• Journal of Welding and Joining
• /
• 제8권3호
• /
• pp.39-52
• /
• 1990

The research is to insure the soundness of the stainless steel overlaid weld metal(21/4Cr-IMo steel + SUS 309L) for a pressure vessel application. Detail studies were conducted for the PWHT influence on the micrstructure and intergranular corrosion characteristics of the overlaid weld metal as well as initiation of hydrogen embrittlement crack(or Disbonding) when welded metal are exposed to the hydrogen atmosphere. Hydrogen was experimentally charged to the overlaid weld metal in order to study PWHT effect on the susceptibility of hydrogen embrittlement crack. The results of this research are as follows: 1. At the bond region, austenite grain of the stainless steel side became coarsed and Cr23C6 type carbide was precipitated at the coarsed austenitic grain boundaries. Intergranular Corrosion width(by Straiss test) increased with increasing PWHT temperature and PWHT time.

• Journal of Welding and Joining
• /
• 제5권2호
• /
• pp.9-16
• /
• 1987

Post weld heat treatment (PWHT) is carried out to increase the fracture toughness in heat affected zone(HAZ) and remove the residual stress. There occur some problems such as toughness decreement and stress relief cracking(SRC) in the coarse grained HAZ subjected to the effect of tempering treatment. Especially, embitterment of structure directly relates to the mode of fracture and is appeared as the difference of fracture surface, that is, grain boundary failure. Therefore, in this paper, PWHT was carried out under the stress of 0, 10, 20 and $30kg/cm^2$ to simulate residual stress in HAZ welded by heat input of 10, 30 and 40KJ/cm. Applied stress in weld HAZ during PWHT assisted precipitin of over saturated alloying element in the structure, and grain boundary failure according to welding heat input didn't almost appear at the heat input of 10 KJ/cm, but it appeared from being the applied stress of $30kg/cm^2$ at $30KJ/cm and 20kg/mm^2$ at 40KJ/cm.

• Journal of Welding and Joining
• /
• 제5권3호
• /
• pp.53-61
• /
• 1987

Post weld heat treatment(PWHT) is usually carried out to remove the residual stress and to improve the microstructure and mechanical properties of welded joints. By the way, welding structure transformed owing to PWHT and reheating for repair loads the random cycles fatigue as offshore welding structure of constant low cycle fatigue as pressure vessel, and then, pre-existing flaws or cracks exist in a structural component and those cracks grow under cyclic loading. Therefore, the effects of PWHT and stress ratio on fatigue crack growth behaviors were studied on the three regions such as HAZ, sub-critical HAZ and deposit metal of welded joints in SM53 steel. Fatigue crack growth behavior of as-weld depended on microstructure and fatigue crack growth rate of HAZ was the lowest at eac region, but after PWHT it was somewhat higher than that of as-wel. In case of applying the stress($10kg/mm^2$) during PWHT, fatigue crack growth resistance tended to increase in the overall range of .DELTA.K.

• 대한기계학회논문집
• /
• 제11권2호
• /
• pp.314-321
• /
• 1987

본 논문에서는 용접열영향부(heat affected zone: HAZ)의 인성에 영향을 미치 는 인자중에서 잔유응력의 영향은 중대한 문제로 주목되고 있으며, 이로 인한 용접재 의 기계적 성질의 저하를 경함하기 위한 방법으로 용접후열처리(post weld heat trea- tment: PWHT)에 의한 제거방법을 이용하고 있다.그러나 이 열처리는 보톤 600.deg. C 이 상의 고온에서 실현되기 때문에 열처리과정에서 템퍼링(tempering)효과로 인한 HAZ의 열화가 때때로 발생하고 있어서 용접 시공상 문제로 되고 있다. 또한 PWHT시에는 가 열중이나 냉각중에도 열처리효과가 진행되고 있다고 볼 수 있으므로, PWHT가열속도는 기계적 성질의 개선이라는 이유외에 경제적 측면에서도 중요시 된다. 특히 용접조직 의 포화는 파괴의 양식에 직접반영되어, 파면형태의 차로 나타나므로, 본 조직의 포화 와 관련시켜 검토하기 위하여 열처리된 HAZ를 대상으로 작용된 응력의 크기와 가열속 도가 HAZ의 파괴인성에 어떠한 영향을 미치는지를 COD파괴인성시험과 미소경도측정, 그리고 주사전자현미경관찰을 통하여 고찰하였다.

• Journal of Advanced Marine Engineering and Technology
• /
• 제25권2호
• /
• pp.409-409
• /
• 2001

해양구조물은 점점 대형화되어 가고 있는 추세에 있으며 또한 이들 구조물의 대형화에 따른 구조물의 보수, 유지관리가 매우 중요한 사안으로 등장하게 되었다. 뿐만 아니라, 이러한 구조물 등이 손상또는 파괴되었을 경우는 그에 따른 인적, 경제적 손실 또한 막대할 것으로 사료되며 이러한 구조물의 파괴사례중 상당 부분이 용접부의 부식문제 및 수소취화와 관련된 사고인것으로 보고되고 있다. 한편 용접은 급속가열, 급속냉각의 공적으로 인한 경도와 열적, 조직적 변화를 일으켜 용접부 각 미세부위별 전위차가 발생하게 되며, 이로 인해 갈바낙부실을 일으키는 것으로 보고 있다. 그리고 갈바닉 부식에 의한 용접부의 부식성을 억제하기 위해 용접후열처리(post weld heat treatment PWHT)를 시행하여 내식성을 향상시키는 경우도 있다. 본 연구에서는 고장력강인 RE36강 시험편을 전기화학적 측면에서 최적의 용접후열처리 온도를 규명하였으며, 용접방법(FCAW, SMAW), 용접후 열처리 유무에 따른 용접부위의 저변형을 인장실험을 통한 기계적 특성, 전기화학적 특성 및 수소취화 감수성을 등을 규명하였다. 따라서 본 연구 결과는 해양구조물 선박의 설계시공시에 용접부 주위의 기계적. 전기화학적 특성 평가 및 수소취화 방지대책에 좋은 참고자료가 될 것으로 기대된다.