• 대한기계학회논문집A
• /
• 제21권6호
• /
• pp.1002-1012
• /
• 1997

When the presintered ceramics are machined with ceramic tool, the tool life becomes extremely short. The CBN tool exhibits the best performance in dry machining of the ceramics presintered at $1450^{\circ}C$ among all cutting tests. The roughness of the machined surface of the ceramics presintered below $1350^{\circ}C$ is smaller than that of the ceramics presintered at $1450^{\circ}C$ While the performance of the cemented carbide and CBN tools is better in dry than in wet machining, the diamond tool shows adverse tendency. The tool life is not affected by the feed rate and depth of cut. During the following full-sintering after the machining of the presintered ceramics, the surface roughness decreases up to 62%. The finished surface in machining the presintered ceramics is much better than that in machining the full-sintered ceramic.

• 한국세라믹학회지
• /
• 제38권9호
• /
• pp.799-805
• /
• 2001

상용 알루미나 분말(0.5${\mu}$m, 3${\mu}$m)을 die-press법을 이용하여 1120$^{\circ}$C에서 2시간 1차 소결하여 다공성 전성형체를 제조하고 1100$^{\circ}$C에서 4시간 $La_2O_3-Al_2O_3-SiO_2$계 유리를 용융 침투시켜 치밀한 유리-알루미나 복합체를 제조하였다. 알루미나 입도가 유리-알루미나 복합체의 충진율, 미세조직, 젖음성, 기공률 및 크기, 기계적 특성에 미치는 영향을 조사하였다. 입도 범위가 0.1∼48${\mu}$m로 넓고 bimodal size 입도 분포를 가지면서 random orientation을 가진 3${\mu}$m 알루미나가 분산된 복합체가 최적의 기계적 특성 및 충진률이 관찰되었으며 강도와 인성값은 각각 519MPa, $4.5MPa{\cdot}m^{1/2}$이었다.

• 한국세라믹학회지
• /
• 제39권2호
• /
• pp.145-152
• /
• 2002

상용 알루미나 분말(0.5, 2.8, 12, 45 ${\mu}m$)을 die-press법을 이용하여 1120$^{\circ}C$에서 2시간 1차 소결하여 다공성 전성형체를 제조하고 1100$^{\circ}C$에서 0∼2시간까지 $La_2O_3-Al_2O_3-SiO_2$계 유리를 용융 침투시켜 유리 침투 깊이와 침투 시간간의 kinetic을 조사하였다. 침투시간이 증가할수록 유리 침투깊이는 Washburn 식의 포물선 관계를 가지면서 증가하였으며 침투 상수인 K는 알루미나 입도가 증가할수록 증가하였다. 유리-알루미나 복합체의 강도값은 2.8${\mu}m$ 알루미나가 분산된 복합체까지 충진률의 증가로 인하여 증가하다가 알루미나 입도가 증가할수록 감소하였다. 파괴인성은 알루미나 입도가 증가할수록 균열 휨 현상과 균열과 알루미나 입자간 결합에 의하여 증가하였다.