• 한국세라믹학회지
• /
• 제55권4호
• /
• pp.392-399
• /
• 2018

$C_f/SiC$ composites were prepared via a process combining chemical vapor infiltration (CVI) and precursor infiltration pyrolysis (PIP), wherein silicon carbide matrices were infiltrated into 2.5D carbon preforms. The obtained composites exhibited porosities of 20 vol % and achieved strengths of 244 MPa in air at room temperature and 423 MPa at $1300^{\circ}C$ under an Ar atmosphere. Carbon fiber pull-out was rarely observed in the fractured surfaces, although intermediate layers of pyrolytic carbon of 150 nm thickness were deposited between the fiber and matrix. Fatigue fracture was observed after 1380 cycles under 45 MPa stress at $1000^{\circ}C$. The fractured samples were analyzed by transmission electron microscopy to observe the distributed phases.

• Composites Research
• /
• 제26권5호
• /
• pp.322-327
• /
• 2013

탄소섬유강화 SiC기지상 복합재는 우수한 산화저항성과 우수한 열충격저항성을 가진다. 그리고 이런 특성들은 탄소섬유강화복합재가 고온구조재로서 응용케하였다. 본 연구에서는 $C_f/SiC$ 복합재가 전구체 함침과 액상 함침이 동반된 열분해공정, Cyclohexene을 사용한 화학기상 경화공정을 통해 제조되었다. 최종 제조된 $C_f/SiC$ 복합재는 5회 함침을 통해 $0.43g/cm^3$ 밀도를 갖는 탄소섬유 프리폼에서 $1.76g/cm^3$의 밀도값을 나타내고 있다. 그리고 산화저항성 특성면에서 $C_f/SiC$ 복합재의 무게가 공기중 $1400^{\circ}C$에서 6시간 유지 후에 81%가 남았다. 결과적으로 Cyclohexene을 사용한 화학기상 경화공정은 효과적으로 높은 치밀화와 증가된 산화저항성을 보이고 있다.