• 대한기계학회논문집A
• /
• 제40권3호
• /
• pp.281-288
• /
• 2016

복합재는 재료 불균질성에 의해 고속 충돌 시 방호성능 자료가 산포한다. 본 연구에서는 다수의 충돌시험으로 복합판재 잔류속도 산포를 확보하고 수치해석으로 예측하는 방법을 정립하였다. 먼저 10개의 동일 시편으로 인장시험을 수행하여 파단변형률 산포를 얻었다. 같은 재료로 제작된 4ply([0/90]s)와 8ply([0/90/0/90]s) GFRP(Glass Fiber Reinforced Plastic) 복합판재에 FSP(Fragment Simulating Projectile) 고속 충돌시험을 동일 조건에서 다수 수행하여 잔류속도 산포를 얻었다. 인장시험에서 얻어진 파단 변형률 분포를 이용하여 수치해석을 수행하였다. 충돌속도는 4ply와 8ply 각각 411.7m/s와 592.5m/s이다. 시험 결과와 비교하여 적절한 잔류속도의 산포를 예측할 수 있었다. 추가적으로 복합판재의 경우 Solid요소 대비 Layered Solid요소로 모델링하면 계산시간이 감소되었다.

• Advanced Composite Materials
• /
• 제17권1호
• /
• pp.57-73
• /
• 2008

The present paper focuses on experimental verification of the ply-by-ply basis inelastic analysis of multidirectional laminates. First of all, rate dependence of the tensile behavior of balanced symmetric cross-ply T800H/epoxy laminates with a $[0/90]_{3S}$ lay-up under off-axis loading conditions at $100^{\circ}C$ is examined. Uniaxial tension tests are performed on plain coupon specimens with various fiber orientations $[{\theta}/(90-{\theta})]_{3S}$ ($\theta$ = 0, 5, 15, 45 and $90^{\circ}C$) at two different strain rates (1.0 and 0.01%/min). The off-axis stress.strain curves exhibit marked nonlinearity for all the off-axis fiber orientations except for the on-axis fiber orientations $\theta$ = 0 and $90^{\circ}$, regardless of the strain rates. Strain rate has significant influences not only on the off-axis flow stress in the regime of nonlinear response but also on the apparent off-axis elastic modulus in the regime of initial linear response. A macromechanical constitutive model based on a ply viscoplasticity model and the classical laminated plate theory is applied to predictions of the rate-dependent off-axis nonlinear behavior of the cross-ply CFRP laminate. The material constants involved by the ply viscoplasticity model are identified on the basis of the experimental results on the unidirectional laminate of the same carbon/epoxy system. It is demonstrated that good agreements between the predicted and observed results are obtained by taking account of the fiber rotation induced by deformation as well as the rate dependence of the initial Young's moduli.

• Composites Research
• /
• 제32권1호
• /
• pp.6-12
• /
• 2019

본 논문에서는 Cross-ply 탄소섬유/에폭시 복합재 적층판의 모드 I 층간분리 특성을 분석하였다. 이를 위하여 Cross-ply 시편에 대한 Double-Cantilever Beam(DCB) 시험을 수행하였다. Cross-ply DCB 시편의 경우 층간 및 층내 파괴를 포함한 복합적인 균열 성장과 기하학적 대변형에 의한 비선형성을 수반하였다. 따라서 변형률 에너지 해방률과 유한요소해석을 기반으로 비선형성을 수반한 DCB 시험에서도 적용되는 모드 I 층간 파괴인성 평가방법을 제안하고 기존의 선형이론으로 구한 결과와 비교 분석하였다. 본 연구에서 제안한 방법으로 Cross-ply DCB 시편의 모드 I 층간 파괴인성과 모드 I 층내 파괴인성을 분류하였고 모드 I 층내 파괴인성이 더욱 낮음을 확인하였다.

• 한국공간구조학회논문집
• /
• 제2권4호
• /
• pp.29-36
• /
• 2002

The responses of composite laminated beams modeled with finite element and excited by stochastic loading are studied. The cantilevered laminated beam having a 5 ply configuration is considered. The beam is 1m long, 0.1m wide, and 0.02m thick, yielding a length to thickness ratio of L/h=50. The laminated beams was assumed to be made of Born Epoxy. The four nodes at the free end of the cantilever were loaded with identical zero-mean white noise excitations. Stress and failure analysis loaded with identical zero-mean white noise excitations is carried out. Along with the obtained results, comparison and discussion are presented for the cases of symmetric-ply, antisymmetric-ply, angle-ply, and cross-ply laminated beams.

• Journal of Biosystems Engineering
• /
• 제23권1호
• /
• pp.1-12
• /
• 1998

This study was intended to investigate experimentally the effect of inflation pressure on tractive performance of bias-ply tires for agricultural tractors. Traction tests were conducted at the three velocities of 3, 4, and 5.5km/h under few different surface conditions using a 13.6-28 6PR bias-ply tire as driving wheel of the test tractor. When the inflation pressure was reduced from 250kPa to 40kPa by a decrement of either 30 or 50kPa depending upon the test surface conditions, some of the test results showed that the tractive coefficient and efficiency were increased maximally by 40% and 17％, respectively, at 20% slippage. However, it was failed to derive any consistent rules depicting the effect of inflation pressure of bias ply tires on the tractive performance of tractors.

• 한국정밀공학회지
• /
• 제29권9호
• /
• pp.938-945
• /
• 2012

To design and estimate material failures of Type III pressure vessels, which have excellent stability and performance, various modeling techniques have been introduced. This paper provided a hybrid modeling technique composed of ply-based modeling for a cylinder part and laminate-base modeling technique for a dome part for enhancing modeling efficiency. The ply-based modeling technique provided accurate ply stresses directly for predicting material failure, on the other hand, additional manipulations in stress calculations, which may cause some errors, were needed for the case of the laminate-based modeling technique. The ply stresses in fiber, transverse and in-plane shear directions were compared with the corresponding material strengths to predict material failure.

• Journal of the Korean Wood Science and Technology
• /
• 제26권1호
• /
• pp.87-96
• /
• 1998

The bending performances were evaluated at the radiata pine plywood through veneer compositions encompassing veneer quality, ply-numbers and overlays of the high density- or medium density-phenol resin impregnated sheets (hereafter abbreviated as resin sheets) on the raw plywood. In addition, a prediction on the bending MOE of veneers and plywoods was carried out by the nondestructive testing with stresswave timer. The summarized results were as follows: I. Bending strength and bending MOE of resin sheets-overlaid plywoods in parallel surface grain direction through 5 and 7ply were increased by 13 to 45% and 17 to 34%, respectively. Resin sheets-overlay occurred an increasing effect of the strength efficiency i.e. strength perpendicular-to-grain direction versus that parallel-to-grain direction, showing the phenomenon that the plywood strength becomes greater at the perpendicular-to-grain direction of 7ply than at that of 5ply. Displacement at bending failure had a greater trend at 7ply than at 5ply, and was decreased by resin sheets-overlay. 2. After the nondestructive bending MOEs were measured for individual veneers, these veneers were rearranged in plywood-manufacture. In these plywoods, including resin sheets-overlay, the actual MOE was predictable with feasibility of $R^2$=0.53, and also the nondestructively-evaluated MOE was lower by 20% in raw plywood, and higher 20% in LVL than actual bending MOEs.

• 한국재난정보학회 논문집
• /
• 제11권4호
• /
• pp.527-533
• /
• 2015

본 논문은 초기하중을 받는 역대칭 Cross-Ply 원통쉘의 동적특성을 고유진동수를 이용하여 해석하였다. 마주보는 두변이 단순지지된 적층 원통쉘의 운동방정식은 곡률항을 고려한 Mindlin 쉘이론과 에너지원리를 이용한 Rayleigh-Ritz법을 이용하여 유도하였다. 초기응력을 받는 적층쉘의 고유진동수, 임계좌굴계수 및 동적불안정영역 문제들을 무재하시의 무차원화 고유진동수로서 각각의 특성을 정립하였다. 본 연구에서 제안한 진동특성에 관한 간편산정식의 타당성과 사용성을 입증하기 위해 수치예를 들어 검토하였다.

• Journal of the Korean Wood Science and Technology
• /
• 제48권6호
• /
• pp.907-916
• /
• 2020

This research was conducted to investigate the linear expansion and resistance properties of a composite board (com-ply). This board was made of medium-density fiberboard (MDF) laminated using avocado (Persea americana), mahogany (Swietenia mahogani), and pine (Pinus merkusii) veneers. These three types of veneers were laminated on both surfaces of the MDF using adhesives, namely, epoxy and isocyanate. Glue (250 g·m^-2) was spread on the surface, followed by cold press for 3 h with an applied pressure of 15 kg·cm^-2. The research result revealed that com-ply exhibited an increased dimensional stability compared with MDF, indicated by reduction in water absorption, thickness swelling, and linear expansion. The com-ply made of the pine veneer and isocyanate adhesive exhibited high density, water absorption, thickness swelling, and screw withdrawal load. The com-ply that exhibited the strongest resistance to drywood termite attacks was the one made of the mahogany veneer and isocyanate adhesive. Moreover, the com-ply that exhibited the biggest weight loss (3.6 %) was made of the pine veneer and epoxy adhesive. The results of this research may facilitate in manufacturing com-ply using the selected veneer and adhesive without the application of hot press.

• 한국염색가공학회지
• /
• 제24권4호
• /
• pp.288-295
• /
• 2012

Although some degree of mechanical properties of suede fabrics mainly related to non-woven suede fabric has some researched, the thin suede fabric has rarely been researched. In this study, polyester(DTY 50/72) was used for warp, and after producing latent yarn and sea-island yarn for weft, two yarns were compounded to produce sea-island DTY yarn. By using the two produced yarns for warp and weft, we produced thin suede fabric with stretch function. For weft 2ply, weft density 85, 90, 100(picks/in) were applied to weave fabric, and for weft 1ply, weft density 125, 135, 140(picks/in) were applied to produce weft face 5-end satin weave. The mechanical properties of the produced fabric were researched. The result are as followed. The weight loss ratio of the suede fabric produced for this experiment reached 15% on the conditions of temperature $90^{\circ}C$ and 20 minutes, so that island parts were completely separated. The strength of weft 1ply applied suede fabric was about 7.5kg and that of 2ply suede fabric and about 3.5kg. But the strain of two samples ranged from about 40 to 43%. Although Hari was high when weft was denser. The values of Koshi and Kisimi were low. And shear stiffness was high when sea-island DTY yarn was used. The WC value was higher in the case of 2ply than in that of 1ply sea-island DTY yarn for weft, so that we may conclude that Fukurami was more affected in the 2ply case.