• 한국재료학회지
• /
• 제20권9호
• /
• pp.483-487
• /
• 2010

To fabricate $TiO_2$ nanoparticle-based dye sensitized solar cells (DSSCs) at a low-temperature, DSSCs were fabricated using hydropolymer and ZnO nanoparticles composites for the electron transport layer around a low-temperature ($200^{\circ}C$). ZnO nanoparticle with 20 nm and 60 nm diameter were used and Pt was deposited as a counter electrode on ITO/glass using an RF magnetron sputtering. We investigate the effect of ZnO nanoparticle concentration in hydropolymer and ZnO nanoparticle solution on the photoconversion performance of the low temperature fabricated ($200^{\circ}C$) DSSCs. Using cis-bis(isothiocyanato)bis(2,20 bipyridy1-4,40 dicarboxylato) ruthenium (II) bis-tetrabutylammonium (N719) dye as a sensitizer, the corresponding device performance and photo-physical characteristics are investigated through conventional physical characterization techniques. The effect of thickness of the ZnO photoelectrode and the morphology of the ZnO nanoparticles with the variations of hydropolymer to ZnO ratio on the photoconversion performance are also investigated. The morphology of the ZnO layer after sintering was examined using a field emission scanning electron microscope (FE-SEM). 60 nm ZnO nanoparticle DSSCs showed an incident photon-to-current conversion efficiency (IPCE) value of about 7% higher than that of 20 nm ZnO nanoparticle DSSCs. The maximum parameters of the short circuit current density ($J_{sc}$), the open circuit potential ($V_{oc}$), fill factor (ff), and efficiency ($\eta$) in the 60 nm ZnO nanoparticle-based DSSC devices were 4.93 mA/$cm^2$, 0.56V, 0.40, and 1.12%, respectively.

• 한국세라믹학회지
• /
• 제53권4호
• /
• pp.393-399
• /
• 2016

We have successfully fabricated 3D (3-dimensional) nanostructures of $TiO_2$ coated with a $g-C_3N_4$ layer via hydrothermal and sintering methods to enhance photoelectrochemical (PEC) performance. Due to the coupling of $TiO_2$ and $g-C_3N_4$, the nanostructures exhibited good performance as the higher conduction band of $g-C_3N_4$, which can be combined with $TiO_2$. To fabricate 3D nanostructures of $g-C_3N_4/TiO_2$, $TiO_2$ was first grown as a double layer structure on FTO (Fluorine-doped tin oxide) substrate at $150^{\circ}C$ for 3 h. After this, the $g-C_3N_4$ layer was coated on the $TiO_2$ film at $520^{\circ}C$ for 4 h. As-prepared samples were varied according to loading of melamine powder, with values of loading of 0.25 g, 0.5 g, 0.75 g, and 1 g. From SEM and TEM analysis, it was possible to clearly observe the 3D sample morphologies. From the PEC measurement, 0.5 g of $g-C_3N_4/TiO_2$ film was found to exhibit the highest current density of $0.12mA/cm^2$, along with a long-term stability of 5 h. Compared to the pristine $TiO_2$, and to the 0.25 g, 0.75 g, and 1 g $g-C_3N_4/TiO_2$ films, the 0.5 g of $g-C_3N_4/TiO_2$ sample was coated with a thin $g-C_3N_4$ layer that caused separation of the electrons and the holes; this led to a decreasing recombination. This unique structure can be used in photoelectrochemical applications.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2006년도 하계학술대회 논문집 Vol.7
• /
• pp.154-154
• /
• 2006

글씨 전도성 잉크의 인쇄공정에 있어서 반복인쇄를 정밀하게 수행할 수 있는 기술로서 align system을 개발하였다. 이 system의 resolution 은 0.5um 이며 인쇄 working plate의 이송속도는 최대 1.5m/s 이다. 현재 소성 공정을 포함한 반복인쇄 실험은 30um이상의 drop탄착점 오차를 보이고 있으며, 두께와 전기전도도 향상을 위한 정밀한 align system이 필요하게 되었다. 이를 충족시키기 위해 개발되어진 초정밀 align system은 $1{\sim}2{\mu}m$이내의 오차로 반복인쇄가 가능하며, head가 토출하는 잉크의 straightness 및 전도성 잉크를 토출하는 인쇄평가기의 기계적 정밀도도 확인할 수 있다. 모든 잉크 배선의 두께 항상 인쇄실험이 가능하며, substrate의 종류와 잉크에 제한적이지 않다. 특히 prototype의 기판배선을 위해 PCB에 배선을 형성할 시에 본 system으로 직접 align mark를 지정할 수 있어 기판 내에 미리 제작되어진 align용 인식마크가 불필요하다. 이 system을 이용하여 drop과 배선의 반복인쇄실험을 진행하였으며, 광학현미경과 3D profiler를 사용하여 분석해 보았다.

• 센서학회지
• /
• 제11권1호
• /
• pp.9-17
• /
• 2002

X-선 저장 형광체 $BaFBr_{1-x}I_x:Eu^{2+}$, $Na^+$의 조성 조건을 조사하고, 제조한 형광체의 광자극발광 강도, 스펙트럼, fading 특성 및 선량의존성을 조사하였다. 그리고 이 특성을 상업적으로 시판하고 있는 일본 부사(富士)사진필름회사 제품 영상판(ST-III)의 특성과 비교하였다. $BaFBr_{1-x}I_x:Eu^{2+}$, $Na^+$ 형광체의 최적 제조 조건은 $Eu_F3$ 0.5mol%, NaF 4.0mol% 그리고 조성비 x=0.3 이었으며, 소결온도는 수소 분위기에서 $950^{\circ}C$이었다. 조성비 x=0일 때 $BaFBr_{1-x}I_x:Eu^{2+}$, $Na^+$ 형광체의 스펙트럼영역은 $365{\sim}420\;nm$이었고, 최대 발광강도는 390 nm 이었다. $x{\neq}0$일 때 스펙트럼의 파장영역과 피이크 파장은 조성비 x가 증가할수록 장파장쪽으로 이동하였다. X-선 조사선량과 PSL 강도 사이에는 좋은 직선성을 나타내었다. 형광체의 fading 특성은 x=0.3일 때 가장 좋았으며, $I^-$ 이온의 농도가 증가할수록 저하되는 경향을 나타내었다. 또한 $BaFBr_{1-x}I_x:Eu^{2+}$ 격자상수는$I^-$이온의 농도가 증가할수록 커졌다.