• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.168.1-168.1
• /
• 2014

We developed poly (3,4-ethylene dioxylene thiophene):poly (styrene sulfonic acid) (PEDOT:PSS)-free organic solar cells (OSCs) using buffer and anode combined Ta doped $In_2O_3$ (ITaO) electrodes. To optimize the ITaO electrodes, we investigated the effect of $Ta_2O_5$ doping power on the electrical, optical, and structural properties of the co-sputtered ITaO films. The optimized ITaO film doped with 20 W $Ta_2O_5$ radio frequency power showed sheet resistance of 17.11 Ohm/square, a transmittance of 93.45%, and a work function of 4.9 eV, all of which are comparable to the value of conventional ITO electrodes. The conventional bulk heterojunction OSC with ITaO anode showed a power conversion efficiency (PCE) of 3.348% similar to the OSCs (3.541%) with an ITO anode. In addition, OSCs fabricated on an ITaO electrode successfully operated without an acidic PEDOT:PSS buffer layer and showed a PCE of 2.634%, which was much higher than the comparable no buffer OSC with an ITO anode. Therefore, co-sputtered ITaO electrodes simultaneously acting as a buffer and an anode layer can be considered promising transparent electrodes for cost-efficient and reliable OSCs because they can eliminate the use of an acidic PEDOT:PSS buffer layer.

• Applied Chemistry for Engineering
• /
• v.25 no.1
• /
• pp.14-19
• /
• 2014

Nanocomposites based on poly(methyl methacrylate) (PMMA)/poly(vinylidene fluoride) (PVDF) and poly(ethylene terephthalate) (PET)/(PVDF) blended with carbon fibers (CF) and carbon nanotube (CNT) were prepared by melt mixing in the twin screw extruder. Morphologies of the PMMA/PVDF/CF/CNT and PET/PVDF/CF/CNT nanocomposites were investigated using SEM. The aggregation of CNT was observed in PMMA/PVDF/CF/CNT nanocomposites while the good dispersion of CNT was shown in PET/PVDF/CF/CNT nanocomposites. In SEM image of PET/PVDF/CF/CNT nanocomposite, the CNT were mainly located at the PET domain of phase-separated PET/PVDF blend due to the ${\pi}-{\pi}$ interaction between the phenyl ring of PET and graphite sheet of the CNT's surface. In addition, a fairly good compatibility between PET/PVDF matrix and CF was shown in the SEM image. In the case of PET/PVDF nanocomposites blended with the co-addition of CF and CNT, the volume electrical resistivity decreased while no change was observed in PMMA/PVDF/CF/CNT composites. The degree of CNT dispersion in morphology results was consistent with the electrical conductivity results. From the DSC results, the crystallization temperature (Tc) of PET/PVDF/CF/CNT nanocomposites increased due to the co-addition of CF and CNTs acting as a nucleating agent. Flexural modulus of PET/PVDF/CF/CNT were sharply enhanced due to increasing the interaction between PET and CF.

• Proceedings of the SCSK Conference
• /
• 2003.09a
• /
• pp.501-519
• /
• 2003

Silk Sericin(SS) is a natural protein extracted from cocoon of bombix mori and shows moisturizing effect to the skin due to a number of hydroxyl groups in the structure. But its application to cosmetics is limited due to its poor solubility in water. In order to solve this drawback and expand its application to cosmetics, polyethyleneglycol(PEG) was conjugated with sericin by reacting activated polyethyleneglycol(ActPEG). Reaction site of sericin is tyrosine residue, which was determined by using $^1$H-NMR. Random coil structure of sericin was transformed to beta-sheet structure by conjugating polyethyleneglycol. It was confirmed that melting point of sericin-PEG conjugate was lowered compared to that of each sericin and PEG due to the interaction between sericin and PEG in crystalline structure. Self-assembled sericin-PEG nanoparticle was obtained by dialyzing with alcohol solution of sericin-PEG conjugate against water. The particle is spherical and has 200-400nm of size. The moisturizing ability of sericin-PEG nanoparticle was much higher than that of sericin itself. Incorporation of vitamin A into sericin-PEG nanoparticle was carried out by diafiltration method. The content of incorporated Vitamin A in sericin-PEG nanoparticle was 8.9 wt％. Releasing behaviour of vitamin A incorporated into nanoparticle was tested in phosphate buffer, pH 7.4 at 37$^{\circ}C$. and half-life of Vitamin A release was 43hrs. Sericin-PEG nanoparticle exhibited higher moisturing effect than sericin itself and distilled water, respectively. No toxicity and irritation were observed in animal tests. It can be expected that the self-assembled sericin-PEG nanoparticle can be developed for cosmetics.

• Journal of Korean Ophthalmic Optics Society
• /
• v.18 no.1
• /
• pp.11-17
• /
• 2013

Purpose: To improve glasses temple's insert processibility of CA/PEG blend, triacetin with higher specific heat values in the processing temperature range is used as second plasticizer. Methods: The total amount of plasticizer is fixed at 30 wt% by CA. To determine optimal CA/PEG/triacetin blend for glasses frame, blends with different composition ratio were examined by various analysis: thermal properties, mechanical properties, glossiness. Results: Specific heat of the CA/PEG blend increased as the content of triacetin. In CA/PEG/triacetin blends, as triacetin concentration is increased, glass transition temperature is decreased and heat conservation rate of composites is increased. Furthermore, CA/PEG/triacetin blend exhibited higher mechanical properties and similar gloss characterization with CA/PEG blend. Conclusions: It is possible to improve the processibility inserting metal support to CA temple through varying the weight ratio of PEG/triacetin. The extruded sheets of CA/PEG/triacetin blend had better glossiness and mechanical properties than those of CA/PEG blend.

• Journal of the Korean Vacuum Society
• /
• v.20 no.3
• /
• pp.233-241
• /
• 2011

Currently, solar module is using the two methods such as a glass-filled method or a super-straight method. The common point of these methods is to use glass structure on the front of solar module. However, the reflectance of the solar module is high depending on the height of the incident sunlight due to the flat surface of the module front glass. Purposed to solve these problems, AG (anti-glare) structures were formed on the glass surface. Next is fabrication methods of AG structure. First, uneven structure made by micro blaster equipment was dipped in Hydro-fluidic acid (HF) acid. HF acid process was carried out to remove particles and to make high transmittance. The reflectance and transmittance of the anti-glare glass was compared to those of the bare glass. The reflectance of anti-glare glass decreased approximately 1% compared with bare glass. The transmittance of anti-glare glass was similar to bare glass. According to the sample angle, the difference of the reflectance between bare glass and the anti-glare glass was about 19%. Isc and efficiency value of anti-glare glass on bare solar cell appeared about 3.01 mA and 0.228% difference compared with bare glass. Anti-glare glass on textured solar cell appeared about 9.46 mA and 0.741% difference compared with bare glass. As a result, the role of anti-glare in the substrate is to reduces the loss of sunlight reflected from the surface. In this study, therefore, AG structure on the solar cell was used to improve the efficiency of solar cell.