• Journal of Welding and Joining
• /
• v.15 no.3
• /
• pp.88-98
• /
• 1997

Welding defects, such as porosity and spike, have sometimes occurred in deep penetration electron beam welds. These defects are known to be one of the serious problem in electron beam welds. So, effects of active parameters ($a_b$) on bead shape and occurrence of defects in electron beam welds of heavy section 9%Ni steel plates were investigated. Partial penetration welding in flat position, and deep penetration welding of 10 ~ 28mm depth were investigated in this study. It is desirable to select low accelerating voltage and above the surface focus position $a_b$$\geq$1.2 at which a wine-cup shaped bead is obtained to avoid the welding defects such as spike and root porosity. When the accelerating voltage of electron beam was low (90kV), active parameter ($a_b$) did not influence on the bead width, penetration depth and weld defects significantly. However, in case of high voltage ($\geq$120kV), active parameter ($a_b$) was sensitively associated with penetraton depth and weld defects, i.e. when the active parameter (($a_b$) was in the range of 0.6 to 1.0, the depth of penetration was always over the target (23mm), while the depth of penetration was dramatically decreased with further increase of active parameter ($a_b$). The weld defects were decreased with the increase of active parameter $a_b$ resulting in the decrease of energy density of the focused beam in the root part of fusion zone.

• Laser Solutions
• /
• v.4 no.2
• /
• pp.1-12
• /
• 2001

This study has been performed to evaluate basic characteristics of CW-CO$_2$ laser welding process of A5083 and A7N01 Al alloy. The effect of welding parameters, such as shielding gas, gas flow rate, laser power and welding speed on the bead shape and porosity from bead on plate welding tests have been investigated. Welds shielded by He gas had deeper penetration and better bead shape than those shielded by Ar. The penetration depth was augmented with the increase of laser Power and the decrease of welding speed. Welds of A7N01 alloy had deeper penetration than those of A5083 alloy In beads of A5083 alloy which has deeper penetration, the volume fraction of porosities was high due to the number of its was few, but size of its was larger. The case of deeper penetration beads of A7N01 alloy, the porosity reduced under relatively higher power The Volume fraction of porosities in weld of A5083 alloy was significantly higher than that in weld of A7N01 alloy.

• Journal of the Korean Society for Precision Engineering
• /
• v.15 no.6
• /
• pp.167-174
• /
• 1998

The ultrasonic test is recognized for its significance as a non-destructive testing method to detect volume defects such as porosity and incomplete penetration which reduce strength in the weld zone. This paper illustrates the defect detection in the weld zone of ferritic carbon steel using ultrasonic wave and the evaluation of pattern recognition by chaotic feature extraction using time series signal of detected defects as data. Shown in the time series data were that the time delay was 4 and the embedding dimension was 6 which indicate the geometric dimension of the subject system and the extent of information correlation. Based on fractal dimension and lyapunov exponent in quantitative chaotic feature extraction, feature value of 2.15, 0.47 is presented for porosity and 2.24, 0.51 for incomplete penetration The precision rate of the pattern recognition is enhanced with these values on the total waveform of defect signal in the weld zone. Therefore, we think that the ultrasonic pattern recognition method of weld zone defects of ferritic carbon steel by ultrasonic-chaotic feature extraction proposed in this paper can boost precision rate further than the existing method applying only partial waveform.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.30 no.4
• /
• pp.367-372
• /
• 2010

A power plant's heat exchangers work under poor conditions, such as high temperature, high pressure, corrosion, mechanical stress and vibration. Especially, partial joint-weld of heat exchanger's header to stub-tube is the place where incomplete penetration flaws can easily occur. But, it is hard to evaluate the safety of the structure by conventional nondestructive testing techniques. So it is necessary to test integrity of the weld inside and to develop testing technique and equipment that can detect the flaws at the weld point in order to enhance reliability of the test result. In this study, we developed a suitable automated ultrasonic testing system that can inspect the partial joint-weld of header to stub-tube of power plant. Finally, we showed the efficiency of the automated ultrasonic-testing-system from the application.

• Journal of Welding and Joining
• /
• v.17 no.6
• /
• pp.70-77
• /
• 1999

Surface depression in the arc welding is calculated numerically to analyze its influence on pool convection and oscillation. The magnitude of surface depression due to arc pressure on the stationary GTA pool surface is relatively small, and fluctuations of the surface and velocity are caused mainly by arc pressure. The inward flow on the surface due to the electromagnetic force and positive surface tension gradient acts to decrease surface depression. Surface depression appears to have minor effects on average flow velocity and thus pool geometry. Pool oscillation occurs due to surface vibration, and oscillation frequencies are affected mainly by the surface tension and pool width. The input parameters such as arc pressure and current have negligible effects on the oscillation frequency, and the surface tension gradient has limited effects. Since the oscillation frequency varies slightly according to penetration, pool oscillation for the partial penetration weld pool is applicable to monitor the pool width.

• Laser Solutions
• /
• v.2 no.3
• /
• pp.19-31
• /
• 1999

This paper introduces the monitoring scheme of laser welding quality using neural network. The developed monitoring scheme detects light signal emitting from plasma formed above the weld pool with optic sensor and DSP-based signal processor, and analyzes to give a guidance about the weld quality. It can automatically detect defects of laser weld and further give an information about what kind of defects it is, specially partial penetration and porosity among the interior defects. Those could be detected only by naked eyes or X-ray after welding, which needs more processes and costs in mass production. The monitoring scheme extracts four feature vectors from signal processing results of optical measuring data. In order to classify pattern for extracted feature vectors and to decide defects, it uses single-layer neural network with perceptron learning. The monitoring result using only the first feature vector shows confidence rate in recognition of 90%($\pm$5) and decides whether normal status or defects status in real time.

• Journal of Welding and Joining
• /
• v.22 no.6
• /
• pp.19-24
• /
• 2004

The laser welding and its analysis of thin-sheet carbon steels were carried out with high power $CO_{2}$ laser. The main factor of weld quality of laser welding is gap and edge quality. This work was preformed to focus on the gap tolerance problem during laser welding. First, bead on plate welding of thin sheet was examined to investigate the effect of laser welding variables, and to obtain optimum welding condition. Butt welding was also carried out to show the effect of gap on the laser weldability of thin sheet. In order to investigate the effect of gap on formability of welded thin sheet, LDH test was caried out. At high welding speed, the partial penetration was obtained by low heat input. Otherwise, porosity was formed in the bead at low weld speed because of too much heat input. The optimum welding condition of welding was derived from bead width, penetration and hardness property. The maximum gap tolerance on laser welding was observed to be about 0.2mm. This gap size has good relationship with beam size of laser spot(about 0.3mm). The formability of welded sheet was about $80{\%}$ value of base metal and the gap size has not affected on the formability, although weld quality is dependent on the gap size.

• Journal of Welding and Joining
• /
• v.20 no.3
• /
• pp.122-128
• /
• 2002

The laser welding in the automotive industries has been used widely for the butt joint of blank sheets rather than the lap joint of automotive body panels. But as a substitute far the spot welding of automotive body panels, the so called three dimensional laser welding will be important far the body panel engineers. Specially the laser welding of body panels with a smooth weld line is applied increasingly, for example, to the side panels. So far, some criteria of the laser weld quality was suggested by in-house regulations or national standards from experiences and/or rule of thumbs. In the manufacturing places, a go or no-go criterion is adopted because of the simplicity or a lack of rational criteria. It is true specially for the selection of the process parameters, which gives the basic causes for the good quality of laser welds. In this study, the effects of joint combination, gap and welding speed on the lap joint $CO_2$ laser welding of two mild steel sheets with different thicknesses are obtained through a $2{\times}3{\times}7$ factorial experiment. The results of the weld quality are statistically analysed using analysis of variance (ANOVA) and compared between two characteristic zones, which are separated by the type of sectional shapes and the level of input energy per volume. The thickness combinations are 0.8mm/1.2mm, 1.2mm/0.8mm of mild steel sheets. The welding speed covers from the deep penetration to the partial penetration. The gap size has three levels of no-gap, 0.16m, and 0.26mm. The bead width, penetration depth and input energy per volume are measured and used as the weld quality criteria.

• Journal of Welding and Joining
• /
• v.27 no.2
• /
• pp.69-75
• /
• 2009

The effects of welding speed were investigated on penetration characteristics, defects and mechanical properties including formability test in Nd:YAG laser welded 1000MPa grade DP steels. A shielding gas was not used and bead-on-plate welding was performed with various welding speeds at 3.5kW laser power. Defects of surface and inner beads were not observed in all welding speeds. As the welding speed increased, the weld cross-section varied from the trapezoid having wider bottom bead, through X type, finally to V type in partial penetration range of welding speeds. The characteristic of hardness distribution was also investigated. The center of HAZ had maximum hardness, followed by a slight decrease of hardness as approaching to FZ. Significant softening occurred at the HAZ near BM. Regardless of the welding speed, the weld showed approximately the same hardness distribution. In the perpendicular tensile test with respect to the weld direction, all specimens were fractured at the softening zone. In the parallel tensile test to the weld direction, the first crack occurred at weld center and then propagated into the weld. Good formability over 80% was taken for all welding conditions.

• Journal of Welding and Joining
• /
• v.15 no.3
• /
• pp.118-127
• /
• 1997

With the trend towards welding automation and robotization, mathematical models for studying the influence of various variables on the weld bead geometry in gas metal arc (GMA) welding process are required. Partial penetration, single-pass bead-on-plate welds using the GMA welding process were fabricated in 12mm mild steel plates employed four different process variables. Experimental results has been designed to investigate the analytical and empirical formulae, and develop mathematical equations for understanding the relationship between process variables and weld bead geometry. The relationships can be usefully employed not only for open loop process control, but also for adaptive control provided that dynamic sensing of process output is performed.