• 한국농업기계학회:학술대회논문집
• /
• 한국농업기계학회 2017년도 춘계공동학술대회
• /
• pp.107-107
• /
• 2017

3D bioprinting is a technology to produce complex tissue constructs through printing living cells with hydrogel in a layer-by-layer process. To produce more stable 3D cell-laden structures, various materials have been developed such as alginate, fibrin and gelatin. However, most of these hydrogels are chemically bound using crosslinkers which can cause some problems in cytotoxicity and cell viability. On the other hand, thermosensitive hydrogels are physically cross-linked by non-covalent interaction without crosslinker, facilitating stable cytotoxicity and cell viability. The examples of currently reported thermosensitive hydrogels are poly(ethylene glycol)/poly(propylene glycol)/poly(ethylene glycol) (PEG-PPG-PEG) and poly(ethylene glycol)/poly(lactic acid-co-glycolic acid) (PEG/PLGA). Chitosan, which have been widely used in tissue engineering due to its biocompatibility and osteoconductivity, can be used as thermosensitive hydrogels. However, despite the many advantages, chitosan hydrogel has not yet been used as a bioink. The purpose of this study was to develop a bioink by chitosan hydrogel for 3D bioprinting and to evaluate the suitability and potential ability of the developed chitosan hydrogel as a bioink. To prepare the chitosan hydrogel solution, ${\beta}-glycerolphosphate$ solution was added to the chitosan solution at the final pH ranged from 6.9 to 7.1. Gelation time decreased exponentially with increasing temperature. Scanning electron microscopy (SEM) image showed that chitosan hydrogel had irregular porous structure. From the water soluble tetrazolium salt (WST) and live and dead assay data, it was proven that there was no significant cytotoxicity and that cells were well dispersed. The chitosan hydrogel was well printed under temperature-controlled condition, and cells were well laden inside gel. The cytotoxicity of laden cells was evaluated by live and dead assay. In conclusion, chitosan bioink can be a candidate for 3D bioprinting.

• 한국세라믹학회지
• /
• 제45권9호
• /
• pp.561-566
• /
• 2008

Carbon fiber fabric-silicon carbide composites were fabricated by liquid silicon infiltration (LSI) process. The porous two-dimensional carbon fiber fabric performs were prepared by 13 plies of 2D-plain-weave fabric in a three laminating method, [0/90], [${\pm}45$], [$0/90/{\pm}45$] lay-up, respectively. Before laminating, a thin pyrolytic carbon (PyC) layer deposited on the surface of 2D-plain weave fabric sheets as interfacial layer with $C_3H_8$ and $N_2$ gas at $900^{\circ}C$. A densification of the preforms for $C_f-Si-SiC$ matrix composite was achieved according to the LSI process at $1650^{\circ}C$ for 30 min. in vacuum atmosphere. The bending strength of the each composite were measured and the microstructural consideration was performed by a FE-SEM.

• 한국수소및신에너지학회논문집
• /
• 제21권4호
• /
• pp.271-277
• /
• 2010

$(Ba(Zr_{0.85}Y_{0.15})O_{3-\delta})$ oxide, showing high protonic conductivity at high temperatures and good chemical stability with $CO_2$ are referred to as hydrogen separation membrane. For high efficiency of hydrogen separation ($H_2$ flux and selectivity) and low fabrication cost, ultimate thin and dense BZY-Ni layer has to be coated on a porous substrate such as $ZrO_2$. Aerosol depostion (AD) process is a novel technique to grow ceramic film with high density and nano-crystal structure at room-temperature, and may be applicable to the fabrication process of AD integration ceramic layer effectively. XRD, SEM, X-ray mapping measurements were conducted in order to analyze the characteristics of BZY-Ni membrane fabricated by AD process. it is observed that it is homogeneous distribution for BZY-Ni. The result of $H_2$ permeation rate suggests that BZY-Ni composite is higher than BZY.

• 상하수도학회지
• /
• 제22권1호
• /
• pp.131-140
• /
• 2008

The application of magnetic ion exchange resin($MIEX^{(R)}$) is effective for natural organic matter(NOM) removal and for control of the formation of disinfection byproducts(DBPs). NOM removal is also enhanced by adding $MIEX^{(R)}$ with coagulant such as polyaluminium chloride(PACl) in conventional drinking water treatment systems. In the application of $MIEX^{(R)}$, it is important to understand changes of NOM characteristics such as hydrophobicity and molecular weight distributions with $MIEX^{(R)}$ or $MIEX^{(R)}$+coagulant treatment.To observe characteristics of NOM by treatment with $MIEX^{(R)}$ or $MIEX^{(R)}$+coagulant, four major drinking water sources were employed. Results showed that the addition of $MIEX^{(R)}$ to coagulation significantly reduced the amount of coagulant required for the optimum removal of dissolved organic matter(DOC) and turbidity in the all four waters. The DOC removal was also increased approximately 20%, compared to coagulant treatment alone. The process with $MIEX^{(R)}$ and coagulant showed that complementary removal of hydrophobic and hydrophilic fraction of DOC. The combined processes preferentially removed the fractions of intermediate (3,000-10,000 Da) and low (< 500 Da) molecular weight. The microfiltration test showed that membrane cake resistance was decreased for waters with flocs from $MIEX^{(R)}$+coagulant. A porous layer was formed to $MIEX^{(R)}$ on the membrane surface and the layer consequently inhibited settling of coagulant flocs, which could act on a foulant.

• 상하수도학회지
• /
• 제21권3호
• /
• pp.359-366
• /
• 2007

Slow sand filtrations have been widely used for water treatment in small communities, however their capacity is often limited by high turbidity in the raw water. For this reason, several pre-treatment facilities were required for a slow sand filter. Turbidity removal from the highly turbid raw water was investigated in roughing filters as a pre-treatment process. The roughing filters followed by rapid mixing tank were operated in the form of a contact filtration. In several jar tests, the predetermined optimum aluminium sulfate (alum) doses for turbid water of 30 and 120NTU were 30 and 50mg/L, respectively. At the optimum alum dose, physically optimum parameters including G value of $220sec^{-1}$ and rapid mixing time of 3 minutes were applied to the contact filtration system. Without addition of alum, the filtrate turbidity from the roughing filters, packed respectively with different media such as sand, porous diatomite ball and gravel, was in the range of 5~30NTU at filtration velocities of 30 and 50m/day. However, the application of a contact filtration to roughing filters showed stably lower filtrate turbidity below 1.0NTU at filtration velocity of 30 m/day. Although the filtration velocity increased to 50m/day, filtrate turbidity was still below 1.0NTU in both single and double layer roughing filters. At influent turbidity of 120NTU, the filtrate turbidity was over 5 NTU in the triple layer roughing filter, which shortened the filter run time. The flocs larger than $10{\mu}m$, formed in the rapid mixing tank, were almost captured through the roughing filter bed, while the almost flocs smaller than $10{\mu}m$ remained in filtrate.

• 박물관보존과학
• /
• 제9권
• /
• pp.95-104
• /
• 2008

광주 신창동 유적에서 출토된 목제 유물에 대해 수종분석 37점, 칠분석 3점등총 40점에 대하여 분석하였다. 결과 목제품에 사용된 수종은 상수리나무류, 벚나무류, 살구나무류, 오리나무류, 단풍나무류, 버드나무류, 사시나무류 등으로 총 7종이 식별되었으며, 특히 칠기와 접시 같은 생활용품의 경우에는 모두 산공재 수종을 사용하였다. 칠도막 분석 결과 유공칠기와 통형칠기 동체부 5는 칠한 횟수에서 차이가 있지만 밑칠을 칠한 후 맨 상층에 흑색안료와 칠을 혼합하여 칠하였으며, 5절판은 토분과 흑색안료를 칠과 혼합하여 밑칠을 한 후에 상층에 흑색안료를 혼합한 칠을 칠한 것으로 확인되었다.

• 대한토목학회논문집
• /
• 제7권3호
• /
• pp.111-119
• /
• 1987

해안구조물(海岸構造物)의 안정성(安定性)과 사면상(斜面上)의 반사파(反射波), run-up, run-down 등 흐름특성(特性)에 대한 모형(模型)의 축척효과(縮尺効果) 발생(發生) 메카니즘과 그 제어(制御) 방법(方法)을 7종(種)의 축척모형(縮尺模型)에 의해 실험적(實驗的)으로 연구(硏究)하였다. 그 결과(結果), 종래(從來)의 많은 연구자(硏究者)들이 소홀히 해 왔던 구조물(構造物) 내부(內部)의 침투류(浸透流) 특성(特性)의 상사(相似) 여부(如否)가 축척효과(縮尺効果) 발생(發生)의 가장 중요(重要)한 요인(要因)임을 지적(指摘)하였다. 해안구조물(海岸構造物) 가운데서 특히 투과성(透過性) 구조물(構造物)의 축척효과(縮尺効果) 제어(制御)를 위해서는 피복층(被覆層), filter층(層), 피복층(被覆層)에 가까운 core부(部)의 침투류(浸透流) Reynolds수(數)가 각각(各各) Re > $2{\times}10^4$, $Re_f$ > $3{\times}10^3$, $Re_c$ > $1{\times}10^3$인 조건(條件)을 만족하도록 구조물(構造物) 각(各) 층(層)의 축척(縮尺)을 결정(決定)하는 것이 바람직함을 강조(强調)하였다.

• 한국정밀공학회지
• /
• 제26권1호
• /
• pp.146-154
• /
• 2009

In recent tissue engineering field, it is being reported that the fabrication of 3D scaffolds having high porous and controlled internal/external architectures can give potential contributions in cell adhesion, proliferation and differentiation. To fabricate these scaffolds, various solid free-form fabrication technologies are being applied. The solid free-form fabrication technology has made it possible to fabricate solid free-form 3D microstructures in layer-by-layer manner. In this research, we developed a multi-head deposition system (MHDS) and used design of experiment (DOE) to fabricate 3D scaffold having an optimized internal/external shape, Through the organization of experimental approach using DOE, the fabrication process of scaffold, which is composed of blended poly-caprolactone (PCL), poly-lactic-co-glycolic acid (PLGA) and tricalcium phosphate (TCP), is established to get uniform line width, line height and porosity efficiently Moreover, the feasibility of application to the tissue engineering of MHDS is demonstrated by human bone marrow stromal cells (hBMSCs) proliferation test.

• 에너지공학
• /
• 제2권2호
• /
• pp.194-199
• /
• 1993

인산형 연료전지에서 cathode 및 anode 전극의 반응 면적을 넓혀 전극성능을 향상시키고자 전극 촉매층에 가스 확산로를 도입하였다. 촉매층의 제작은 기체확산로로 이용하고자 제조된, 촉매가 담지되어 있지 않은 PTFE/carbon과 10w/o의 촉매가 담지된 Pt/carbon을 혼합 비율을 달리하면서 촉매 분말법으로 제작하였다. PTFE를 60w/o 담지한 PTFE(60 w/o)/carbon 분말과 Pt(10 w/o)/carbon분말을 7 : 3의 비율로 혼합하여 제조된 전극이 가장 우수한 성능을 보였다. 이들 조성을 변화시키면서 전극의 다공성과 전극성능을 비교 검토하여 본 결과 전극성능은 기체 확산로로 이용되는 macro pore와 전해질의 침투로 이용되는 micro pore 모두가 많이 형성됨에 따라 향상되었음을 알 수 있었다. 이때 전극에 담지된 백금 촉매의 양은 0.2mg/$\textrm{cm}^2$이었으며 PTFE함량은 42w/o이었다. 작동온도 15$0^{\circ}C$, 단자전압 0.7 V에서 전류밀도는 220 ㎃/$\textrm{cm}^2$이었다.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2017년도 춘계학술대회 논문집
• /
• pp.150.2-150.2
• /
• 2017

This research was conducted to investigate in detail the effect of $PO_4{^{3-}}$, $CO_3{^{2-}}$ and $F^-$ anions on the electrochemical properties of the thin air-formed oxide film-covered AZ31 Mg alloy. In this work, native air-formed oxide films on AZ31 Mg alloy samples were prepared by knife-abrading method and the changes in the electrochemical properties of the air-formed oxide film were investigated in electrolytes containing 0.01 M, 0.05 M and 0.1 M of $PO_4{^{3-}}$, $CO_3{^{2-}}$ and $F^-$ anions. It was observed that the trend of open circuit potential (OCP) transients changed only in the solution containing $PO_4{^{3-}}$ ions. The Nyquist plots obtained from electrochemical impedance spectroscopy (EIS) showed that the resistance of the new surface films formed in fluoride ion containing bath increased with the increase in concentration of fluoride ions but the resistance of surface films formed in carbonate ion containing bath decreased with the increase in concentration of carbonate ions. The potentiodynamic polarization curves illustrated that under anodic polarization, there was growth of porous passive layer only in fluoride ion containing solution while the surface layer formed in phosphate and carbonate ion containing solutions lost its passivity at high anodic potential of $2.5V_{Ag/AgCl}$.