• Journal of the Korean Society for Heat Treatment
• /
• v.9 no.3
• /
• pp.205-211
• /
• 1996

Structural studies have been performed on precipitation hardening discovered in $Ll_2$-ordered $Ni_3$(Al,Cr) containing 0.2 and 0.5 mol% of carbon in terms of transmission electron microscopy(TEM). By aging at temperatures around 1073 K after solution treatment at 1423 K, fine polyhedral precipitates appear firstly on the dislocations and then in the matrix. The selected area electron diffraction (SAED) studies revealed that these particles are a $M_{23}C_6$ type carbide which has the cube-cube orientation relationship with the matrix lattice. Weak-beam electron microscopy observations of deformation induced dislocations suggested that the dislocations bypass the carbide particles during deformation.

• Corrosion Science and Technology
• /
• v.9 no.2
• /
• pp.67-73
• /
• 2010

Niobium microalloying is effective in hot-rolled and cold-rolled steels by providing a fine-grained microstructure resulting in increased strength. To optimize the strengthening effect, alloy design and hot-rolling conditions have to be adapted. As a key issue the dissolution and precipitation characteristics of Nb are discussed in particular with regard to the run-out table conditions. It is then considered how the hot-rolled microstructure and the solute state of Nb interact with the hot-dip galvanizing cycle. The adjusted conditions allow controlling the morphology and distribution of phases in the cold-rolled annealed material. Additional precipitation hardening can be achieved as well. The derived options can be readily applied to produce conventional HSLA and IF high strength steels as well as to modern multiphase steels. It will be explained how important application properties such as strength, elongation, bendability, weldability and delayed cracking resistance can be influenced in a controlled and favorable way. Examples of practical relevance and experience are given.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2005.05a
• /
• pp.307-310
• /
• 2005

Ageing behavior of the Al-Mg-Si alloy was modeled for the use of optimization of Al forging product. Typical precipitates of Al-Mg-Si alloy are a wide variety of metastable phases (e.g. GP zones, $\beta',\beta'$). These rod shaped particles take a role to hinder the dislocation movement. The precipitation sequence in Al-Mg-Si alloys is quite complex and the strength of precipitate particles differs with the ageing condition. In the present study, the ageing behavior of Al-Mg-Si alloy was investigated by using an industrial grade Al 6061 alloy forged product, which was a perform for an Al impeller for turbo charger. The precipitate hardening models by Esmaeili's approach were used for the analysis of ageing behavior.

• Korean Journal of Materials Research
• /
• v.15 no.7
• /
• pp.480-485
• /
• 2005

Sc has been known to be an very effective ppt-hardening element in Al and Al alloys and also to be effective in modification of eutectic Si in hypoeutectic Al-Si alloys. The modification mechanism of Sc is different from that of the traditional modifier Sr in Al-Si alloys. In the present study the effects of Sc on the primary and eutectic Si in hypereutectic Al-Si alloys were investigated with evaluating the microstructures with OM, EPMA and EBSD methods. The results represent that Sc has only a small effect on primary Si when added less than $0.8wt\%$. However, when Sc addition leading to the precipitation of metallic Sc within primary Si reaches $1.6wt\%$, very coarse primary Si occurs.

• Journal of Technologic Dentistry
• /
• v.19 no.1
• /
• pp.21-35
• /
• 1997

The Ag-Pd-Cu alloys containing a small amount of Au is commonly used for dental purposes, because this alloy is cheaper than Au-base alloys for clinical use. However, the most important characteristic of this alloy is age-hardenability, which is not exhibited by other Ag-base dental alloys. The specimens used were Ag-20Pd-20Cu ternary alloy and Au addition alloy. These alloys were melted and casted by induction electic furace and centrifugal casting machine in Ar atmoshpere. These specimens were solution treated for 2hr at $800^{\circ}C$ and were then quenched into iced water, and aged at $350{\sim}550^{\circ}C$ Age-hardening characteristics of the small Au-containing Ag-pPd-Cu dental alloys were investigated by means of hardness testing, X-ray diffraction and electron microscope observations, electrical resistance, differential scanning calorimetric, emergy dispersed spectra and electron probe microanalysis. Principal results are as follows : Hardening occured in two stages, I. e., stage I in low temperature and stage II in high temperature regions, during continuous aging. The case of hardening in stage I was due to the formation of the Llo type face centered tetragonal PdCu-ordered phase in the grain interior and hardening in stage I was affedted by the Cu concentration. In stage II, decomposition of the $\alpha$ solid solution to a PdCu ordered phase(L1o type) and an Agrich ${\alpha}2$ phase occurred and a discontiunous precipitation occurred at the grain boundary. Form the electron microscope study, it was concluded that the cause of age-hardening in this alloy is the precipitation of the PdCu ordered phase, which has AuCu I type face-centered tetragonal structure. Precipitation procedure was ${\alpha}\to{\alpha}+{\alpha}2+PdCu\to{\alpha}1+{\alpha}2+PdCu$ at Pd/Cu = 1 Ag-Pd-Cu alloy is more effective dental alloy as ageing treatment and is suitable to isothermal ageing at $450^{\circ}C$.

• Journal of the Korean Society for Heat Treatment
• /
• v.22 no.1
• /
• pp.8-15
• /
• 2009

Structural studies have been performed on precipitation hardening found in $Ni_{3}Al$ based ordered alloys using transmission electron microscopy (TEM). Tilt experiments by the weak-beam method were made to obtain some information concerning the cross slip mechanism of the superlattice dislocation. The strength of ${\gamma}'-Ni_3$(Al,Ti) increases over the temperature range of experiment by the precipitation of fine $\gamma$ particles. The peak temperature where a maximum strength was obtained shifted to higher temperature. Over the whole temperature range, the interaction between dislocation and $\gamma$ precipitates is attractive. On the temperature range of 773 K to 973 K, the dislocations in ${\gamma}'$ matrix move on (111) primary slip plane. When the applied stress is removed, the dislocations make cross slip into (010) plane, while those in $\gamma$ precipitates remain on the (111) primary slip plane. The increase of high temperature strength in ${\gamma}'-Ni_3$(Al,Ti) containing $\gamma$ precipitates is due to the restraint of cross slip of dislocations from (111) to (010) by the dispersion of disordered $\gamma$ particles.

• Journal of the Korean Society for Heat Treatment
• /
• v.16 no.1
• /
• pp.10-15
• /
• 2003

In Nb, V and Ti added steels, carbo-nitrides are formed due to their strong interaction with C and N. The formation of carbo-nitrides has an important role to control the microstructure as well as mechanical properties by grain size refinement and precipitation hardening. However, the quantitative analysis of distribution of precipitates and the effect of precipitates on the phase transformation and mechanical properties are still far from satisfactory. In this study, the quantitative analysis of precipitates in austenite was investigated using the fact that the formation of precipitates in Nb, V and Ti added steels accelerates austenite/ferrite transformation. The formation of precipitates was controlled by adjusting holding temperature and time in austenite region, transformed Volume fractions were measured by dilatometer during slow cooling, Iso-precipitation kinetics were determined by comparing 5% and 50% volumes transformed at various conditions respectively. The result was compared with the calculated.

• Nuclear Engineering and Technology
• /
• v.51 no.5
• /
• pp.1365-1372
• /
• 2019

The effects of Y and Ti on the microstructure stability and tensile properties of the reduced activation ferritic/martensitic steel have been investigated. The addition of Y and Ti affected the prior austenite grain size due to the pinning of the inclusions. Ti addition of 0.008 wt% to the steel was intended to promote the precipitation of nano-sized carbides with a high resistance to coarsening. 8Ti14Y exhibited a higher yield strength and a lower DBTT than the other alloys due to the fine grain size and additional precipitation hardening by (Ti, Ta)-rich MX. After thermal exposure at $550^{\circ}C$ for 1500 h, yield strength was dropped significantly in exposed 0Ti13Y. On the contrary, a lower reduction of YS was observed in 8Ti14Y. The $M_{23}C_6$ in 0Ti13Y and 8Ti14Y and MX in 25Ti14Y and 39Ti15Y coarsened seriously during ageing, which could be responsible for the reduction of the tensile properties of alloys.

• Journal of the Korea Institute of Building Construction
• /
• v.18 no.2
• /
• pp.109-115
• /
• 2018

Since the current method of SCW cement milk pouring method uses one to one ratio of cement milk with OPC, there are some problems such as drying shrinkage, increased cost, difficulty of controlling mix proportions for various conditions of applied soil, and precipitation of $Cr^{6+}$ due to the excessively used cement. Specifically, in aspect of sustainability issues of cement manufacturing, the consumption of cement should be reduced. Hence, in this research, as a replacement of cement for SCW method, blast furnace slag with sulfate or alkali as a stimulant, and expansive admixture were used. By using blast furnace slag as a hardening composite of SCW, there are many advantages such as free controllable mix proportions, rapid setting time with less mud occurrence, less cost with less energy for mixing, constant strength development, and less precipitation of $Cr^{6+}$. Regarding the alternative composites for SCW, in this research, durability and chloride resistance were evaluated.

• Laser Solutions
• /
• v.10 no.3
• /
• pp.25-32
• /
• 2007

The effect of welding speed on the weldability, microstructures, hardness, tensile property of Nd:YAG laser welding joint in 600MPa grade precipitation hardening high strength steel was investigated. A shielding gas was not used, and bead-on-plate welding was performed using various welding speeds at a power of 3.5kW. Porosity in the joints occurred at 1.8m/min, but were not observed over the welding speed of 2.1m/min. However, spatter occurred over the welding speed of 6.6m/min. The hardness was the highest at heat affected zone(HAZ) near fusion zone(FZ), and was decreased on approaching to the base metal. The maximum hardness increased with increasing welding speed. The microstructure of FZ was composed of coarse grain boundary ferrite and bainite(upper) but the HAZ near the FZ contained bainite(Lower) and fine ferrite at a low welding speed. With increasing welding speed, ferrite at the FZ and the HAZ became finely and upper binite changed to lower bainite. In a perpendicular tensile test to the weld line, all specimens were fractured at the base metal, and the tensile strength and the yield strength of joints was equal to those of raw material. Elongation was found to be lower than that of the raw material.