• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2001.06a
• /
• pp.3-3
• /
• 2001

Recently TiN, TiAlN, CrN hardcoatings have adapted many industrial application such as die, mold and cutting tools because of good wear resistant and thermal stability. However, in terms of high speed process, general hard coatings have been limited by oxidation and thermal hardness drop. Especially in the case of PCB drill, high speed cutting and without lubricant process condition have not adapted these coatings until now. Therefore more recently, superhard nanocomposite coating which have superhard and good thermal stability have developed. In previous works, WC-TiAlN new nanocomposite film was investigated by cathodic arc ion plating system. Control of AI concentration, WC-TiAlN multi layer composite coating with controlled microstructure was carried out and provides additional enhancement of mechanical properties as well as oxidation resistance at elevated temperature. It is noted that microhardness ofWC-TiA1N multi layer composite coating increased up to 50 Gpa and got thermal stability about $900^{\circ}C$. In this study WC-TiAlN nanocomposite coating was deposited on PCB drill for enhancement of life time. The parameter was A1 concentration and plasma cleaning time for edge sharpness maintaining. The characteristic of WC-TiAlN film formation and wear behaviors are discussed with data from AlES, XRD, EDS and SEM analysis. Through field test, enhancement of life time for PCB drill was measured.

• Journal of Welding and Joining
• /
• v.17 no.1
• /
• pp.77-81
• /
• 1999

Through-hole PCB(Printed Circuit Board) was soldered by flow soldering process using cleaning or noncleaning fluxes. Preheating temperature and conveyor speed were changed in the range of 323∼413K and 0.3∼2m/min respectively. The soldered joints were tensile tested in order to evaluated bonding strength. As experimental results, relatively high tensile fracture load, 120∼140N, were obtained in case of preheating temperature of 383K, and conveyor speed was 0.6∼1.0 m/min. Fractured surfaces of higher tensile strength show some dimple area, while those of lower tensile fracture load show brittle fracture.

• Journal of the Semiconductor & Display Technology
• /
• v.8 no.2
• /
• pp.15-21
• /
• 2009

Atmospheric pressure plasma equipment was successfully applied to the flip chip BGA manufacturing process to improve the uniformity of flux printing process. The problem was characterized as shrinkage of the printed flux layer due to insufficient surface energy of the flip chip BGA substrate. To improve the hydrophilic characteristics of the flip chip BGA substrate, remote DBD type atmospheric pressure plasma equipment was developed and adapted to the flux print process. The equipment enhanced the surface energy of the substrate to reasonable level and made the flux be distributed over the entire flip chip BGA substrate uniformly. This research was the first adaptation of the atmospheric pressure plasma equipment to the flip chip BGA manufacturing process and a lot of possible applications are supposed to be extended to other PCB manufacturing processes such as organic cleaning, etc.