• Membrane Journal
• /
• v.23 no.2
• /
• pp.170-175
• /
• 2013

Poly (vinyl alcohol) (PVA) solution containing the glutaraldehyde (GA) as a crosslinking agent was coated onto the polyacrylonitrile (PAN) hollow fiber membrane as the supporter. Pervaporation experiments were carried out to characterize the prepared PVA/PAN composite membrane for water-isopropyl alcohol mixture. The flux and separation factor were measured at 30, 50, $90^{\circ}C$ for the feed mixture of aqueous 85 wt% IPA solution with varying the reaction temperature and composition of coating solutions. Typically the flux showed 1,870 $g/m^2{\cdot}hr$ at $90^{\circ}C$ feed mixture and the coating concentration of 3.5 wt% and the highest separation factor of 804 was obtained at $30^{\circ}C$ feed mixture and the coating concentration of 7 wt% as well.

• Proceedings of the Korean Fiber Society Conference
• /
• 2007.11a
• /
• pp.449-450
• /
• 2007

• Proceedings of the Korean Fiber Society Conference
• /
• 1998.10a
• /
• pp.13-16
• /
• 1998

Poly(vinyl alcohol) (PVA) gels are easily formed via physical pathway. Most PVA solutions including PVA/water solution are well known to form thermally reversible gels at low temperature but these gels showed poor mechanical properties. In order to overcome this weak point, transparent crosslinked PVA hydrogels were prepared by electron beam irradiation or by chemical process with crosslinking agents or additives. (omitted)

• Fibers and Polymers
• /
• v.3 no.2
• /
• pp.73-79
• /
• 2002

Nanoscaled PVA fibers were prepared by electrospinning. This paper described the electrospinning process, the processing conditions fiber morphology, and some potential applications of the PVA nato-fibers. PVA fibers with various diameters (50-250 nm) were obtained by changing solution concentration, voltage and tip to collector distance (TCD). The major factor was the concentration of PVA solution which affected the fiber diameter evidently. Increasing the concentration, the fiber diameter was increased, and the amount of beads was reduced even to 0%. The fibers were found be efficiently crosslinked by glyoxal during the curing process. Phosphoric acid was used as a catalyst activator to reduce strength losses during crosslinking. Scanning electron micrograph (SEM) and differential scanning calorimetric (DSC) techniques were employed to characterize the morphology and crosslinking of PVA fibers. It was fecund that the primary factor which affected the crosslinking density was the content of chemical crosslinking agent.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2003.11a
• /
• pp.537-540
• /
• 2003

The effects of substituting cement with fly ash(10%, 15%, 20%) and different fiber addition(polypropylene, cellulose, poly vinyl alcohol), on the control of microcrack and enhanced durability performance of face slab concrete in CFRD was studied experimentally It was conducted experiments of plastic shrinkage of mortar and concrete, and drying shrinkage of concrete. Also, durability test were carried out the chloride permeability, abrasion resistance and freeze-thaw repetition. Through the experimental results, it was concluded that ploy vinyl alcohol fiber containing concrete was the most effective mixture in control of cracking and durability.

• Textile Coloration and Finishing
• /
• v.25 no.2
• /
• pp.118-125
• /
• 2013

Poly(vinyl alcohol) (PVA)/titanium dioxide ($TiO_2$) composite nanofibers were produced at different $TiO_2$ concentrations (0.5, 1 and 1.5 wt.%) using the electrospinning method. The parameters of electrospinning including polymer contents, voltage and tip-to-collector distance (TCD) were optimized for fabrication process. The study showed that 7.5 wt.% PVA, 15 kV applied voltage and 15 cm TCD are the best condition to obtain uniform PVA/$TiO_2$ nanofibers. $TiO_2$ nanoparticles give significant effect in fiber morphology. $TiO_2$ content increases the diameter of the fibers and roughen the fiber surfaces. The PVA/$TiO_2$ nanofibers were characterized by scanning electron microscope (SEM), transmission electron microscope (TEM) and X-ray diffraction (XRD).

• Proceedings of the Korean Fiber Society Conference
• /
• 2003.10b
• /
• pp.46-48
• /
• 2003

Poly(vinyl alcohol) (PVA) obtained from PVPi has the highest syndiotacticity among (PVA)s obtained via radical polymerization, and the s-diad content of PVA prepared by low temperature polymerization of vinyl pivalate (VPi)[1-5] comes to eve. 60%, Therefore, we an obtain (PVA)s with various tacticities through the copolymerization of vinyl acetate (VAc) and VPi and can examine the relation between physical properties of (PVA)s and their tacticities. (omitted)

• Proceedings of the Korean Fiber Society Conference
• /
• 1999.10a
• /
• pp.25-28
• /
• 1999

• Proceedings of the Korean Fiber Society Conference
• /
• 2001.04a
• /
• pp.301-304
• /
• 2001

• Proceedings of the Korean Fiber Society Conference
• /
• 1995.10a
• /
• pp.68-69
• /
• 1995