This is an experimental study on manufacturing of non-cement matrix. Materials like cement and blowing agent in foamed concrete is replaced by by-products from blast furnace slag and paper ash. Further, the experiment was performed by replacing alkali with red mud by (0, 5, 10, 15, 25, 35, 45) of weight of alkali (wt.%) in order to reduce the amount of expensive alkali acclerator. Sample Plain with density showed lowest. The compressive strength test result, showed a similar trend with density. And it showed that compressive strength of the RM-0.05 was highest.

• Steel and Composite Structures
• /
• 제6권1호
• /
• pp.1-14
• /
• 2006

Experiments have been carried out on six composite and two plain steel plate girders under shear loading to understand the elastic and inelastic behaviour of such girders. The failure mechanism assumed and used to develop design equations is normally based on the failure patterns observed in the experiments. Therefore, different types of cracks and failure patterns observed in the experiments are reviewed briefly first. Based on the observed failure patterns, a design method to predict the ultimate shear capacity of composite plate girders is proposed in this paper. The values of ultimate shear capacity obtained using the proposed design method are compared with the corresponding experimental values and it is found that the proposed method is able to predict the shear capacity accurately.

• 한국제4기학회지
• /
• 제16권1호
• /
• pp.55-62
• /
• 2002

한반도 중부지역 경기 서부지역의 두 지점의 청동기유적에서 출토된 토기에 대한 기초적인 관찰에서 태토와 비짐의 구성 광물 결정의 크기와 종류의 차이가 관찰되는데, 이는 태토와 비짐의 출처에 따라 다를 수 있을 것이며 또한 토기를 제작하는 기술의 차이에서 왔을 가능성도 있다고 보여진다. 정확한 판정을 위해 더 많은 토기편에 대한 분석이 필요하다고 생각된다.

• 한국세라믹학회지
• /
• 제45권6호
• /
• pp.350-357
• /
• 2008

The use of shotcrete-sprayed concrete for the support of underground excavations was pioneered by the civil engineering. Now, for the nuclear wastes disposal plant in our country, watertightness of shotcrete is one of the very important properties. This study evaluated the watertightness of shotcrete using cement mineral accelerator with watertightness materials for the long-term watertightness. In this study, for improvement of watertightness of shotcrete, it used two types of obtainable at a store. Watertightness tests of shotcrete were performed the water absorption coefficient, permeability, porosity and hydrates variation. In a shotcrete containing watertightness materials, watertightness of shotcrete was improved about $15%{\sim}65%$ rather than plain shotcrete.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2010년도 춘계 학술논문 발표대회 2부
• /
• pp.53-56
• /
• 2010

In this study, three kinds of cellulose fibers to crack reduction performance were evaluated and the results are as follows. Plastic shrinkage cracking is evaluated by the relative crack area, at all levels between $0.9kg/m^3$ and $1.2kg/m^3$, except for UF0.9% of upto50% showed are duction compared with Plain. In according to recommended amount of fiber in each area of the crack HF0.9>CEL1.2>UF0.6 effect of the order was more effective. While the impact strength of UF and CEL fibers until the final destruction are about five times the number of falls, HF fiber count drop was 10-18 time.

• 한국도로학회논문집
• /
• 제15권5호
• /
• pp.81-89
• /
• 2013

PURPOSES : This study is to evaluate ASR(alkali silica reactivity) resistance of ternary blended binder adding ultra fine mineral admixture. METHODS : This study analyzes ASR expansion using ASTM C 1260 and 1567. RESULTS : This study showed that the fineness of mineral admixture had no effect on ASR expansion. The expansion of ternary blended binder(UFFA 20%+FGGBS 10%) were below 0.1%, and this binder met the ASR standard. Also when adding the CSA expansion agent, ASR expansion slightly decreased. The expansion of latex modified mixture increased by 80% comparing plain mixture. CONCLUSIONS : Ternary blended binder met the ASR standard, and this binder is available in concrete bridge deck overlay.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2022년도 가을 학술논문 발표대회
• /
• pp.165-166
• /
• 2022

In this paper, the characteristics of slag cement mortar added with neutralized liquid red mud with nitric acid to reduce pH by neutralizing liquid red mud with nitric acid were reviewed to improve strength degradation of cement concrete added with liquid red mud. As a result, the compressive strength of cement mortar added with liquid red mud was higher than that of Plain on 1 and 3 days, and the strength of red mud neutralized with nitric acid was lower than that of cement mortar added with liquid red mud on 7 days, but the strength was recovered on 28th. It was found that the addition of red mud has the effect of improving the strength in the early age.

• 콘크리트학회논문집
• /
• 제23권4호
• /
• pp.479-486
• /
• 2011

이 연구에서는 휨인장강도 평가 방법에 따른 무근 콘크리트 원형패널의 휨거동을 비교하기 위해 유한요소해석과 실험을 수행하였다. 이를 위해 ASTM C 1550 round panel test(RPT) 시험법과 biaxial flexure test(BFT) 시험법을 적용하여 콘크리트 원형패널의 휨인장강도를 측정하였으며, 두 원형패널에 작용하는 응력 분포를 알아보기 위하여 패널의 아랫면 중앙에 두 개의 변형률 게이지가 직교하도록 부착하여 하중-변형률 관계를 측정하였다. 실험 결과 RPT 시험체와 BFT 시험체의 파괴 형상은 유사하게 관찰되었으며, 두 시험체 모두 중앙 아랫면의 하중-변형률 관계 또한 모든 방향에 일정한 것으로 나타나, 시험 시 등방성 휨인장응력 상태에 놓이는 것을 확인할 수 있었다. RPT 시험에 의한 평균 휨인장강도가 BFT의 경우보다 29% 더 큰 것으로 나타났다. 두 시험체의 휨인장강도 분포 모두 정규분포를 보이는 것으로 나타났으며, RPT 휨인장강도의 변동계수(coefficient of variation)와 BFT의 변동계수는 각각 8%와 6%로 측정되었다. 이는 BFT 시험을 통하여 신뢰할 수 있는 이방향 휨인장강도 측정이 가능한 것으로 판단된다.

• 한국도로학회논문집
• /
• 제7권3호
• /
• pp.31-42
• /
• 2005

본 연구는 도로용 포장재로서 포러스콘크리트의 실질적인 현장적용을 위한 자료제시와 성능향상 방안을 도출하기 위하여 실리카퓸과 강섬유 혼입률에 따른 포장용 포러스콘크리트의 물리 역학적 특성, 내구성 및 흡음특성을 평가하였다. 시험결과, 모든 시험조건에서 포장용 포러스콘크리트의 공극률과 투수계수는 국내외 기준치 및 제안값을 만족시키는 것으로 나타났고, 강도특성의 경우 압축강도는 대한주택공사 도로기준의 기준치를 모든 배합요인에서 만족시키는 것으로 나타났으나 휨강도의 경우에는 강섬유 혼입률 0.6vol% 이상에서 일본콘크리트공학협회 제안값을 만족시키는 것으로 나타났으며, 실리카퓸과 강섬유를 동시에 혼입한 경우가 우수한 강도특성을 나타냈다. 또한 내구성은 역학적 특성과 유사한 경향성을 나타내 실리카퓸과 강섬유를 동시에 사용한 경우가 가장 우수한 내구성능을 나타냈으며, 실리카퓸 10wt.%와 각섬유 0.6vol.%를 함께 사용한 경우 Plain의 경우에 비해 골재비산저항성은 27%정도, 동결응해저항성은 약 60%정도 개선되는 것으로 나타났다. 또한 포장용 포러스콘크리트의 흡음특성은 소음저감계수가 0.48로 나타나 50%에 가까운 흡음성능을 발휘하는 것을 확인할 수 있었다.

• 한국전산구조공학회논문집
• /
• 제31권5호
• /
• pp.251-258
• /
• 2018

도심지나 문화재가 인접한 지역 등의 소음, 진동 등 기존 발파해체 공법이 제한적인 조건에서 사용할 수 있는 구조물 해체공법으로 무소음화학팽창제(soundless chemical demolition agent, SCDA)를 이용한 공법이 있다. 그러나 SCDA의 사용에 대한 기준이나 가이드라인에 참고될 만한 연구는 미미한 실정이다. 이 연구에서는 실내실험을 수행하여 강관의 길이, 외부수분차단, 수화열 발산 등의 다양한 조건에 따른 SCDA의 팽창압 발현 특성을 확인하였다. 또한 SCDA의 최소요구팽창압 예측을 위한 해석모델(자유단 1면, 고정단 3면의 직사각형 모델)을 개발하고 주요변수해석(홀 간 거리, 콘크리트 압축강도)을 수행하였다. 이 연구의 해석결과를 활용하여 자유단으로부터 콘크리트 구조물의 박락을 효과적으로 유도할 수 있을 것으로 판단된다.