• Restorative Dentistry and Endodontics
• /
• 제21권1호
• /
• pp.321-338
• /
• 1996

The purpose of this study was to evaluate the effect of moistening and air-drying of acid conditioned dentin and enamel on the marginal microleakage. In this study, Class V cavity were prepared on both buccal and lingual surface of sixty extracted human premolars with cementum margin. These specimens were randomly devided into three groups and three dentin adhesives(Scotchbond Multi-Purpose, All bond 2, Prisma Universal Bond 3) were applied to each group. The specimens in each group were subdevided into four groups (Wet/primed, Dry/primed, Wet/not primed, Dry/not primed) and the etched dentin and enamel surface were treated these four surface treatments prior to the placement of a bonding agent or adhesive. Wet/primed group was simply blot-dried with a damp facial tissue before primer placement ; Dry/primed group was air dried for 30 seconds before the placement of a primer ; Wet/not primed group and Dry/not primed group were not primed after blot dried and air dried for 30 seconds each group. The bonding agent and composite resin were applied for each group. All specimens were exposed to 500 cycle of thermal stress. Specimens were placed in a silver nitrate solution and then sectioned buccolingually through the center of the restoration. The dye penetrations of the specimens were observed with a stereo microscope. The statistical test were applied to the results using a one way analysis variance (ANOVA) and Duncan's multiple range test. The aspects of silver ion penetration into the resin/dentin interface were examined under scanning electron microscopy. The results were as follows. 1. In all groups, the enamel margin showed significantly lower leakage value than the cementum margin (p<0.05). 2. Regardless of various surface treatment and dentin adhesives, there was no significant difference at the enamel margins (p>0.05). 3. At the dentin margins, the leakage values of Dry/not primed group showed significantly higher than that of the other groups (p<0.05). The leakage values of Wet/primed group showed significantly lower than that of the other groups, but, there was no significant difference between Wet group and Dry group. 4. There was no significantly difference between the dentin adhesives regarding the surface treatments in all groups(p>0.05). 5. On the backscatterd scanning electron microscopy observation, the penetration of the silver ion occured at the bonding resin/dentin interface. In the Wet/primed group, resindentin hybrid zone and resin penetration into the dentin was observed. The resin tags were compactively formed to a thickness of $3\sim4{\mu}m$ at the upper part of dentinal tubules. In the Dry/primed group, the thickness of the hybrid zone and the diameter, depth of the resin tags diminished. In the Non-primed groups, the hybrid zone was not identified and few resin tag was observed. There was the gap formation in the resin/dentin interface.

• Restorative Dentistry and Endodontics
• /
• 제20권1호
• /
• pp.328-341
• /
• 1995

I. Shear Bond Strength to Air-dried and Remoistened Dentin.. The effect of air-drying and remoistening of acid-conditioned dentin before priming with the primer of All-Bond 2(BISCO. INC., U. S. A.) on shear bond strength(SBS) was investigated. Ninty freshly extracted sound human molars were divided at random into 9 groups of 10 teeth each. SBSs were meaured for acid-conditioned and non-conditioned dentin to which the primer and bonding agent of All-Bond 2 and composite resin(Z-100, 3M Dental Products, U. S. A.) were applied. The following values(Mean${\pm}$ SD, MPa) were obtained for the groups conditioned with 10% phosphoric acid for 15 seconds: Group l(blot dried) $6.7{\pm}4.1$ ; Group 2(10 seconds dried) $16.1{\pm}5.3$ ; Group 3(20 seconds dried) $15.4{\pm}4.8$ ; Group 4(30 seconds dried) $15.2{\pm}6.3$ ; Group 5(10 seconds dried/remoistened) $26.4{\pm}2.6$ ; Group 6(20 seconds dired/remositened) $22.2{\pm}2.7$ ; Group 7(30 seconds dried/remoistened) $21.5{\pm}4.1$. For the non-conditioned groups the values were: Group 8 (blot dried) $13.3{\pm}2.6$ ; Group 9(10 seconds dried) $12.9{\pm}3.5$. The data were analyzed using ANOVA. In the acid-conditioned groups, mean values of SBS for the air-dried specimens(Grps. 2, 3 and 4) and the 20 and 30 seconds dried/remoistened specimens (Grps. 6 and 7) were significantly lower than that of blot dried specimens.(p<0.05) The value for 10 seconds dried/remoistened specimens (Grp. 5), however, was not statistically different compared to that of blot dried specimens.(p>0.05) In the non-conditined groups, there was no statistical difference between blot dried and 10 seconds dried specimens.(p>0.05) The results suggest that the acid-conditioned dentin surface is more vulnerable to dentin bonding when it is air-dried or even remoistened after long period of drying. II. Shear bond stengh to the moistened and primed enamel. The effect of moistening and priming of enamel compared to the air-drying of enamel on the shear bond strength of enamel bonding agent was investigated. The experiment was divided into 4 groups each containing 10 caries-free maxillary incisor teeth. Shear bond strength values were measured for the primed and non-primed enamel to which All-Bond 2 and Z-100 were applied. The following values(MPa) were obtained for the primed groups pretreated with 32 % phosphoric acid for 15 seconds. : Group 1 (10 seconds dried) $29.8{\pm}2.2$ ; Group 2(moistened) $26.8{\pm}5.4$. For the non-primed groups the values were: Group 3(10 seconds dried/primed) $27.6{\pm}5.0$ ; Group 4(mostened/primed) $28.2{\pm}3.5$. The data were subjected to statistical analysis using ANOVA. The results showed that mean shear bond strengths among the experimental groups were not statistically different. (p>0.05) Conclusively, It is suggested that the bonding ability to enamel is not decreased by the moistening and priming of the enamel.

• Restorative Dentistry and Endodontics
• /
• 제25권1호
• /
• pp.46-55
• /
• 2000

During bonding procedure of composite resin, the prepared cavity can be contaminated by saliva. In this study, marginal microleakage and shear bond strength of a composite resin to primed enamel and dentin treated with artificial saliva(Taliva$^{(R)}$) were evaluated. For the marginal microleakage test, Class V cavities were prepared in the buccal surfaces of fifty molars. The samples were randomly assigned into 5 groups with 10 samples in each group. Control group was applied with a bonding system (Scotchbond$^{TM}$ Multi-Purpose plus) according to manufacture's directions without saliva contamination. Experimental groups were divided into 4 groups and contaminated with artificial saliva for 30 seconds after priming: Experimental 1 group ; artificial saliva was dried with compressed air only, Experimental 2 group ; artificial saliva was rinsed and dried. Experimental 3 group ; cavities were etched with 35% phosphoric acid for 15 seconds after rinsing and drying artificial saliva. Experimental 4 group ; cavities were etched with 35% phosphoric acid for 15 seconds and primer was reapplied after rinsing and drying artificial saliva. All the cavities were applied a bonding agent and filled with a composite resin (Z-100$^{TM}$). Specimens were immersed in 0.5% basic fuschin dye for 24 hours and embedded in transparent acrylic resin and sectioned buccolingually with diamond wheel saw. Four sections were obtained from one specimen. Degree of marginal leakage was scored under stereomicroscope and their scores were averaged from four sections. The data were analyzed by Kruscal-Wallis test and Fisher's LSD. For the shear bond strength test, the buccal or occlusal surfaces of one hundred molar teeth were ground to expose enamel(n=50) or dentin(n=50) using diamond wheel saw and its surface was smoothed with Lapping and Polishing Machine(South Bay Technology Co., U.S.A.). Samples were divided into 5 groups. Treatment of saliva-contaminated enamel and dentin surfaces was same as the marginal microleakage test and composite resin was bonded via a gelatin capsule. All specimens were stored in distilled water for 48 hours. The shear bond strengths were measured by universal testing machine (AGS-1000 4D, Shimaduzu Co., Japan) with a crosshead speed of 5 mm/minute. Failure mode of fracture sites was examined under stereomicroscope. The data were analyzed by ANOVA and Tukey's studentized range test. The results of this study were as follows : 1. Enamel marginal microleakage showed no significant difference among groups. 2. Dentinal marginal microleakages of control, experimental 2 and 4 groups were lower than those of experimental 1 and 3 groups (p<0.05). 3. The shear bond strength to enamel was the highest value in control group (20.03${\pm}$4.47MPa) and the lowest value in experimental 1 group (13.28${\pm}$6.52MPa). There were significant differences between experimental 1 group and other groups (p<0.05). 4. The shear bond strength to dentin was higher in control group (17.87${\pm}$4.02MPa) and experimental 4 group (16.38${\pm}$3.23MPa) than in other groups, its value was low in experimental 1 group (3.95${\pm}$2.51 MPa) and experimental 2 group (6.72${\pm}$2.26MPa)(p<0.05). 5. Failure mode of fractured site on the enamel showed mostly adhesive failures in experimental 1 and 3 groups. 6. Failure mode of fractured site on the dentin did not show adhesive failures in control group, but showed mostly adhesive failure in experimental groups. As a summary of above results, if the primed tooth surface was contaminated with artificial saliva, primer should be reapplied after re-etching it.