• Journal of the Korean Recycled Construction Resources Institute
• /
• v.6 no.2
• /
• pp.79-86
• /
• 2018

In this study, emulsion type hydrophobic admixture was prepared by mixing polyvinyl alcohol surfactant, polymethyl hydro-siloxane and meta kaolin, and the compressive strength and mechanical properties such as permeability and contact angle test of the mortar were evaluated. The developed hydrophobic admixture showed no decrease in strength and the mortar specimen with magnesium oxide developed the early strength. In the case of permeability, total seepage was significantly decreased when the hydrophobic admixture was directly mixed with the mortar, but the effect of meta kaolin contained in hydrophobic admixture was not significant. The surface of specimens coated with hydrophobic admixture shows that the contact angle on the surface was highly increased compared with reference mortar specimen. Further researches to obtain the optimum mix proportion of the PVA fiber, nano-silica and meta kaolin for producing the super-hydrophobic surface are required.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.9 no.2
• /
• pp.127-134
• /
• 2021

A hydrophobic emulsion consisting of PMHS and PVA was mixed into a cement mortar to observe changes in cement hydrate and microstructure, and to experimentally evaluate compressive strength and flexural strength. The hydrophobic emulsion was added with metakaolin and PVA fibers, and the stirring speed and sequence were adjusted to prepare a shell-concept hydrophobic emulsion. It was then mixed when mixing mortar to enhance filling of the internal pores and change of the hydrates. It was observed that the mortar mixed with a hydrophobic emulsion was filled with micropores and a coating film was formed on the surface of the hydrates by the emulsion. It was analyzed that the total pore area and porosity of the mortar mixed with the emulsion decreased from 30% to 60% compared to OPC, excluding the 50MK variable, which was extremely reduced and the median pore diameter decreased in some variables. It was also found that the compressive strength of the mortar mixed with emulsion 1% was increased up to 20%, but the strength of the mortar specimen mixed with 2% decreased to 50%.