• KOREAN JOURNAL OF CROP SCIENCE
• /
• v.45 no.2
• /
• pp.118-122
• /
• 2000

An extensive investigation has been made for the possible utilization of polypropylene spunbonded fabrics in rice seedling nursery. Considering the cropping systems available in southern part of Korea, sowing dates were fixed at April 5 and April 20 for single cropping and May 6 and May 26 for double cropping. Nursery period was fixed to 35 days for each sowing date. Four different thickness of polypropylene spunbonded fabrics, 40, 60, 80, 100 g/$m^2$, were tested in rice seedling nursery. The temperature and light intensity were not significantly different among the thickness of polypropylene spunbonded fabrics. Light intensity was significantly reduced in polypropylene spunbonded fabric (72.2 Klux) compared with polyethylene mm (85.5 Klux), however, the reduced light intensity was enough for seedling growth. The temperature in the polypropylene spunbonded fabric covering during low air temperature was higher than that in polyethylene mm tunnel. At transplanting, the rice seedlings grown in polypropylene spunbonded fabric condition was shorter (17cm) but healthier than those in polyethylene mm (23cm). The estimated possible nursery periods using the polypropylene spunbonded fabric covering may start from April 1 at Chinju (plain area in Southern Korea, 20m altitude) and April 15 at Susang (mountainous area, 430m altitude). Labour hours and cost were reduced by about 28% and 48%, respectively.

• Transactions of Materials Processing
• /
• v.25 no.6
• /
• pp.402-408
• /
• 2016

A manufacturing technology of carbon fiber composites with thermoplastic polymer pellets and continuous woven fiber was investigated using a compression molding process. To secure the impregnation of resin into the porosity of fabric the composite specimens were prepared with general injection-molding grade polypropylene pellets and low viscosity polycarbonate pellets. Tensile tests of polypropylene and polycarbonate composites were performed. Polycarbonate composites showed higher fracture strength than that of polypropylene composites because of the difference of matrix properties. However, the increase rate of strength was lower than that of polypropylene composites due to the difference of coherence between matrix and reinforcement. To investigate the effect of carbon fiber volume fraction on the fracture strength variation polypropylene composites with different volume fraction were compression molded and tensile tests were performed together. It was shown that the fracture strength of the polypropylene composites increased by 3.2, 5.4 and 6.9 times with the increase of carbon fabric volume fraction of 0.256, 0.367, and 0.480, respectively.

• Textile Coloration and Finishing
• /
• v.30 no.3
• /
• pp.199-207
• /
• 2018

In this study, the properties of polypropylene(PP) non-woven fabric spun under various conditions by the Melt-blown method were verified, and the deodorant content and deodorization of PP non-woven fabric after deodorant-treatment were investigated. PP non-woven fabrics are manufactured by varying the temperature of spin beam, hot air temperature and amount, the RPM of collector R/O and the distance between collector and spinneret, which affects the structure of the non-woven fabric. After that, the structural characteristics and air permeability of the non-woven fabric were measured. The experimental results show that the amount of air, the distance between the collector and the spinneret significantly affect the structural characteristics and air permeability of the PP non-woven fabric. And, regardless of the weight of the PP non-woven fabric, the deodorizing effect of UiO-66 MOF deodorant add-on ratio and content was higher.

• Fashion & Textile Research Journal
• /
• v.11 no.3
• /
• pp.481-487
• /
• 2009

The purpose of this study is to improve the defects of dyeable polypropylene(DPP) fabric by heat setting and to describe the change of physical properties of DPP fabrics. The thermosetting was carried out in autoclave from 100 to $140^{\circ}C$ temperature range for 2 min. In this study, we investigated the effect of the thermosetting temperatures on the structural, thermal, mechanical properties(e.g., the strength and elongation) and dyeability of DPP fabrics. The melting energy(J/g), the tensile strength was found to increase with increasing temperature of thermosetting. The diffraction peak at Bragg angle($2{\theta}$) about $13.8^{\circ}$ were very strong and diffraction intensity increased with increasing thermosetting temperatures. And d-spacing and half-width decreased with increasing thermosetting temperatures. On the other hand, the dyeability(K/S) and crease recovery decreased with an increasing thermosetting temperatures.

• Journal of Radiation Industry
• /
• v.9 no.2
• /
• pp.57-62
• /
• 2015

In this study, we fabricated effect of storage conditions on graft of polypropylene (PP) non-woven fabric induced by electron beam. The electron beam irradiations on PP non-woven fabric were carried out over a range of irradiation doses from 25 to 100 kGy to make free radicals on fabric surface. The radical measurement was established by electron spin resonance (ESR) for confirming the changes of the alkyl radical and peroxy radical according to effect of storage time, storage temperature and atmosphere. It was observed that the free radicals were increased with irradiation dose and decreased with storage time due to the continuous oxidation. However, the radical extinction was significantly delayed due to reduced mobility of radicals at extremely low temperature. The degree of graft based on the analysis of ESR was investigated. The conditions of graft reaction were set at a temperature: $60^{\circ}C$, reaction time: 6 hours and styrene monomer concentration: 20 wt%.

• Composites Research
• /
• v.32 no.6
• /
• pp.335-341
• /
• 2019

In this study, an acrylic acid (AAc) was grafted on a polypropylene (PP) nonwoven fabric using electron beam irradiation. Electron beam grafting was carried out under various conditions to produce AAc grafted PP (PP-g-AAc) nonwoven fabric having a grafting yield of about 50% at radiation dose of 100 kGy and a monomer concentration of 60%. The physical and chemical properties of PP-g-AAc nonwoven fabric were evaluated by SEM, ATR-FTIR, thermal analysis and tensile strength. The morphology of PP and PP-g-AAc nonwoven fabric confirmed by SEM showed no significant change, and it was judged that AAc was introduced into PP nonwoven fabric from ATR-FTIR. PP-g-AAc nonwoven fabric showed an increase in tensile strength and a decrease in tensile strain compared to PP nonwoven fabric. However, since change of value is not significant, it is considered that there is no significant influence on the physical characterization. Adsorption experiments of PP-g-AAc nonwoven fabric on various ions showed selective adsorption behavior for lead ion. In conclusion, the electron beam radiation-induced PP-g-AAc nonwoven fabric is expected to be applied as an effective adsorbent for the adsorption of lead ions.

• Applied Chemistry for Engineering
• /
• v.10 no.3
• /
• pp.477-485
• /
• 1999

The grafting of 2,3-epoxypropylmethacrylate (GMA) onto polypropylene fabric was carried out by the $\gamma$-ray preirradiation grafting technique. Subsequently, the GMA-grafted polypropylene fabric was reacted with iminodiacetic acid (IDA) in different mixed solvents to prepare the fibrous metal adsorbent. The grafting extent was found to be dependent on the reaction time, temperature, preirradiation dose and dose rate. The effects of various mixed solvents on the IDA amination onto GMA-grafted polypropylene fabric were investigated. Compared with other mixed solvents, the extent of amination was highest in the dimethylsulfoxide (DMSO)/water, but the reaction did not occur in the water. The adsorption characteristics of various metal ions by the prepared adsorbent were examined when it was immersed in the 100 ppm metal ion solution. The amount of adsorption followed the order:$Pb^{2+}>Co^{2+}>Fe^{2+}$.

• Journal of Environmental Science International
• /
• v.17 no.11
• /
• pp.1255-1263
• /
• 2008

The efficiency of PP-g-AA and PP-g-St nonwoven fabric synthesized by photoinduced polymerization as an adsorbent for removal $NH_3-N$ from waste water was evaluated. The results evidently indicate that the adsorption capacities of $NH_3-N$ onto PP-g-AA nonwoven fabric were extremely superior to those onto sulfonated PP-g-St nonwoven fabric, PK and zeolite. PP-g-AA nonwoven fabric showed the maximum adsorption capacity of $NH_3-N$ at the degree of grafting of 80 wt.%. The adsorption behaviour of $NH_3-N$ onto PP-g-AA and sulfonated PP-g-St nonwoven fabric was controlled by an ion exchange reaction, and tended to be similar to both trends of Langmiur and Freundlish isotherm. Futhermore, PP-g-AA non-woven fabric could be regenerated more than 5 times by a simple washing with 0.1N HCl with no decrease of adsorption capacity and no degradation of physical properties. Also sulfonated PP-g-St nonwoven fabric could be regenerated by washing with 0.1N ${H_2}{O_4}$. However, their regeneration efficiency was significantly low because grafting layer acted as functional radical for adsorption was continuously desquamated in the adsorption or regeneration processes, which resulted in decrease of adsorption capacity and weight of adsorbent. All results obtained from this study indicate that the $NH_3-N$ removal capacity of PP-g-AA non-woven fabric was extremely superior to those of PP-g-St non-woven fabric, PK and zeolite.

• Fashion & Textile Research Journal
• /
• v.6 no.3
• /
• pp.384-392
• /
• 2004

The purpose of this study is in development of effective filter-type polymer adsorbent for removal of pollutants from wastewater by UV irradiation graft polymerization. Photografting of acrylic acid (AA) on polypropylene (PP) nonwoven fabric using benzophenone (BP) as a photosensitizer was investigated. Inhibition of homopolymerization was achieved by adding various concentrations of $FeSO_4{\cdot}7H_2O$, $CuSO_4{\cdot}5H_2O$ and Mohr's salt. As AA concentration was increased, the degree of grafting was increased as to a specific value and then decreased, and the effect of BP concentration showed the same tendency. It was also found that the degree of grafting increased with reaction time and reaction temperature. Addition of the polyfunctional monomers and $H_2SO_4$ to the grafting system accelerated the photografting. The melting temperature, molecular weight and breaking stress and breaking strain were decreased with the increase in the degree of grafting.

• Fashion & Textile Research Journal
• /
• v.6 no.3
• /
• pp.377-383
• /
• 2004

Photografting of styrene (St) on polypropylene (PP) nonwoven fabric using benzoin ethyl ether (BEE) as a photosensitizer was investigated. Inhibition of homopolymerization was achieved by adding various concentrations of $FeSO_4{\cdot}7H_2O$, $CuSO_4{\cdot}5H_2O$ and Mohr's salt. As St concentration was increased, the degree of grafting was increased as to a specific value and then decreased, and the effect of BEE concentration showed the same tendency. It was also found that the degree of grafting increased with reaction time and reaction temperature. Addition of the polyfunctional monomers and $H_2SO_4$ to the grafting system accelerated the photografting. The melting temperature, molecular weight, tensile strength and elongation were decreased with the increase in the degree of grafting.