• The Transactions of the Korean Institute of Electrical Engineers
• /
• v.41 no.2
• /
• pp.192-198
• /
• 1992

The electrical properties of the ultrasonic probes and the piezoelectric composite materials with 1-3 connectivity by the extrusion method have been studied. The relative permittivity and piezoelectric coefficient increase linearly as PZT volume% increases and resonance frequency moves to low frequency as the sample thickness increases. The acoustic impedance matching with body and water is better than PZT ceramics' and the reception sensitivity is fine as the thickness thins down.

• Korean Journal of Materials Research
• /
• v.19 no.4
• /
• pp.198-202
• /
• 2009

For use in ultrasonic actuators, we investigated the structural and piezoelectric properties of $(1\;-\;x)Pb(Zr_{0.515}Ti_{0.485})O_3$ - $xPb(Sb_{1/2}Nb_{1/2})O_3$ + 0.5 wt% $MnO_2$ [(1 - x)PZT - xPSN + $MnO_2$] ceramics with a variation of x (x = 0.02, 0.04, 0.06, 0.08). All the ceramics, which were sintered at $1250^{\circ}C$ for 2 h, showed a typical perovskite structure, implying that they were well synthesized. A homogeneous micro structure was also developed for the specimens, and their average grain size was slightly decreased to $1.3{\mu}m$ by increasing x to 0.8. Moreover, a second phase with a pyrochlore structure appeared when x was above 0.06, which resulted in the deterioration of their piezoelectric properties. However, the 0.96PZT-0.04PSN+$MnO_2$ ceramics, which corresponds with a morphotropic phase boundary (MPB) composition in the (1 - x)PZT - xPSN + $MnO_2$ system, exhibited good piezoelectric properties: a piezoelectric constant ($d_{33}$) of 325 pC/N, an electromechanical coupling factor ($k_p$) of 70.8%, and a mechanical quality factor ($Q_m$) of 1779. The specimens with a relatively high curie temperature ($T_c$) of $305^{\circ}C$ also showed a significantly high dielectric constant (${\varepsilon}_r$) value of 1109. Therefore, the 0.96PZT - 0.04PSN + $MnO_2$ ceramics are suitable for use in ultrasonic vibrators.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.19 no.5
• /
• pp.417-421
• /
• 2006

In this study, in order to develop low temperature sintering piezoelectric ceramics for LTCC (Low-Temperature Cofired Ceramic) multilayer piezoelectric actuator, PMW-PMN-PZT ceramics using $0.2wt%\; Li_2CO_3$ and $0.25wt%\;CaCO_3$ as sintering aids were investigated according to the varation of PMW substution. Composition ceramics could be sintered at $900^{\circ}C$ by adding sintering aids. As the amount of PMW substitution increased, the crystal structure of PMW-PMN-PZT ceramics moved from tetragonal phase to rhombohedral phase gradually, and MPB(Morphotrophic Phase Boundary) region appeared at 2 mol% PMW substitution. At the sintering temperature of $900^{\circ}C$, the density, electromechanical coupling factor(kp), mechanical quality factor(Qm), dielectric constant(${\epsilon}r$), piezoelectric constant(d33) and Curie temperature(Tc) of 2 mol% PMW substituted PMW-PMN-PZT ceramics showed the optimal values of $7.88g/cm^3$, 0.58, 1002, 1264, 352 pC/N and $336^{\circ}C$, respectively, for LTCC multilayer piezoelectric actuator application.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.11a
• /
• pp.212-213
• /
• 2005

In this study, in order to develop low temperature sintering piezoelectric actuator, $Pb_{0.985}Bi_{0.01}(Mg_{1/2}W_{1/2})_{0.03}(Ni_{1/3}Nb_{2/3})_{0.13}(Zr_{0.50},Ti_{0.50})_{0.84}$ (PMW-PNN-PZT) ceramic systems were fabricated using $CaCO_3-Li_2CO_3$, sintering aid through a post-annealing process. The sinterability of PMW-PNN-PZT ceranics was remarkably enhanced by liquid phase sintering of $CaCO_3$ and $Li_2CO_3$. But, it was confimed form the X-ray diffraction pattern that the secondary phase along grain boundaries, deteriorated the piezoelectric properties. The secondary phase along grain boundaries was significantly removed by annealing after sintering. The 0.2wt% $Li_2CO_3$-0.25wt% $CaCO_3$-added PMW-PNN-PZT ceramics post-annealed at 900$^{\circ}C$ for 90min exhibited the excellent electromechanical coupling factor($k_p$) of 63.3% and piezoelectric constant($d_{33}$) of 452pC/N, respectively, for multilayer piezoelectricactuatorapplication.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.1
• /
• pp.33-38
• /
• 2003

Highly homogeneous PZT powder was prepared by a partial oxalate method using chemicals of (Z $r_{0.53}$ $Ti_{0.47}$) $O_2$, Pb(N $o_3$)$_2$and (COOH)$_2$ㆍ2$H_2O$. N $b_2$ $O_{5}$ addition effect on microstructure and electrical properties of PZT ceramics was investigated. When the precursors were calcined at 71$0^{\circ}C$, a single perovskite phase was obtained. After sintering at 110$0^{\circ}C$, X-ray diffraction Patterns showed coexistence of rhombohedral and tetragonal phases regardless of the N $b_2$ $O_{5}$ content. As the content of N $b_2$ $O_{5}$ increased, grain size decreased but sintered density increased. The electromechanical coupling factor of kp and the piezoelectric constant of $d_{31}$ increased linearly with the content of N $b_2$ $O_{5}$, and those values reached 0.7 and -200, respectively, when 1.2 mol% of N $b_2$ $O_{5}$ is added. is added.ded.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.357-360
• /
• 2000

Ferroelectric 0.05PZN-xPZT(90/10)-(0.95-x)PZT(10/90) (x=0.65, 0.85) specimens were fabricated by the mixed-oxide method and cold-pressing method using sol-gel derived PZT(90/10) and PZT(10/90) powders. All specimens show a uniform ferroelectric grain without the presence of the pyrocholre phase. Average grain size increased with an increase in sintering temperature, the value for the x=0.65 specimen sintered at 125$0^{\circ}C$ was 14.4${\mu}{\textrm}{m}$. The dielectric constant and dielectric loss of the x=0.65 specimen sintered at 125$0^{\circ}C$ were 1247, 2.05%, respectively. All specimens showed fairly good temperature and frequency stability of dielectric constant with the range from -2$0^{\circ}C$ to 6$0^{\circ}C$ and 100Hz to 10MHz. The coercive electric field and the remanent polarization of x = 0.65 specimen sintered at 125$0^{\circ}C$ were 8.5 kV/cm and 13 $\mu$C/cm$^2$, respectively.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.14 no.11
• /
• pp.904-911
• /
• 2001

High-density lead zirconate titanate(Pb(Zr$\_$0.53/Ti$\_$0.47/)O$_3$, PZT) ceramics were fabricated by a new milling-precipitation(MP) process improved from the conventional solid state process. This process was progressed by a milling impregnation through mixing ZrO$_2$ and TiO$_2$ powders with lead nitrate(Pb(NO$_3$)$_2$) water solution in zirconia ball media, and then milling precipitation was induced from precipitation of PbC$_2$O$_4$ by adding ammonium of oxalate monohydrate((NH$_4$)$_2$C$_2$O$_4$$.$H$_2$O) as a precipitant. As a result of this process, single-phase perovskite structure was formed at the calcination temperature of 750$\^{C}$ for Pb(Zr$\_$0.53/Ti$\_$0.47/)O$_3$ powders. In addition, the highest density at the sintering temperature of 1100$\^{C}$ was obtained, because of the highly sinterable PZT Powders ground through the re-milling process. Piezoelectric and dielectric properties of sintered sample were improved by MP process.

• The Journal of the Institute of Internet, Broadcasting and Communication
• /
• v.12 no.1
• /
• pp.245-248
• /
• 2012

In this paper, the optimized growing conditions of PZT thin films on low temperature co-fired ceramics (LTCC) substrates are studied. The LTCC technology is an emerging one in the fields of mesoscale (from 10 um to several hundred um) sensor and actuator against silicon based technology due to low cost, high yield, easy manufacturing of 3 dimensional structure, etc. The LTCC substrates with thickness of 400 um are fabricated by laminating 100 um green sheets using commercial power (NEG, MLS 22C). The Pt/Ti bottom electrodes are deposited on the LTCC substrates, then the growing conditions of PZT thin films using rf magnetron sputtering method are studied. The growing conditions are tested under various rf power and gas ratio of oxygen to argon. And the crystallization and ingredient of PZT films are analyzed by X-ray diffraction method (XRD) and energy dispersive spectroscopy (EDS). The optimized growing conditions of PZT thin films are rf power of 125W, Ar/O2 gas ratio of 15:5.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.11a
• /
• pp.317-321
• /
• 2002

Piezoelectric properties of $(Pb_{1-x}Y_x)[(Ni_{1/3}Nb_{2/3})_{0.15}(Zr_{1/2}Ti_{1/2)})_{0.85}]O_{3}$ (x=0~0.05) ceramics were investigated, The stoichiometric PNN-PZT ceramics required the sintering temperature above $1100^{\circ}C$, but the addition of $Y_{2}O_{3}$ in the PNN-PZT ceramic lowered the sintering temperature down to $1000^{\circ}C$. In case of x=0.005, the electro-mechanical coupling $factor(K_p)$, the piezoelectric $constant(d_{33})$, and the maximum strain ratio of PNN-PZT ceramics sintered at $1000^{\circ}C$ were 53.1%, 395pC/N, and $2200{\times}10^{-6}$ respectively, A 30-layer piezoelectric actuator$(10{\times}10{\times}1.7mm)$ fabricated with the above material showed the maximum strain of $2.09{\mu}m$ under 100V DC bias.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.19 no.7
• /
• pp.655-661
• /
• 2006

Dielectric and piezoelectric properties of PMN-PZT ceramics with a high mechanical quality factor$(Q_m)$ and a low temperature sintering temperature were investigated as a function of PZN substitution in order to develop multilayer piezoelectric transformer for AC-DC converter. Multilayer piezoelectric transformers were subsequently manufactured using the PMN-PZN-PZT ceramic offering the optimal behavior and then the electrical performance were invetigated. At the sintering temperature of $940^{\circ}C$, density, electromechanical coupling factor$(k_p)$, mechanical qualify factor$(Q_m)$ and dielectric constant$(\varepsilon_r)$ of 8 mol% PZN substituted specimen were $7.73g/cm^3$, 0.524, 1573 and 1455, respectively. The PZN substitution caused a increase in the dielectric constant and the electromechnical coupling factor. The voltage step-up ratio of multilayer piezoelectric transformer showed the maximum value at near the resonant frequency of 76.55 kHz and increased according to the increase of load resistance. The multilayer piezoelectric transformer with the output impedance coincided with the load resistance showed the temperature increase of less than $20^{\circ}C$ at the output power of 10 W. Based on the results, the manufactured multilayer transformer using the low temperature sintered PMN-PZN-PZT ceramics can be stably driven for both step-up and down transformers.