• Korean Journal of Materials Research
• /
• v.29 no.6
• /
• pp.363-370
• /
• 2019

The recent development of information and communication technologies brings new changes to automobile traffic systems. The most typical example is the advancement of dedicated short range communication(DSRC). DSRC mainly consists of an intelligent transportation system(ITS), an electronic toll collection system(ETCS) and an advanced traveler information system(ATIS). These wireless communications often cause unnecessary electromagnetic waves, and these electromagnetic waves, in turn, cause frequent system malfunction. To solve this problem, an absorber of electromagnetic waves is suggested. In this research, various materials, such as powdered metal and iron oxides, are used to test the possibility for an effective absorption of the unnecessary electromagnetic waves. The various metal powders are made into a thin sheet form by compositing through processing. The electromagnetic characteristics(complex permittivity, complex permeability) of the fabricated sheet are measured. As a result, we achieve -6.5 dB at 940 MHz(77.6 % absorption rate) with a 1.0 mm-thickness electromagnet wave absorber, and -9.5 dB at 940 MHz(88.8 % absorption rate) with a 2.0 mm-thickness absorber.

• Journal of Powder Materials
• /
• v.30 no.2
• /
• pp.156-168
• /
• 2023

The semiconductor industry faces physical limitations due to its top-down manufacturing processes. High cost of EUV equipment, time loss during tens or hundreds of photolithography steps, overlay, etch process errors, and contamination issues owing to photolithography still exist and may become more serious with the miniaturization of semiconductor devices. Therefore, a bottom-up approach is required to overcome these issues. The key technology that enables bottom-up semiconductor manufacturing is area-selective atomic layer deposition (ASALD). Here, various ASALD processes for elemental metals, such as Co, Cu, Ir, Ni, Pt, and Ru, are reviewed. Surface treatments using chemical species, such as self-assembled monolayers and small-molecule inhibitors, to control the hydrophilicity of the surface have been introduced. Finally, we discuss the future applications of metal ASALD processes.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2020.11a
• /
• pp.77-78
• /
• 2020

An alkaline activator was synthesized by dissolving waste glass powder (WGP) in NaOH-4M solution to explore its effects on the Class-C fly ash (FA) and ground granulated blast furnace slag (GGBS) based alkali-activated material (AAM). The compressive strength and porosity were measured, and (SEM-EDX) were used to study the hydration mechanism and microstructure. Results indicated that the composition of alkali solutions was significant in enhancing the properties of the obtained AAM. As the amount of dissolved WGP increased in alkaline solution, the silicon concentration increased, causing the accelerated reactivity of FA/GGBS to develop Ca-based hydrate gel as the main reaction product in the system, thereby increasing the strength. Further increase in WGP dissolution led to strength loss, which were believed to be due to the excessive water demand of FA/GGBS composites to achieve optimum mixing consistency. Increasing the GGBS proportion in a composite also appeared to improve the strength which contributed to develop C-S-H-type hydration.

• Journal of Powder Materials
• /
• v.31 no.2
• /
• pp.163-168
• /
• 2024

As the demand for lithium-ion batteries for electric vehicles is increasing, it is important to recover valuable metals from waste lithium-ion batteries. In this study, the effects of gas flow rate and hydrogen partial pressure on hydrogen reduction of NCM-based lithium-ion battery cathode materials were investigated. As the gas flow rate and hydrogen partial pressure increased, the weight loss rate increased significantly from the beginning of the reaction due to the reduction of NiO and CoO by hydrogen. At 700 ℃ and hydrogen partial pressure above 0.5 atm, Ni and Li₂O were produced by hydrogen reduction. From the reduction product and Li recovery rate, the hydrogen reduction of NCM-based cathode materials was significantly affected by hydrogen partial pressure. The Li compounds recovered from the solution after water leaching of the reduction products were LiOH, LiOH·H₂O, and Li₂CO₃, with about 0.02 wt% Al as an impurity.

• Advances in concrete construction
• /
• v.17 no.4
• /
• pp.211-220
• /
• 2024

Concrete, consisting mainly of cement, water and aggregates; is the most used construction material all over the world. Cement manufacturing industry is one of the carbon dioxide producing sources that contributes to global warming. Therefore, in the last few years, there is a growing interest in using waste materials and by-products as cement replacement materials. Using these kinds of materials as a part of cement replacement reduces the air pollution, cost and also enhances some properties of concretes. In the present work, marble dust (MD) was examined as a partial cement replacement material with seven proportions as 0%, 10%, 20%, 30%, 40%, 50%, 60% and glass powder (GP) was used as an additive, 8% by cement weight, in a 0.55 water-binder ratio concrete. In order to evaluate their effects; workability, strength (compressive, flexural and split tensile), alkalinity, sulphate resistance and ultrasonic pulse velocity tests were performed. Experimental results indicated that with MD replacement and GP addition; there is a loss in the workability but improvement in mechanical properties. With 10% replacement of MD compressive, flexural and tensile strengths increased by 10.7%, 6.2% and 5.3% respectively. Moreover, up to 30% replacement of MD reasonable strength values were obtained.

• Journal of Microbiology
• /
• v.45 no.6
• /
• pp.485-491
• /
• 2007

The effects of biological pretreatment on the Japanese red pine Pinus densiflora, was evaluated after exposure to three white rot fungi Ceriporia lacerata, Stereum hirsutum, and Polyporus brumalis. Change in chemical composition, structural modification, and their susceptibility to enzymatic saccharification in the degraded wood were analyzed. Of the three white rot fungi tested, S. hirsutum selectively degraded the lignin of this sortwood rather than the holocellulose component. After eight weeks of pretreatment with S. hirsutum, total weight loss was 10.7%, while lignin loss was the highest at 14.52% among the tested samples. However, holocellulose loss was lower at 7.81 % compared to those of C. lacerata and P. brumalis. Extracelluar enzymes from S. hirsutum showed higher activity of ligninase and lower activity of cellulase than those from other white rot fungi. Thus, total weight loss and changes in chemical composition of the Japanese red pine was well correlated with the enzyme activities related with lignin- and cellulose degradation in these fungi. Based on the data obtained from analysis of physical characterization of degraded wood by X-ray Diffractometry (XRD) and pore size distribution, S. hirsutum was considered as an effective potential fungus for biological pretreatment. In particular, the increase of available pore size of over 120 nm in pretreated wood powder with S. hirsutum made enzymes accessible for further enzymatic saccharification. When Japanese red pine chips treated with S. hirsutum were enzymatically saccharified using commercial enzymes (Cellulclast 1.5 L and Novozyme 188), sugar yield was greatly increased (21.01 %) compared to non-pre treated control samples, indicating that white rot fungus S. hirsutum provides an effective process in increasing sugar yield from woody biomass.

• Corrosion Science and Technology
• /
• v.6 no.4
• /
• pp.147-153
• /
• 2007

This study sought to investigate the reaction of Co-binder containing tungsten with molten zinc. Four kinds of Co-W alloys (pure, 10%W, 20%W, 30%W) were prepared using the powder metallurgy method. The specimens were immersion-tested in molten pure zinc baths at $460^{\circ}C$. To evaluate the corrosion property in molten zinc, the weight loss of the specimen was measured after the immersion tests at different immersion times (10~300 min.). Co-10%W alloys, compared with pure cobalt, showed no effect of tungsten addition on the reaction rate in molten zinc. The relationship between the weight loss and the square root of immersion period represents a straight line in both pure cobalt and Co-10%W alloy. The Co-Zn reaction layer in Co- 1O%W alloy consists of $\gamma2$, $\gamma1$, $\gamma$ and ($\beta1$ phases. The rate of weight loss significantly increases and the weight loss behavior is not well accord with the linear relationship as the tungsten content in the Co-W alloy increases. The $\beta1$ layer was not formed on the Co-20%W alloy and neither was a stable Co-Zn intermetallic compound layer found on the Co-30%W alloy. The main cause of increase in reaction rate with increasing tungsten content is related with the instability of the Co-Zn reaction phases as seen on micro-structural analysis.

• Journal of Hydrogen and New Energy
• /
• v.21 no.6
• /
• pp.533-539
• /
• 2010

Ni-YSZ supported button cells were prepared by spray-coating YSZ and screen-printing YSZ-LSM powder as an electrolyte and oxygen electrode on Ni-YSZ cermet disks. In order to identify the polarization loss mechanism in high temperature electrolysis current-voltage characteristics coupled with electrochemical impedance spectroscopy were investigated as a function of temperature, current load, and the humidity. The effects of the different current collectors of platinum and silver for oxygen electrodes were compared. With Ag current collector two polarization losses were distinguished. The high frequency component was attributed to the Ni-YSZ cermet which was less susceptible to temperature variation but increasing in loss with humidity. The lower frequency component was attributed to the LSM electrode. Platinum current collector led to a much lower polarization loss.

• The Journal of Internal Korean Medicine
• /
• v.27 no.4
• /
• pp.836-844
• /
• 2006

Background: Mahuang (Ephedra sinica STAPF) is well known as an herbal medicine and has been widely used to reduce body weight and increase athletic ability. However, as a result of reporting many cases of adverse effects on the cardiovascular system, use of dietary supplements containing ephedra was prohibited by the FDA. Objectives : The object of this study was to find the effectiveness of ephedra on weight loss without severe adverse effect. Methods : 16 healthy volunteers consisting of an ephedra group (N=8) and a placebo group (N=8) were investigated. Study form was a randomized, controlled, double-blind clinical trial. The ephedra group took 12g of ephedra while the placebo group took 12g of glutinous rice powder. Both groups were measured with BCA (body composition analysis) on weight loss and with HRV (heart rate variability) on its adverse effect before and after medication. Results : The following results were obtained after taking 12g of ephedra for 14 days. In the ephedra group, body weight reduced significantly. In the placebo group, there were no significant differences of body weight between before and after placebo treatment. There was a slight increase of heart beat rate and deactivation of cardiac activity. Parasympathetic nerves were deactivated, but balances of autonomic nervous system were well maintained. Conclusions : The results suggest that ephedra in healthy adults tends to reduce body weight and deactivation of autonomic nervous system and cardiac activity.

• Korean Chemical Engineering Research
• /
• v.54 no.1
• /
• pp.44-51
• /
• 2016

The powder core, conventionally fabricated from iron particles coated with insulator, showed large eddy current loss under high frequency, because of small specific resistance. To overcome the eddy current loss, the increase in the specific resistance of powder cores was needed. In this study, copper oxide coating onto electrically conductive iron particles was performed using a planetary ball mill to increase the specific resistance. Coating factors were optimized by the Response surface methodology. The independent variables were the CuO mass fraction, mill revolution number, coating time, ball size, ball mass and sample mass. The response variable was the specific resistance. The optimization of six factors by the fractional factorial design indicated that CuO mass fraction, mill revolution number, and coating time were the key factors. The levels of these three factors were selected by the three-factors full factorial design and steepest ascent method. The steepest ascent method was used to approach the optimum range for maximum specific resistance. The Box-Behnken design was finally used to analyze the response surfaces of the screened factors for further optimization. The results of the Box-Behnken design showed that the CuO mass fraction and mill revolution number were the main factors affecting the efficiency of coating process. As the CuO mass fraction increased, the specific resistance increased. In contrast, the specific resistance increased with decreasing mill revolution number. The process optimization results revealed a high agreement between the experimental and the predicted data ($Adj-R^2=0.944$). The optimized CuO mass fraction, mill revolution number, and coating time were 0.4, 200 rpm, and 15 min, respectively. The measured value of the specific resistance of the coated pellet under the optimized conditions of the maximum specific resistance was $530k{\Omega}{\cdot}cm$.