• Journal of the Korean Applied Science and Technology
• /
• v.29 no.1
• /
• pp.141-148
• /
• 2012

In this study, the composite coating materials with improved thermal insulation property were prepared by incorporating the hydrophobic silica aerogel. The surface modification of silica aerogel was performed to obtain UV curable urethane acrylate hybrid coating sols with good compatibility by using surfactant(Brij 56). The polycarbonate substrates were coated by the prepared composites and cured under UV radiation. The incorporation of aerogel with only 10 vol% of content resulted in remarkable improvement by about 28% in the thermal insulation property of the coated film, as compared with substrate. In addition, increasing aerogel content was found to give minor effect on the variation of optical transparency, adhesion, and surface hardness of the coated film.

• Transactions of the Society of Information Storage Systems
• /
• v.1 no.2
• /
• pp.127-131
• /
• 2005

We report a nanometer scale mark formation using a $PtO_x$ thin film or a TbFeCo rare-earth transition metal film and the mechanism. The multi-layer samples($ZnS-SiO_2/PtOx/ZNS-SiO_2,\;ZnS-SiO_2/TbFeCo/ZnS-SiO_2$) were prepared with a magnetron sputtering method on a polycarbonate or a glass substrate. By laser irradiation of approximately a few nanoseconds, nanometer scale marks were fabricated. During the fabrication process, the thin films were thermally reacted or inter-diffused during the laser irradiation. 75 nm bubble marks in the PtOx multi-layer sample by an approximately 4-ns laser irradiation. Inside the bubble mark, Pt particles with a few nanometer sizes are distributed. The $50{\sim}100$ nm bubble marks in the TbFeCo multi-layer sample by a few nanosecond laser irradiations. We will report the detail structure of the samples, the bubble mark formation process and the mechanism.

• Journal of the Optical Society of Korea
• /
• v.19 no.5
• /
• pp.508-513
• /
• 2015

A capacitive-type touch screen panel (TSP) composed of silver nanowire (AgNW) crossing electrodes and transparent bridge structures was fabricated on a polycarbonate film. The transparent bridge structure was formed with a stack of Al-doped ZnO (AZO) electrodes and SU-8 insulator. The stable and robust continuity of the bridge electrode over the bridge insulator was achieved by making the side-wall slope of the bridge insulator low and depositing the conformal AZO film with atomic layer deposition. With an extended exposure time of photolithography, the lower part of the SU-8 layer around the region uncovered by the photomask can be exposed enough to the UV light scattered from the substrate. This leads to the low side-wall slope of the bridge insulator. The fabricated TSP sample showed a large capacitance change of 22.71% between with and without touching. Our work supplies the technological clue for ensuring long-term reliability to the highly flexible and transparent TSP made by using conventional fabrication processes.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.381-382
• /
• 2007

IZO/Ag/IZO (IAI) anode films for flexible organic light emitting diodes (OLEDs) were grown on PC (polycarbonate) substrate using DC sputter (IZO) and thermal evaporator (Ag) systems as a function of Ag thickness. To investigate electrical and optical properties of IAI stacked films, 4-point probe and UV/Vis spectrometer were used, respectively. From a IAI stacked film with 12nm-thick Ag, sheet resistance of $6.9\;{\Omega}/{\square}$ and transmittance of above 82 % at a range of 500-550 nm wavelength were obtained. In addition, structural and surface properties of IAI stacked films were analyzed by XRD (X-ray diffraction) and SEM (scanning electron microscopy), respectively. Moreover, IAI stacked films showed dramatically improved mechanical properties when subjected to bending both as a function of number of cycles to a fixed radius. Finally, OLEDs fabricated on both flexible IAI stacked anode and conventional ITO/Glass were fabricated and, J-V-L characteristics of those OLEDs were compared by Keithley 2400.

• Clean Technology
• /
• v.24 no.3
• /
• pp.190-197
• /
• 2018

Various waterborne polyurethanes (WPU) with three different types of polyol such as ester type polyol [adipic acid (A)/BD/3-methyl-1,5-pentandiol (MPD) and A/BD]//carbonate type polyol (C/HD/MPD, C/HD, C/BD)//ether type polyol (PTMG) were prepared in this study. This study focused on the effect of polyol type on the properties of WPU. Soft segment Tg (Tgs), 100% elastic modulus and tensile strength were highest when using carbonate polyol, followed by ester polyol and ether polyol, while those of elongation showed the opposite trend. The WPU synthesized with MPD - containing polyol showed lower Tgs, 100% elasticity and strength, and higher elongation than MPD - free WPU. The % transmittance and transparency of the WPU film containing the MPD component was superior to that of the WPU film containing no MPD component, and it was found that the film based on carbonate polyol was slightly better than the film based on ester polyol and ether polyol.

• Journal of the Institute of Electronics Engineers of Korea SD
• /
• v.45 no.5
• /
• pp.12-18
• /
• 2008

Ag paste was employed for source and drain electrode of OTFTs and for the data metal lines of OTFT-OLED array on PC(polycarbonate) substrate. We tested two kinds of Ag-pastes such as pastes for 325 mesh and 500 mesh screen mask to examine the pattern ability and electrical performance for OTFTs. The minimum feature size was 60 ${\mu}m$ for 325 mesh screen mask and 40 ${\mu}m$ for 500 mesh screen mask. The conductivity was 60 $m{\Omega}/\square$ for 325 mesh and 133.1 $m{\Omega}/\square$ for 500 mesh. For the OTFT performance the mobility was 0.35 $cm^2/V{\cdot}sec$ and 0.12 $cm^2/V{\cdot}sec$, threshold voltage was -4.7 V and 0.9 V, respectively, and on/off current ratio was ${\sim}10^5$, for both screen masks. We applied the 500 mash Ag paste to OTFT-OLED array because of its good patterning property. The pixel was composed of two OTFTs and one capacitor and one OLED in the area of $2mm{\times}2mm$. The panel successfully worked in active mode operation even though there were a few bad pixels.

• Journal of Pharmaceutical Investigation
• /
• v.22 no.2
• /
• pp.155-161
• /
• 1992

Although glycosylated liposomes have attracted much attention as targeting delivery systems (DDS) of drugs to specific organs which have glycoside receptors, physical instability of liposomes greatly limits their practical application. In this case, proliposomes might be a potential answer to solve this problem. Utilizing the proliposomes as tageting DDS has been a goal of our series of works; we have tried to develop DDS which form liposomes uppon adding water and can deliver drugs to specific target organs/cells such as hepatocytes. In this paper, preparation of glycosylated liposomes and binding of the liposomes with lectin (agglutinin RCA 120) was studied. Asialoletuin (AF) was selected as a model compound which has galactose terminal and is favorable for binding with galactose receptor on the surface of hepatocytes. AF was obtained by splitting the terminal N-acetylneuraminic acid (NANA) of fetuin. Small unilamellar AF-liposomes were prepared by mixing aqueous solution of AF-palmitate with thin film of phosphatidyl choline and cholesterol (30:10 w/w) formed on the innersurface of the round bottomed flask. They were successively extruded through polycarbonate membranes (0.45 mm). Palmitoyl-AF not incorporated into the liposomal bilayer was separated from liposomes by a Sepharose 4B column equilibrated with 10 mM Tris-HCI buffered saline. Lectin (agglutinin RCA 120) was added to the suspension of AF-liposomes and incubated at $37^{\circ}C$ for 2 hr. After centrifugation, the unbound lectin in the supernatant was assayed for protein. The binding of the lectin to AF-liposomes (AF content 2.8 nmole) at $37^{\circ}C$ was linear at least upto 35 mg of lectin indicating high affinity association of the lectin to AF molecules of the liposomes.

• Design & Manufacturing
• /
• v.2 no.2
• /
• pp.29-32
• /
• 2008

A back light unit (BLU) is a key module of a thin film transistor liquid crystal display (TFT-LCD), frequently utilized in various mobile displays. In this study, we experimentally characterize transcription and optical properties of concave and convex microlens arrays (MLAs) of light guide plate (LGP) fabricated by injection molding with polycarbonate as a LGP substrate material. Nickel mold inserts were manufactured by electroforming on the MLA which was fabricated by the thermal reflow of photoresist microstructures patterned by UV-photolithography. For the case of convex microlens, the height of replicated microlens was less than that of the mold insert while maintaining almost the same microlens diameter of the mold insert as the location of the microlens is far from the gate. In contrast, for the concave microlens, the diameter of replicated microlens was larger than that of mold insert, while showing almost the same microlens height as the mold insert. From the optical examination of replicated convex and concave MLAs, it was found that a higher luminance of the LGP was achieved by the concave MLAs compared to the convex MLAs (about 30% enhancement in this case)due to the utilization of a larger amount of light provided by the light sources.

• Korean Chemical Engineering Research
• /
• v.55 no.6
• /
• pp.830-836
• /
• 2017

Hydrophilic coating solutions were prepared by reacting a silane coupling agent, GPTMS (3-glycidoxypropyl trimethoxysilane) with colloidal silica. Hydrophilic coating films were also obtained by depositing the hydrophilic coating solutions on polycarbonate substrates by spin-coating and subsequently by thermal curing at $120^{\circ}C$. During this process, the effect of average particle sizes of colloidal silica was studied on the properties of coating films. As a result, coating film, prepared from colloidal silica with average particle size of 25 nm, showed a low contact angle of $20^{\circ}$ and a good pencil hardness of H. On the other hand, coating films, prepared from colloidal silica with average particle sizes of 15 nm and 45 nm, exhibited high contact angles of $27^{\circ}$ and $36^{\circ}$ and pencil hardness of H and B, respectively.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2000.02a
• /
• pp.170-170
• /
• 2000

Synthetic polymers such as polyimide, polycarbonate, and poly(methyl methacrylate) are long chain molecules which consist of carbon, hydrogen, and heteroatom linked together chemically. Recently, polymer surface can be modified by using a high energy ion beam process. High energy ions are introduced into polymer structure with high velocity and provide a high degree of chemical bonding between molecular chains. In high energy beam process the modified polymers have the highly crosslinked three-dimensionally connected rigid network structure and they showed significant improvements in electrical conductivity, in hardness and in resistance to wear and chemicals. Polyimide films (Kapton, types HN) with thickness of 50~100${\mu}{\textrm}{m}$ were used for investigations. They were treated with two different surface modification techniques: Plasma Source Ion Implantation (PSII) and conventional Ion Implantation. Polyimide films were implanted with different ion species such as Ar+, N+, C+, He+, and O+ with dose from 1 x 1015 to 1 x 1017 ions/cm2. Ion energy was varied from 10keV to 60keV for PSII experiment. Polyimide samples were also implanted with 1 MeV hydrogen, oxygen, nitrogen ions with a dose of 1x1015ions/cm2. This work provides the possibility for inducing conductivity in polyimide films by ion beam bombardment in the keloelectronvolt to megaelectronvolt energy range. The electrical properties of implanted polyimide were determined by four-point probe measurement. Depending on ion energy, doses, and ion type, the surface resistivity of the film is reduced by several orders of magnitude. Ion bombarded layers were characterized by Time-of-Flight Secondary Ion Mass Spectrometry (TOF-SIMS), XPS, and SEM.