.66}Zr_{0.34}]O_3$ did not cause a large change in grain size. But the addition of $La^{3+}$ did show transition temperature, which shifted toward low temperature in the $Pb[(Mg_{1/3}Ta_{2/3})Zr]O_3$ systems. In addition, the dielectric and pyroelectric properties (${\varepsilon}{\sim}20000$, $p{\sim}0.03C/m^2K$) of this system using $La^{3+}$ have been greatly improved. Pyroelectrics $Pb_{0.97}La_{0.02}(Mg_{1/3}Ta_{2/3})_{0.66}Zr_{0.34}]O_3$ system was found to have a relatively high ferroelectric FOMs ($F_V{\sim}0.035m^2/C$, $F_D{\sim}0.52{\times}10^{-4}Pa^{-1/2}$) at room temperature. Spontaneous polarization showed a value of $0.27{\sim}0.35C/m^2$ in the composition added to $La^{3+}$. The piezoelectric constant ($d_{33}=350{\sim}490pC/N$) and electromechanical coupling factor ($k_P=0.25{\sim}0.35$) are obtained in $Pb_{1-3x/2}La_x[(Mg_{1/3}Ta_{2/3})_{0.66}Zr_{0.34}]O_3$ compositions with $La^{3+}$ dopant.