• Journal of Nuclear Fuel Cycle and Waste Technology(JNFCWT)
• /
• v.18 no.3
• /
• pp.407-414
• /
• 2020

Thermal decomposition of the uranyl phosphate mineral phase meta-ankoleite (KUO₂PO₄·3H₂O) has been considered in relation to high temperature thermal sintering for the immobilisation of a uranyl phosphate containing waste. Meta-ankoleite thermal decomposition was studied across the temperature range 25 - 1200℃ under an inert N₂ atmosphere at 1 atm. It is shown that the meta-ankoleite mineral phase undergoes a double de-hydration event at 56.90 and 125.85℃. Subsequently, synthetically produced pure meta-ankoleite remains stable until at least 1150℃ exhibiting no apparent phase changes. In contrast, when present in a mixed waste the meta-ankoleite phase is not identifiable after thermal treatment indicating incorporation within the bulk waste either as an amorphous phase and/or as uranium oxide. Visual inspection of the waste post thermal treatment showed evidence of self-sintering owing to the presence of glass former materials, namely, silica (SiO₂) and antimony(V) oxide (Sb₂O₅). Therefore, incorporation of the uranium phase into the waste as part of waste sentencing and immobilisation via high temperature sintering for the purpose of long-term disposal is deemed feasible.

• Restorative Dentistry and Endodontics
• /
• v.41 no.3
• /
• pp.196-201
• /
• 2016

Objectives: The aim of this in vitro study was to evaluate the effect of incorporating three different nanobiomaterials into bleaching material on microhardness of bleached enamel. Materials and Methods: The crowns of 24 extracted sound human molars were sectioned. Sixty enamel specimens ($2{\times}3{\times}4 mm$) were selected and divided into five groups (n = 12): Group 1 received no bleaching procedure (control); Group 2 underwent bleaching with a 40% hydrogen peroxide (HP) gel; Groups 3, 4, and 5 were bleached with a 40% HP gel modified by incorporation of bioactive glass (BAG), amorphous calcium phosphate (ACP) and hydroxyapatite (HA), respectively. The enamel microhardness was evaluated. The differences in Knoop microhardness data of each group were analyzed by one-way ANOVA, followed by post hoc Tukey tests. Results: Significant differences were observed between the study groups. The enamel microhardness changes in Groups 1, 3, 4, and 5 were significantly lower than that of Group 2 (p < 0.001). Conclusions: Within the limitations of this study, it can be concluded that incorporation of each one of the three tested biomaterials as remineralizing agents might be effective in decreasing enamel microhardness changes subsequent to in-office bleaching.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.337-337
• /
• 2009

가시광선영역에서 매우 균일한 높은 투과성뿐만 아니라 근적외선영역에서 가파른 홉수성 엣지와 함께 낮은 투과율을 제공하는 산화구리(II)를 함유하는 포스페이트 유리는 컬러 비디오 카메라의 컬러 보정 필터, 발광 컬러 디스플레이용 보호판(sheild), 모노크로메이터의 미광 필터, 플라스틱 복합재 필터의 무기 성분 및 CCD(전하 결합 소자) 및 CMOS(상보성 금속 산화물 반도체) 카메라 및 검출기 분야용 필터 유리로서 사용된다. 용융온도 및 산화구리(II) 첨가량에 따른 투과율을 측정하기 위해 포스페이트 유리 시료를 $1100\sim1500^{\circ}C$ 용융한 후 $400^{\circ}C$에서 2시간 동안 어닐링 공정을 거쳐 제조하였다. 제조된 시료는 두께 0.3mm로 폴리싱하여 자외선-적외선 분광 광도기를 이용하여 광학적 특성을 측정하였다. 본 실험을 통하여 용융온도에 따라 가시광선영역 및 근적외선영역에서의 투과율 거동을 비교한 결과 $1100\sim1200^{\circ}C$에서의 우수한 투과율 특성을 나타냈다. 용융온도가 내려감에 따른 가시광선영역 (400~600nm)에서 높은 투과율 및 근적외선영역 (750~1100nm)에서 낮은 투과율과 가파른 흡수성 엣지를 나타냈다.

• The Journal of Advanced Prosthodontics
• /
• v.7 no.6
• /
• pp.475-483
• /
• 2015

PURPOSE. The objective of this study was to evaluate the influence of various cement types on the stress distribution in monolithic zirconia crowns under maximum bite force using the finite element analysis. MATERIALS AND METHODS. The models of the prepared #46 crown (deep chamfer margin) were scanned and solid models composed of the monolithic zirconia crown, cement layer, and prepared tooth were produced using the computer-aided design technology and were subsequently translated into 3-dimensional finite element models. Four models were prepared according to different cement types (zinc phosphate, polycarboxylate, glass ionomer, and resin). A load of 700 N was applied vertically on the crowns (8 loading points). Maximum principal stress was determined. RESULTS. Zinc phosphate cement had a greater stress concentration in the cement layer, while polycarboxylate cement had a greater stress concentration on the distal surface of the monolithic zirconia crown and abutment tooth. Resin cement and glass ionomer cement showed similar patterns, but resin cement showed a lower stress distribution on the lingual and mesial surface of the cement layer. CONCLUSION. The test results indicate that the use of different luting agents that have various elastic moduli has an impact on the stress distribution of the monolithic zirconia crowns, cement layers, and abutment tooth. Resin cement is recommended for the luting agent of the monolithic zirconia crowns.

• Imaging Science in Dentistry
• /
• v.51 no.3
• /
• pp.261-269
• /
• 2021

Purpose: The aim of this study was to evaluate the radiopacities of various types of restorative materials with different thicknesses compared with enamel, dentin, and aluminum. Materials and Methods: Four bulk-fill resins, 2 hybrid ceramics, 2 micro-hybrid resin composites, 6 glass ionomer-based materials, 2 zinc phosphate cements, and an amalgam were used in the study. Twelve disk-shaped specimens were prepared from each of 17 restorative materials with thicknesses of 1 mm, 2 mm, and 4 mm (n=4). All the restorative material specimens with the same thickness, an aluminum (Al) step wedge, and enamel and dentin specimens were positioned on a phosphor storage plate and exposed using a dental X-ray unit. The mean gray values were measured on digital images and converted to equivalent Al thicknesses. Statistical analyses were performed using 2-way analysis of variance and the Bonferroni post hoc test(P<0.05). Results: Radiopacity was significantly affected by both the thickness and the material type (P<0.05). GCP Glass Fill had the lowest radiopacity value for samples of 1 mm thickness, while Vita Enamic had the lowest radiopacity value for 2-mm-thick and 4-mm-thick samples. The materials with the highest radiopacity values after the amalgam were zinc phosphate cements. Conclusion: Significant differences were observed in the radiopacities of restorative materials with different thicknesses. Radiopacity was affected by both the material type and thickness.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.29 no.4
• /
• pp.154-159
• /
• 2019

The glass-ceramic of $Li_2O-Al_2O_3-SiO_2$ system was fabricated by using yttrium oxide and iron oxide that it can reduce the melting temperature and affect the homogenization. Zirconium sulfate was used as a nucleation agent. Calcium phosphate was used to improve the flow the glass so as reduce the viscosity of the glass. The glass-ceramics met a thermal shock test of more than $750^{\circ}C$ and the temperature at which the coefficient of thermal expansion rapidly increased at over $800^{\circ}C$ was shifted by about the above $30^{\circ}C$. Therefore, it is concluded that the glass-ceramic of $Li_2O-Al_2O_3-SiO_2$ system with yttrium oxide and iron oxide was founded to have good melting conditions and excellent thermal expansion resistance at high temperature such as special field for kitchen utensils.

• Journal of Periodontal and Implant Science
• /
• v.40 no.3
• /
• pp.125-131
• /
• 2010

Purpose: Among available biomaterials, bioceramics have drawn special interest due to their bioactivity and the possibility of tailoring their composition. The degradation rate and formulation of bioceramics can be altered to mimic the compositions of the mineral phase of bone. The aim of this study was to investigate the bone formation effect of amorphous calcium phosphate glass cement (CPGC) synthesized by a melting and quenching process. Methods: In five male beagle dogs, $4{\times}4$ mm 1-wall intrabony defects were created bilaterally at the mesial or distal aspect of the mandibular second and fourth premolars. Each of the four defects was divided according to graft materials: CPGC with collagen membrane (CM), biphasic calcium phosphate (BCP) with CM, CM alone, or a surgical flap operation only. The dogs were sacrificed 8 weeks post-surgery, and block sections of the defects were collected for histologic and histometric analysis. Results: There were significant differences in bone formation and cementum regeneration between the experimental and control groups. In particular, the CPGC and BCP groups showed greater bone formation than the CM and control groups. Conclusions: In conclusion, CPGC was replaced rapidly with an abundant volume of new bone; CPGC also contributed slightly to regeneration of the periodontal apparatus.

• Restorative Dentistry and Endodontics
• /
• v.16 no.1
• /
• pp.87-105
• /
• 1991

The purpose of this experiment was to measure the leaking and solubility of commonly used dental restorative materials - Silux plus (CS), Hi-pol (CH), Clearfil F-II, Fissureseal (FS), Glass-Ionomer cement Fuji Type II (GI), Amalgam Cavex 68 (AM), Zinc Phosphate Cement (ZP) and gutta-percha (GP) and investigate the relation between the solubility and marginal leakage. Disc-shape specimens were fabricated with each material and dipped into deionized water, 0.01M lactic acid and 0.005M KOH solution, thus the total ionic concentrations in each solution was measured with ion chromatograph after 1, 3, and 7 days, respectively. For the solubility test, each specimen was immersed in 0.001M and 0.01M lactic acid for 24 hours, respectively and total weight loss was calculated. Also, Zn leaking through the margin of restorations was measured. The obtained results were as follows: 1. The amounts of eluted ion from the eight materials were most in 0.01M lactic acid and least in deionized water. 2. Of the eight materials, the fluoride release was greatest for glass ionomer cement (GI) in 0.01 M lactic acid after 7 days. 3. In analysis of the divalent cation, Mg was eluted most for zinc phosphate cement (ZP) and Ca for Clearfil F-II (CF) in 0.01M lactic acid after 7 days. 4. In analysis of transition metals, Cu and Zn were detected only. 5. The solubility rate of eight materials was greater in 0.01M lactic acid than in 0.001M for 24 hours, for zinc phosphate cement (ZP) the rate was greatest (5.4%) in 0.001M lactic acid, and amalgam least (0.01%). 6. The Zn concentration of restorative material with Z.P.C base was greater in 0.01M lactic acid than in 0.001M lactic acid.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.24 no.3
• /
• pp.120-126
• /
• 2014

Translucent green colored opal glass was fabricated to substitute polycarbonate diffuser of LED lighting in order to solve the durability problem. Batch materials of green colored opal glass with the composition of calcium phosphate for opacifier and iron oxide for colorant were made and melted at $1550^{\circ}C$. As the results, translucent green colored opal glass was obtaind, which had excellent optical properties compare with nomal color glass for the diffuser of LED lighting, with no dazzling from direct light by high haze value over 90 % and low parallel transmittance value about 1 %. Therefore, it is concluded that this translucent green colored opal glass can be used for the glass diffuser materials of LED lighting with high heat resistance and high durability to substitute polycarbonate diffuser.

• Journal of the Korean Ceramic Society
• /
• v.40 no.2
• /
• pp.178-183
• /
• 2003

Electrical conductivity of$50Li_2O-xTiO_2-(50-x)P_2O_5$ glasses has been studied with an increase of the intermediate$TiO_2$content. Thermal properties were observed from TG-DTA measurement and the variation of glass structure was investigated by FT-IR. The density and glass transition temperature increased with an increase of the $TiO_2$ content. These results were attributed to the fact that bond strengthening was occurred because of the formation of P-O-Ti cross linkages in the glass. The ionic conductivity increased with $TiO_2$ content and a maximum value, $1.2{imes}10^{-6}$S/cm showed at x=20. The ionic conductivity showed a large increasement as a result that the pyrophosphate group become the predominant structural unit. This result can explain that Li ions mobility increased as a number of non-bridging oxygen on phosphate units increased.