• 한국진공학회지
• /
• 제12권S1호
• /
• pp.21-27
• /
• 2003

Micro-arc discharge oxidation (MDO) is a cost-effective plasma electrolytic process which can be used to improve the wear and corrosion resistance of Al-alloy parts by forming a alumina coating on the component surface. However, the MDO coated Al-alloy components often exhibit relatively high friction coefficients and low wear resistance fitted with many counterface materials, additionally, the pitting corrosion for the MDO coated AI-alloy components, especially for a thinner alumina coating, often occurs in atmosphere circumstance due to the porous alumina coats. Therefore, a duplex treatment, combining a MDO coated ahumina thin layer with a TiN coating, prepared by magnetron sputtering (MS), has been investigated. The Vicker's microhardness, pin-on-disc, electrochemical measurement, salt spray, XRD and SEM tests were used to characterize and analyze the treated samples. The work demonstrates that the MDO/MS coated samples have a combination of a very low friction coefficient and good wear resistance as well as corrosion since the micro-holes on alumina coating are partly or fully covered by TiN material.

• 한국표면공학회지
• /
• 제50권6호
• /
• pp.432-438
• /
• 2017

AZ91D casting alloy requires an advanced plasma anodizing processing because large amount of defects are liable to generate during anodization. In this study, plasma electrolytic oxidation (PEO) of AZ91D Mg alloy was conducted by the application of either constant voltage or current using a pulse mode and its effects on pore formation, surface roughness and corrosion resistance were investigated. The PEO films showed a three-layer structure. The PEO film thickness was found to increase linearly with voltage. The surface roughness, Ra, ranged between $0.2{\mu}m$ and $0.3{\mu}m$. The corrosion resistance increased from RN 3.5 to 9.5 by the PEO treatment when evaluated according to the 72 hour salt spray test. The PEO-treated surface exhibited higher pitting potential than the raw material.

• 한국표면공학회지
• /
• 제36권4호
• /
• pp.339-346
• /
• 2003

Stainless steel wire has been used in industry, dental and medical parts. Especially, it has been used widely for the dental orthodontic materials. The orthodontic wire requires good mechanical properties, such as elastic strength, combined with a high resistance to corrosion. To increase elastic strength and good corrosion resistance, drawing methods(one-step and two-step drawing) have been used and the electrochemical characteristics of drawed wire have been researched using potentiodynamic method in 0.9％NaCl and field emission scanning electron microscope. The one-step drawed wire showed the formation of rough surface. The hardness and tensile strength of two-step drawed wire increased. For the case of two-step drawed wire, the corrosion resistance and pitting potential increased compared with one-step drawed wire due to the drawing induced small surface roughness, such as scratch. The passivation and active current density decreased as the reduction in area for drawing increased.

• 대한금속재료학회지
• /
• 제46권8호
• /
• pp.489-494
• /
• 2008

The effect of drawing rate on the electrochemical properties of 3003 Al alloys in 5 wt.% NaCl solution was investigated by electrochemical techniques (potentiodynamic polarization test, potentiostatic polarization test, electrochemical impedance spectroscopy (EIS)) and surface analyses (OM, SEM, EDS). Four kinds of automotive pipe materials were prepared (raw material, drawing rate = 5, 10, 15%). As the drawing rate of Al alloy tube increased, the pitting corrosion resistance increased due to the enrichment of Al oxides on the surface.

• 부식과 방식
• /
• 제12권1호
• /
• pp.12-23
• /
• 2013

원자력 발전소 주요 부품에 사용되는 Alloy 600의 PWSCC 개시와 전파기구를 살펴보고 그 억제 기술을 소개하였다. ○ 균열은 경화된 표면 산화층이 깨질 경우, 입계부식, 공식(pitting), 열처리 또는 물속에 노출되었을 때 일어나는 선택부식(selective corrosion), MnS등 게재물의 용출등에 의해 시작된다. ○ 균열의 전파는 '느린 성장'과 '빠른 성장'으로 구별해 볼 수 있는데 빠른 균열성장은 균열 선단에서의 응력확대 계수(K_I)가 균열이 전파하는 임계값(K_Iscc)을 넘는 경우에 일어난다. ○ Slip Dissolution/Film Rupture Model, Enhanced surface mobility model, Hydrogen assisted creep rupture, Internal oxidation 등의 모델이 제시되어 있으며 Internal oxidation 모델이 여러 실험자료로 잘 뒷 받침되고 있다. ○ PWSCC 억제 방안으로는 부식환경과의 격리 및 보수용접이 대표적이며 부품의 교체를 통한 안전 확보의 방안도 있다. 수소량 조절을 통한 억제 방안도 제시되어 있다. ○ Alloy 600 PWSCC열화 관리 전략프로그램은 결함 발생 가능성이 높은 부위 선정, 우선 순위에 따른 계획적인 검사, 결함이 발견될 경우 완화조치를 취하거나 필요시 교체/보수를 실시하고 그 운영프로그램을 지속적으로 갱신관리하는 방안으로 유지되어야 한다.

• 한국표면공학회지
• /
• 제49권5호
• /
• pp.431-438
• /
• 2016

This research investigated the relationship between the corrosion damage characteristics of offshore wind steel substructure and the time of current density application by electrochemical accelerated short-term corrosion test. The galvanostatic corrosion was conducted on the steel specimens in natural seawater with a constant current density ranging from $1mA/cm^2$ to $200mA/cm^2$ for 1 ~ 180 min. Macro and micro observation was carried out on the surface of the corrosion damaged area using SEM and 3-dimensional analysis microscope. The weight loss of the specimens before and after was calculated as the difference between the initial weight prior to corrosion and weight after removal of the corrosion product. It was shown that during galvanostaic corrosion process, the corrosion behavior could be characterized by the onset of pitting corrosion in the early stage and the uniform corrosion in the late stage, showing damage development in the depth direction with the time of current application. The result of the 3D analysis revealed that both damage depth and surface roughness increased with increasing time of current application. The weight loss curves with time showed that a coefficient of determination ($R^2$) was relatively high for the relationship between the time of current application and weight loss. As a result, the degree of corrosion can be controlled by simply varying the time of current application.

• 한국표면공학회지
• /
• 제21권4호
• /
• pp.176-182
• /
• 1988

Effects of Cr, Ni and W on the anodic polarization behavior were investigated for Fe-Cr-Ni-W alloys in deaerated 1N HCI solution. Surface films formed on the polarization were analysed using AES, SEM and EDAX. A higerconcentration of tungten was found in the surface oxide film compared to the matrix. It played an importanet role on incresing the stability of the passive film. The presence of an adequate amount of Cr was essential to increase the pitting resistance of the alloys in acid chloride media. Under 12 wt%cr,alloys containing 6wt%W did not exhidit any passivity at all. The main role of Ni was to control the microstructure rather than to modify the corrosion resistance. In 23 cr-14Ni-^W alloy, the duplex microstructure of ferrite($\delta$-phase) in an austenic matrix was developed. The reson why proferred pitting appeared in austenite and ferrite/austenite interface was that ferrite had more amount of Cr and W than austenite.

• 대한금속재료학회지
• /
• 제48권12호
• /
• pp.1090-1096
• /
• 2010

This pitting corrosion study of welded joints of austenitic stainless steels (AISI 304L and 316L) has addressed the differentiating solidification mode using three newly introduced filler wires with a flux-cored arc welding process (FCAW). The delta ferrite (${\delta}$-ferrite) content in the welded metals increased with an increasing equivalent weight ratio of chromium/nickel ($Cr_{eq}/Ni_{eq}$). Ductility dip cracking (DDC) was observed in the welded metal containing ferrite with none of AISI 304L and 0.1% of AISI 316L. The potentiodynamic anodic polarization results revealed that the $Cr_{eq}/Ni_{eq}$ ratio in a 3.5% NaCl solution didn't much affect the pitting potential ($E_{pit}$). The AISI 316L welded metals with ${\ddot{a}}$-ferrite content of over 10% had a superior $E_{pit}$ value. Though the AISI 316L welded metal with 0.1% ferrite had larger molybdenum contents than AISI 304L specimens, it showed a similar $E_{pit}$ value because the concentration of chloride ions and the corrosion product induced severe damage near the DDC.

• Corrosion Science and Technology
• /
• 제20권6호
• /
• pp.451-465
• /
• 2021

In this investigation, electrochemical characteristics and damage behavior of 316L stainless steel polymer electrolyte membrane fuel cell(PEMFC) were analyzed by potentiodynamic and potentiostatic tests in cathode operating condition of PEMFC. As the result of potentiodynamic polarization test, range of passive region was larger than range of active region. In the result of potentiostatic test, damage depth and width, pit volume, and surface roughness were increased 1.57, 1.27, 2.48, and 1.34 times, respectively, at 1.2 V compared to 0.6 V at 24 hours. Also, as a result of linear regression analysis of damage depth and width graph, trend lines of damage depth and width according to applied potentials were 16.6 and 14.3 times larger, respectively. This demonstrated that applied potential had a greater effect on pitting damage depth of 316L stainless steel. The damage tendency values were 0.329 at 6 hours and 0.633 at 24 hours with applied potentials, representing rapid growth in depth direction according to the test times and applied potentials. Scanning electron microscopy images revealed that surface of specimen exhibited clear pitting damage with test times and applied potentials, which was thought to be because a stable oxide film was formed by Cr and Mo.

• 대한금속재료학회지
• /
• 제47권2호
• /
• pp.129-137
• /
• 2009

Corrosion behaviors of TiN coated dental casting alloys have been researched by using various electrochemical methods. Three casting alloys (Alloy 1: 63Co-27Cr-5.5Mo, Alloy 2: 63Ni-16Cr-5Mo, Alloy 3: 63Co-30Cr-5Mo) were prepared for fabricating partial denture frameworks with various casting methods; centrifugal casting(CF), high frequency induction casting(HFI) and vacuum pressure casting(VP). The specimens were coated with TiN film by RF-magnetron sputtering method. The corrosion behaviors were investigated using potentiostat (EG&G Co, 263A. USA) in 0.9% NaCl solution at $36.5{\pm}1^{\circ}C$. The corrosion morphologies were analyzed using FE-SEM and EDX. Alloy 1 and Alloy 2 showed the ${\alpha}-Co$ and ${\varepsilon}-Co$ phase on the matrix, and it was disappeared in case of TiN coated Alloy 1 and 2. In the Alloy 3, $Ni_2Cr$ second phases were appeared at matrix. Corrosion potentials of TiN coated alloy were higher than that of non-coated alloy, but current density at passive region of TiN coated alloy was lower than that of non-coated alloy. Pitting corrosion resistances were increased in the order of centrifugal casting, high frequency induction casting and vacuum pressure casting method from cyclic potentiodynamic polarization test.