Influence of Particle Size Distribution on Green and Sintered Properties of Fe-Cr-Mo Prealloy Powder (Fe-Cr-Mo 합금 분말의 성형 및 소결특성에 미치는 입도분포 영향)

  • Kim, Ki-Bong;Yang, Sangsun;Kim, Yong-Jin;Park, Yong-Ho
    • Journal of Powder Materials
    • /
    • v.20 no.1
    • /
    • pp.7-12
    • /
    • 2013
  • The effect of particle size distribution on green and sintered properties of Fe-Cr-Mo prealloy powder was investigated in this study. For the study, prealloyed Fe-Cr-Mo powders with different particle sizes were mixed as various ratios and cold compacted at various pressure and sintered at $1250^{\circ}C$ for 30 min, $90%N_2+10%H_2$ atmosphere in the continuous sintering furnace. The results shows that the powders with large particle size distribution have high compressibility and low ejection force. However the green strength are much less than those with small particle size distribution. Tensile prperties of the sintered specimes with large particles size also have high strength and elongation.

Gigacycle Fatigue Crack Initiation in Cr-Mo Prealloy Sintered Steel

  • Xu, Chen;Danninger, Herbert;Khatibi, Golta;Weiss, Brigitte
    • Proceedings of the Korean Powder Metallurgy Institute Conference
    • /
    • 2006.09a
    • /
    • pp.136-137
    • /
    • 2006
  • Crack initiation and short crack propagation was studied on the polished notched surfaces of Cr-Mo prealloy sintered steels with 7.35 $g.cm^{-3}$ sintered density. An ultrasonic resonance test system operating in push-pull mode at 20 kHz and R=-1 was used. It showed that crack initiation took place in several places, small cracks growing oriented to the local pore structure rather than to stress orientation. Their growth rate is markedly higher than the corresponding one of long cracks. Finally, several microcracks join to form a dominant crack.

  • PDF

Effect of Alloying on the Microstructure and Fatigue Behavior of Fe-Ni-Cu-Mo P/M Steels

  • Bohn, Dmitri A.;Lawley, Alan
    • Proceedings of the Korean Powder Metallurgy Institute Conference
    • /
    • 1997.04a
    • /
    • pp.34-34
    • /
    • 1997
  • The effect of alloying mode and porosity on the axial tension-tension fatigue behavior of a P/M steel of nominal composition Fe-4w/o Ni-1.5w/o Cu-O.5w/o Mo-O.5w/o C has been evaluated. Alloying modes utilized were elemental powder mixing, partial alloying(distaloy) and prealloying by water atomization; in each case the carbon was introduced as graphite prior to sintering. Powder compacts were sintered($1120{\circ}C$/30 min.) in 7Sv/o $H_2$/25v/o $N_2$ to densities in the range 6.77-7.2 g/$cm^3$. The dependence of fatigue limit response on alloying mode and porosity was interpreted in terms of the constituent phases and the pore and fracture morphologies associated with the three alloying modes. For the same nominal composition, the three alloying modes resulted in different sintered microstructures. In the elemental mix alloy and the distaloy, the major constituent was coarse and fine pearlite, with regions of Ni-rich ferrite, Ni-rich martensite and Ni-rich areas. In contrast, the prealloy consisted primarily of martensite by with some Ni-rich areas. From an examination of the fracture surfaces following fatigue testing it was concluded that essentially all of the fracture surfaces exhibited dimpled rupture, characteristic of tensile overload. Thus, the extent of growth of any fatigue cracks prior to overload was small. The stress amplitude for the three alloying modes at 2x$l0^6$ was used for the comparison of fatigue strengths. For load cycles <3x$l0^5$, the prealloy exhibited optimum fatigue response followed by the distaloy and elemental mix alloy, respectively. At load cycles >2x$l0^6$, similar fatigue limits were exhibited by the three alloys. It was concluded that fatigue cracks propagate primarily through pores, rather than through the constituent phases of the microstructure. A decrease in pore SIze improved the S-N behavior of the sintered steel.

  • PDF

Fabrication and Properties of High Strength Hypereutectic Al-Si Powder by Gas Atomization Process I. Powder Production and Compressibility (가스분무 공정에 의한 고강도 과공정 Al-Si 합금 분말의 제조 및 특성 연구 I. 분말 제조 및 성형성)

  • Kim Yong-Jin;Kim Jin-Chun
    • Journal of Powder Materials
    • /
    • v.12 no.4 s.51
    • /
    • pp.296-302
    • /
    • 2005
  • In order to improve mechanical properties, the hypereutectic Al-20 wt%Si based prealloy powder was prepared by gas atomization process. Microstructure and compressibility of the atomized Al-Si powder were investigated. The average powder size was decreased with increasing the atomization gas pressure. Size of primary Si particles of the as-atomized powder was about $5-8\;\mu{m}$. The as-atomized Al-Si powder such as AMB 2712 and AMB 7775 to increase compressibility and sinterability. Relative density of the mixed powder samples sintered at $600^{\circ}C$ was reached about 96% of a theoretical density.