• 대한기계학회논문집A
• /
• 제22권3호
• /
• pp.554-561
• /
• 1998

Vehicle body structures are formed by thousands of spot welds and fatigue failure of vehicle structures occur near the spot welds after driving a long way at a durability test road. It is necessary to know accurately the reason of the fatigue failure of the spot weld in the developing stage in order to reinforce it. Many investigations have been done regarding the strength of spot welded joints, contributing to understand its fatigue strength. In developing process, a fatigue failed spot welded area can be repaired by $CO_2$ welding or another method to continue the test. To know the effect of reinforcing these welds, several methods of welding were analyzed and compared to spot welding. With the results of this test, the appropriate repair method can be used instead of spot welding during the development of new car and best design guide can be given for the strength. In this study, fatigue and static tensile tests are made and microstructure is investigated for the purpose of estimating the strength of welded joints by using spot welded and $CO_2$ plug welded specimens. The tested specimens are of two types : Tensile-shear type(TS) and L-tension type(LT).

• 대한기계학회논문집A
• /
• 제34권9호
• /
• pp.1137-1143
• /
• 2010

가스용접 구조물의 장 수명 피로설계기준(fatigue design criterion)을 결정하기 위해서는 정확한 응력해석과 체계적인 피로강도평가가 필요하다. 그러나 실 구조물로부터 피로설계기준을 결정하는 것은 대단히 어려우므로 구조물의 기계적 구조적 특성을 만족하는 간편 시편을 만들어서 $\Delta{\sigma}-N_f$ 관계를 도출하여 피로강도를 평가하고 있다. 그리고 가스용접에 의해 제작된 실 구조물의 피로설계를 위해서는 피로균열발생과 파단 기점이 되는 용접부의 용접잔류응력(welding residual stress)이 고려되어야 한다. 따라서, 본 연구에서는 플러그 및 링 가스용접 이음재에 대한 용접잔류응력을 고려하기 위해 용접 열 사이클(heat cycle)에 의한 비선형 열해석(non-linear thermal analysis)과 열 응력(thermal stress) 해석을 수행하고, 실험 치와 비교 분석하여 용접잔류응력을 고려한 응력 진폭-피로수명($(\sigma_a)_R-N_f$) 관계를 도출하여 자동적으로 피로설계기준을 제시할 수 있도록 하고자 하였다.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2008년도 추계학술대회A
• /
• pp.1355-1360
• /
• 2008

Stainless steel sheets are widely used as the structure material for the railroad cars and the commercial vehicles. These kinds structures used stainless steel sheets are commonly fabricated by using the gas welding. Gas welding is very important and useful technology in fabrication of an railroad car and vehicles structure. However fatigue strength of the gas welded joints is considerably lower than parent metal due to stress concentration at the weldment, fatigue strength evaluation of gas welded joints are very important to evaluate the reliability and durability of railroad cars and to establish a criterion of long life fatigue design. In this paper, ${\Delta}P-N_f$ curve were obtained by fatigue tests. Using these results, the accelerated life test (ALT) is conducted. From the experimental results, an acceleration model is derived and acceleration factors are estimated. So it is intended to obtain the useful information for the fatigue lifetime of plug and ring gas welded joints and data analysis by statistic reliability method, to save time and cost, and to develop optimum accelerated life prediction plans.

• 한국자동차공학회논문집
• /
• 제19권3호
• /
• pp.1-8
• /
• 2011

Stainless steel sheets are widely used as the structure material for the railroad cars and the commercial vehicles. These kinds structures used stainless steel sheets are commonly fabricated by using the gas welding. Gas welding is very important and useful technology in fabrication of an railroad car and vehicles structure. However fatigue strength of the gas welded joints is considerably lower than parent metal due to stress concentration at the weldment, fatigue strength evaluation of gas welded joints are very important to evaluate the reliability and durability of railroad cars and to establish a criterion of long life fatigue design. In this paper, ${\Delta}-N_f$ curve were obtained by fatigue tests. Using these results, the accelerated life test (ALT) is conducted. From the experimental results, an acceleration model is derived and acceleration factors are estimated. So it is intended to obtain the useful information for the fatigue lifetime of plug and ring gas welded joints and data analysis by statistical reliability method, to save time and cost, and to develop optimum accelerated life prediction plans.

• Journal of Welding and Joining
• /
• 제28권1호
• /
• pp.77-85
• /
• 2010

Stainless steel sheets are widely used as the structure material for the railroad cars and the commercial vehicles. These kinds structures used stainless steel sheets are commonly fabricated by using the gas welding. Gas welding is very important and useful technology in fabrication of a railroad car and vehicles structure.However fatigue strength of the gas welded joints is considerably lower than parent metal due to stress concentration at the weld, fatigue strength evaluation of gas welded joints are very important to evaluate the reliability and durability of railroad cars and to establish a criterion of long life fatigue design. In this paper, $({\Delta}{\sigma}_a)_R-N_f$ curve were obtained by fatigue tests. Using these results, the accelerated life test(ALT) was conducted. From the experimental results, an acceleration model was derived and acceleration factors are estimated. So it is intended to obtain the useful information for the fatigue lifetime of plug and ring gas welded joints and data analysis by statistic reliability method, to save time and cost, and to develop optimum accelerated life prediction plans.

• 한국지반공학회:학술대회논문집
• /
• 한국지반공학회 1999년도 가을 학술발표회 논문집
• /
• pp.381-388
• /
• 1999

The existing methods for installation of long steel pipe pile have some uneconomical problems such as increase of installation cost and period due to the welding of two piles and removal of soil plug, and decrease of driving efficiency due to the increase of driving resistance by time effect during the welding of piles and removal of soil plug, etc. Thus, in this study, new installation method for long steel pipe pile is suggested to work out the existing problems, and calibration chamber tests are peformed to investigate both driving and economical efficiency for the suggested method. The test results showed that the new installation method has increase bearing capacity as well as reduce installation cost and period for long steel pipe piles as compared with existing methods.

• 한국지반공학회논문집
• /
• 제16권1호
• /
• pp.235-241
• /
• 2000

기존의 장대강관말뚝 공법들은 말뚝의 용접이음이나 관내토의 제거 작업으로 인하여 공비와 공기가 증가하고 이들 작업이 진행되는 동안 시간효과에 의하여 말뚝의 관입 저항이 증가하여 타입이 어려워지는 등 각종 비경제적인 문제점들을 갖고 있다. 이러한 문제들을 해결하기 위하여 본 연구에서는 새로운 장대강관말뚝 공법을 제안하였으며, 제안된 공법의 시공성과 경제성을 분석하기 위하여 모형말뚝시험을 행하였다. 시험결과 새로 제안된 장대말뚝공법은 기존 공법에 비해 공기와 공비는 절감되고 지지력은 증가시키는 것으로 나타났다.

• Journal of Welding and Joining
• /
• 제28권4호
• /
• pp.49-54
• /
• 2010

Stainless steel sheets are widely used as the structural material for the railroad cars and the commercial vehicles. These kinds structures used stainless steel sheets are commonly fabricated by using the GMAW (gas metal arc welding). For fatigue design of GMA welded joints such as fillet and plug, ring type joint, it is important to obtain optimum design factor information on GMA welded joints. in this paper, analysis approach for fatigue test using design of experiment are evaluated optimum factor in GMA welded joint type and geometrical parameters of materials. Using these results, that factors applied to fundamental information for fatigue design.

• 한국공작기계학회논문집
• /
• 제15권4호
• /
• pp.98-104
• /
• 2006

In this paper, for the purpose of investigation the acoustic emission(AE) behaviors during resistance spot welding process and tension test of spec steels. As the results present the resistance spot welding method that can get suitable welding qualities or structural integrity estimating method. The resistance spot welding process consists of several stages: set-down of the electrodes; squeeze; current flow; forging; hold time; and lift-off. Various types of AE signals are produced during each of these stages. For tensile-shear test and cross tensile test in resistance spot welded specimens, fracture pa 야 ems are produced: tear fracture; shear fracture; and plug fracture. Tensile-shear specimens strength appeared higher than cross tensile specimens one. In case of tensile-shear specimen happened tear fracture that crack happens in most lower plate. Also, in case of cross tensile specimens, upper plate and lower plate are detached perfect fracture was exposed increases a little as acting force is lower than ordinary welding condition. Therefore, the structure which is combined by resistance spot welding confirmed that welding design must attain so that shear stress may can interact mainly.

• 한국안전학회지
• /
• 제20권1호
• /
• pp.87-93
• /
• 2005

In this paper, we analyzed ignition characteristics of combustible material and the waveform of power dissipation, voltage and current by poor contact. And the surface structure of plug by poor contact was analyzed. In the results of experiment, the heat generated by poor contact and ignited the combustible material on power cord sets. The insulation material was molten and carbonized by the heat conduction though plug pit and voids were formed inside of insulation material. The waveform of voltage and power dissipation distorted because of a growth of oxidation by poor contact. In particular, in case that load was big load, the waveform of voltage and power dissipation severely distorted as with the passage of time. The surface of plug pin was changed from erosion mark to welding mark according to big load. The results will be applied to the cause analysis of electrical disaster.